Search

Abstract: Photocatalytically active, N-doped TiO2 thin films were prepared by low pressure metalorganic chemical vapor deposition (MOCVD) using titanium tetra-iso-propoxide (TTIP) as a precursor and NH3 as a reactive doping gas. We present the influence of the growth parameters (temperature, reactive gas phase composition) on the microstructural and physico-chemical characteristics of the films, as deduced from X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), secondary ion mass spectrometry (SIMS) and ultra-violet and visible (UV/Vis) spectroscopy analysis. The N-doping level was controlled by the partial pressure ratio R =[NH3]/[TTIP] at the entrance of the reactor and by the substrate temperature. For R =2200, the N-doped TiO2 layers are transparent and exhibit significant visible light photocatalytic activity (PA) in a narrow growth temperature range (375–400 °C). The optimum N-doping level is approximately 0.8 at.%. However, the PA activity of these N-doped films, under UV light radiation, is lower than that of undoped TiO2 films of comparable thickness. [Copyright &y& Elsevier]

This study aims at evaluating the biocompatibility of titanium surfaces modified according two different ways: (i) deposition of a bio-inert, thin film of rutile TiO2 by chemical vapour deposition (MOCVD), and (ii) biochemical treatment with collagen gel, in order to obtain a bio-interactive coating. Behind the comparison is the idea that either the bio-inert or the bio-active coating has specific advantages when applied to implant treatment, such as the low price of the collagen treatment for instance. The stability in buffer solution was evaluated by open circuit potential (OCP) for medium time and cyclic voltametry. The OCP stabilized after 5·104 min for all the specimens except the collagen treated sample which presented a stable OCP from the first minutes. MOCVD treated samples stabilized to more electropositive values. Numeric results were statistically analysed to obtain the regression equations for long time predictable evolution. The corrosion parameters determined from cyclic curves revealed that the MOCVD treatment is an efficient way to improve corrosion resistance. Human dermal fibroblasts were selected for cell culture tests, taking into account that these cells are present in all bio-interfaces, being the main cellular type of connective tissue. The cells grew on either type of surface without phenotype modification. From the reduction of yellow, water-soluble 3-(4,5-dimethyldiazol-2-yl)-2,5-diphenyl tetrazolium bromide (MTT cytotoxicity test), MOCVD treated samples offer better viability than mechanically polished Ti and collagen treated samples as well. Cell spreading, as evaluated from microscope images processed by the program Sigma Scan, showed also enhancement upon surface modification. Depending on the experimental conditions, MOCVD deposited TiO2 exhibits different nanostructures that may influence biological behaviour. The results demonstrate the capacity of integration in simulated physiologic liquids for an implant pretreated by either method. [ABSTRACT FROM AUTHOR]

Abstract: Due to the high diffusivity of the chemical species, chemical vapor infiltration (CVI) is a suitable process for the conformal coverage of objects with large dimensions and complex shape geometry. Its large scale capacity and high reproducibility have made the technique favorable for the deposition of non-oxide ceramics. There are few works on other materials and metal-organic compounds are rarely used as molecular precursors. In this study we focus on the deposition of anatase thin films on substrates with large surface area (microfibers) for photocatalytic air treatment systems. Titanium tetra-isopropoxide (TTIP) was used as precursor without additional oxygen source. Using low mole fractions (26–124×10−5) and low deposition temperatures (300–400 °C), a relatively good thickness uniformity was obtained along the reactor axis. Infiltration experiments were achieved in this temperature range and under 1 Torr for high TTIP diffusivity (110–146 cm2 s−1) and low initial Thiele modulus (0.11–0.13) values. Photocatalytic activity of TiO2 coated glass microfiber samples depends on the film morphology, average thickness and infiltration efficiency. It is shown that this later parameter plays a major role due to the increase of active surface area. [Copyright &y& Elsevier]

Abstract: We report on the in vitro response of human gingival fibroblasts (HGF-1 cell line) to various thin films of titanium dioxide (TiO2) deposited on titanium (Ti) substrates by low pressure metal-organic chemical vapor deposition (LP-MOCVD). The aim was to study the influence of film structural parameters on the cell behavior comparatively with a native-oxide covered titanium specimen, this objective being topical and interesting for materials applications in implantology. HGF-1 cells were cultured on three LP-MOCVD prepared thin films of TiO2 differentiated by their thickness, roughness, transversal morphology, allotropic composition and wettability, and on a native-oxide covered Ti substrate. Besides traditional tests of cell viability and morphology, the biocompatibility of these materials was evaluated by fibronectin immunostaining, assessment of cell proliferation status and the zymographic evaluation of gelatinolytic activities specific to matrix metalloproteinases secreted by cells grown in contact with studied specimens. The analyzed surfaces proved to influence fibronectin fibril assembly, cell proliferation and capacity to degrade extracellular matrix without considerably affecting cell viability and morphology. The MOCVD of TiO2 proved effective in positively modifying titanium surface for medical applications. Surface properties playing a crucial role for cell behavior were the wettability and, secondarily, the roughness, HGF-1 cells preferring a moderately rough and wettable TiO2 coating. [ABSTRACT FROM AUTHOR]

Abstract: The photocatalytic degradation of gaseous (toluene) and aqueous (imazapyr, malic acid, orange G) pollutants over TiO2 supported photocatalysts is investigated using a batch reactor. A strong influence of the microstructural characteristics of TiO2 on the decomposition kinetics of the pollutants is found. Well crystallized, porous TiO2-anatase films grown under low pressure at 400–500°C by MOCVD on glass plates and by MOCVI on glass micro-fibers are the best heterogeneous photocatalysts, showing the highest activity. We demonstrate a good control of these characteristics by choosing the deposition parameters. Achieving conformal coverage (i.e. good infiltration) of glass micro-fibers by the TiO2 thin films has also a strong influence on the photocatalytic activity. A correlation between optimal infiltration, film microstructure and photocatalytic activity is established. Strong similarities between optimal photocatalytic decomposition rate in gas and liquid phase were found with respect to the film microstructure and the photocatalyst mass. The total mineralization of the toluene was prevented because of the deactivation of the photocatalyst surface. However the reactivation of the photocatalyst was achieved by UV irradiation under oxygen stream. This allows a long-term use of the photocatalyst. [Copyright &y& Elsevier]