Search

There is a growing need for small-diameter (6 mm) off-the-shelf synthetic vascular conduits for different surgical bypass procedures, with actual synthetic conduits showing unacceptable thrombosis rates. The goal of this study was to build vascular grafts with better compliance than standard synthetic conduits and with an inner layer stimulating endothelialization while remaining antithrombogenic.Tubular vascular conduits made of a scaffold of polyurethane/polycaprolactone combined with a bioactive coating based on chondroitin sulfate (CS) were created using electrospinning and plasma polymerization. In vitro testing followed by a comparative in vivo trial in a sheep model as bilateral carotid bypasses was performed to assess the conduits' performance compared to the actual standard.In vitro, the novel small-diameter (5 mm) electrospun vascular grafts coated with chondroitin sulfate (CS) showed 10 times more compliance compared to commercial expanded polytetrafluoroethylene (ePTFE) conduits while maintaining adequate suturability, burst pressure profiles, and structural stability over time. The subsequent in vivo trial was terminated after electrospun vascular grafts coated with CS showed to be inferior compared to their expanded polytetrafluoroethylene counterparts.The inability of the experimental conduits to perform well in vivo despite promising in vitro results may be related to the low porosity of the grafts and the lack of rapid endothelialization despite the presence of the CS coating. Further research is warranted to explore ways to improve electrospun polyurethane/polycaprolactone scaffold in order to make it prone to transmural endothelialization while being resistant to strenuous conditions.

PURPOSE To evaluate if synovial inflammation and hypervascularization are present in a dog model of knee osteoarthritis and can be detected on conventional magnetic resonance imaging (MRI), dynamic contrast-enhanced magnetic resonance imaging (DCE-MRI), contrast-enhanced magnetic resonance imaging (CE-MRI), and quantitative digital subtraction angiography (Q-DSA) imaging. MATERIALS AND METHODS Six dogs underwent MRI and angiography of both knees before and 12 weeks after right knee anterior cruciate ligament injury. Synovial vascularity was evaluated on CE-MRI, DCE-MRI, and Q-DSA by 2 independent observers. Synovial inflammation and vascularity were histologically scored independently. Cartilage lesions and osteophytes were analyzed macroscopically, and cartilage volumetry was analyzed by MRI. Vascularity and osteoarthritis markers on imaging were compared before and after osteoarthritis generation, and between the osteoarthritis model and the control knee, using linear mixed models accounting for within-dog correlation. RESULTS In all knees, baseline imaging showed no abnormalities. Control knees did not develop significant osteoarthritis changes, synovial inflammation, or hypervascularization. In osteoarthritis knees, mean synovial enhancement score on CE-MR imaging increased by 13.1 ± 0.59 (P < .0001); mean synovial inflammation variable increased from 47.33 ± 18.61 to 407.97 ± 18.61 on DCE-MR imaging (P < .0001); and area under the curve on Q-DSA increased by 1058.58 ± 199.08 (P = .0043). Synovial inflammation, hypervascularization, and osteophyte formations were present in all osteoarthritis knees. Histology scores showed strong correlation with CE-MR imaging findings (Spearman correlation coefficient [SCC] = 0.742; P = .0002) and Q-DSA findings (SCC = 0.763; P < .0001) and weak correlation with DCE-MR imaging (SCC = -0.345; P = .329). Moderate correlation was found between CE-MR imaging and DSA findings (SCC = 0.536; P = .0004). CONCLUSIONS In this early-stage knee osteoarthritis dog model, synovial inflammation and hypervascularization were found on imaging and confirmed by histology.

To compare the efficacy of an embolization agent with sclerosing properties (made of chitosan and sodium tetradecyl sulfate, CH–STS) with a similar embolization agent but without sclerosing properties (made of chitosan, CH) in treating endoleaks in a canine endovascular aneurysm repair model. Two chitosan-based radiopaque hydrogels were prepared, one with STS and one without STS. Their rheological, injectability, and embolizing properties were assessed in vitro; afterwards, their efficacy in occluding endoleaks was compared in a canine bilateral aneurysm model reproducing type I endoleaks (n = 9 each). The primary endpoint was endoleak persistence at 3 or 6 months, assessed on a CT scan and macroscopic examination. Secondary endpoints were the occurrence of stent-graft (SG) thrombosis, the evolution of the aneurysm mean diameter, as well as aneurysm healing and inflammation scores in pathology examinations. In vitro experiments showed that both products gelled rapidly and presented initial storage moduli greater than 800 Pa, which increased with time. Both gels were compatible with microcatheter injection and occlude flow up to physiological pressure in vitro. In a type I endoleak model, the injection of CH–STS sclerosing gel tended to reduce the risk of occurrence of endoleaks, compared to CH non-sclerosing agent (2/9 vs. 6/9, p = 0.069). No case of SG thrombosis was observed. Moderate inflammation was found around both gels, with a comparable intensity score in both CH and CH–STS groups (2.6 ± 0.9 and 2.7 ± 0.9, respectively; p = 0.789). Flow occlusion combined with chemical endothelial denudation appears promising for the treatment of endoleaks. N/A.

To evaluate the ability to create in vivo antegrade fenestrations (IVAF) using a radiofrequency probe in juxtarenal aortic stent-grafts to preserve the patency of renal arteries.Modified stent-grafts with an unsupported fenestration area were deployed in the juxtarenal aorta of 2 25-kg dogs. Prior to deployment, both renal arteries were marked with detachable coils that were later removed (dog 1) or with hydrophilic catheters (dog 2). After deployment, a radiofrequency probe was used to perforate the graft. If puncture was successful, attempts were made to pass guidewires into the renal arteries for balloon dilation and stenting of the graft perforation. Doppler ultrasound scans of the renal arteries were taken after 1 week. Doppler ultrasound and angiography were repeated prior to autopsy and macroscopic analysis at 1 month.Fenestration was attempted in 3 renal arteries (1 in dog 1 and 2 in dog 2). It was successful in 2 renal arteries but required 6 attempts in dog 1 and 3 in dog 2. The failed case was related to the position of a stent-graft strut close to the fenestration area. One stent thrombosis was seen during follow-up, while the other fenestrated artery remained patent. No stent fracture was encountered during follow-up.This radiofrequency device allowed successful fenestration but was difficult to control. Technical improvements are required to improve clinical success and patency.

Purpose: To examine in a canine model the feasibility of antegrade fenestration of abdominal aortic stent-grafts to preserve the patency of the renal arteries. Methods: Two large dogs underwent antegrade fenestration of stent-grafts in the perirenal aorta. Before fenestration, bare stents were inserted in both renal arteries as fluoroscopic landmarks. A 12-mm iliac extension served as the canine aortic endograft. The first procedure was done under ultrasound and fluoroscopic guidance, using an intravascular ultrasound (IVUS) probe inserted in the vena cava and a Pioneer IVUS catheter. The second was performed exclusively under fluoroscopic guidance with a Brockenbrough needle. Angiograms and duplex ultrasound were planned for 1 month, after which the dogs would be sacrificed for autopsy. The explanted endograft was subjected to biomaterials analysis, with a focus on fabric tear. Results: Perforation of the aortic graft and catheterization of the renal arteries with a floppy guidewire were possible in both animals. In dog 1, aortic graft dilation and subsequent fenestration were not possible, and the experiment was terminated. However, the procedure was successful in both renal arteries of dog 2. At 1-month follow-up in this dog, both renal arteries were patent. Stent fractures were observed bilaterally. There was no extension of the damage to the fabric beyond the area of fenestration. Conclusion: In vivo antegrade fenestration of aortic endografts is technically feasible. However, improvements in technique, instrumentation, and materials are required to make it a reliable and reproducible way of allowing stent-graft vascularization of aortic side branches.

To investigate if shear wave imaging (SWI) can detect endoleaks and characterize thrombus organization in abdominal aortic aneurysms (AAAs) after endovascular aneurysm repair. Stent grafts (SGs) were implanted in 18 dogs after surgical creation of type I endoleaks (four AAAs), type II endoleaks (13 AAAs) and no endoleaks (one AAA). Color flow Doppler ultrasonography (DUS) and SWI were performed before SG implantation (baseline), on days 7, 30 and 90 after SG implantation, and on the day of the sacrifice (day 180). Angiography, CT scans and macroscopic tissue sections obtained on day 180 were evaluated for the presence, size and type of endoleaks, and thrombi were characterized as fresh or organized. Endoleak areas in aneurysm sacs were identified on SWI by two readers and compared with their appearance on DUS, CT scans and macroscopic examination. Elasticity moduli were calculated in different regions (endoleaks, and fresh and organized thrombi). All 17 endoleaks (100 %) were identified by reader 1, whereas 16 of 17 (94 %) were detected by reader 2. Elasticity moduli in endoleaks, and in areas of organized thrombi and fresh thrombi were 0.2 ± 0.4, 90.0 ± 48.2 and 13.6 ± 4.5 kPa, respectively (P

To assess the ability of noninvasive vascular elastography (NIVE) to help characterize endoleaks and thrombus organization in a canine model of abdominal aortic aneurysm after endovascular aneurysm repair with stent-grafts, in comparison with computed tomography (CT) and pathologic examination findings.All protocols were approved by the Animal Care Committee in accordance with the guidelines of the Canadian Council of Animal Care. Stent-grafts were implanted in a group of 18 dogs with aneurysms created in the abdominal aorta. Type I endoleak was created in four aneurysms; type II endoleak, in 13 aneurysms; and no endoleak, in one aneurysm. Doppler ultrasonography and NIVE examinations were performed at baseline and at 1-week, 1-month, 3-month, and 6-month follow-up. Angiography, CT, and macroscopic tissue examination were performed at sacrifice. Strain values were computed by using the Lagrangian speckle model estimator. Areas of endoleak, solid organized thrombus, and fresh thrombus were identified and segmented by comparing the results of CT and macroscopic tissue examination. Strain values were compared by using the Wilcoxon rank-sum and Kruskal-Wallis tests.All stent-grafts were successfully deployed, and endoleaks were clearly depicted in the last follow-up elastography examinations. Maximal axial strains over consecutive heart cycles in endoleak, organized thrombus, and fresh thrombus areas were 0.78% ± 0.22, 0.23% ± 0.02, 0.10% ± 0.04, respectively. Strain values were significantly different between endoleak and organized or fresh thrombus areas (P.000) and between organized and fresh thrombus areas (P.0002). No correlation was found between strain values and type of endoleak, sac pressure, endoleak size, and aneurysm size.NIVE may be able to help characterize endoleak and thrombus organization, regardless of the size, pressure, and type of endoleak.

The authors implemented a PCR protocol to rapidly screen for Pasteurella pneumotropica and to accurately identify contaminated laboratory mice in a clinical setting. This protocol was implemented in response to a severe outbreak of P. pneumotropica in their animal facility. Although a sentinel program was in place to routinely screen for P. pneumotropica, it was inadequate for the identification of contaminated animals. As a result, several additional strains of mice were contaminated and developed clinical signs of infection. The authors implemented a screening method using PCR with reported primer pairs previously developed to identify the biotype isolates of P. pneumotropica in laboratory mice. Throat culture swabs were collected from live mice and placed in a bacterial culture. The DNA from these cultures was isolated and screened by PCR. This procedure enabled the authors to eliminate P. pneumotropica from several animal housing rooms. The assay can be easily applied in most animal facilities.

Investigators of our research facility generally accept the concept of asepsis as an important component of adequate surgical care for animals. However, they experience difficulties putting it into practice, especially in the case of rodents. The reasons for this are inconvenience, cost, and lack of training. To better assist investigators in the implementation of aseptic surgical techniques in their laboratories, we have created an Operating Room (OR) Committee modeled after OR committees found in human hospitals. A reconstructive surgeon, a veterinarian, a research scientist, a nurse involved in the training of OR personnel, interns, graduate students, and an animal health technician were chosen as committee members in light of their OR and animal care expertise. The first task of the OR Committee was to establish institutional guidelines for aseptic surgery, taking into account the costs imposed on research budgets by these procedures. The OR Committee also supports a complete training program in aseptic surgery techniques, which consists of lectures, a training manual, videos, and a practical course. Furthermore, when experimental procedures require specialized equipment, the OR Committee collaborates with researchers to develop strategies to achieve asepsis. This OR Committee and the training program proved to be important tools to promote and improve the quality of animal care during surgery.