Search

Highly transparent Ho:Y2O3 ceramics for laser diode lighting were prepared using the vacuum sintering method with 0.3 at.% Nb2O5 as a sintering additive. The microstructures, transmittance, and luminescence properties of the Ho:Y2O3 ceramic samples were investigated in detail. The transmittance levels of all samples with various Ho3+ concentrations reached ~81.5% (2 mm thick) at 1100 nm. Under the excitation of 363 nm (ultraviolet) or 448 nm (blue) light, Ho:Y2O3 transparent ceramic samples showed that green emission peaked at 550 nm. The emission intensity was strongly affected by the concentration of Ho3+ ions, reaching its highest level in the sample doped with 1 at.% Ho3+. The CIE coordinates of the luminescence were in the green region (i.e., the CIE coordinates of the sample doped with 1 at.% Ho3+ were [0.27, 0.53] and [0.30, 0.69], under the excitation of 363 nm and 448 nm light, respectively). The possibility of its application as laser diode lighting was reported. Under the excitation of 450 nm blue laser, the sample doped with 0.5 at.% Ho3+ had the best performance: the saturated luminous flux, lumen efficiency, and the luminescence saturation power densities were 800 lm, 57.7 lm/W, and 17.6 W/mm2, respectively. Furthermore, the materials have high thermal conductivity and mechanical strength due to their host of rare-earth sesquioxide. Thus, Ho:Y2O3 transparent ceramics are expected to be a promising candidate for green-light-emitting devices for solid-state lighting, such as laser diode lighting. [ABSTRACT FROM AUTHOR]

Differential densification has been observed in the sintering of Ho:Y 2 O 3 ceramics at heating rates of ≤3 °C. The temperature gradients in compacts during the heating process were simulated using ANSYS software. At a heating rate of 3 °C/min, the simulation results indicate a small temperature discrepancy of about 2 °C between the surface and the center area of the samples. Compared with those in the near-center (NC) area of the compact, the grain coarsening and rearrangement in the near-surface (NS) area are more pronounced during the initial and intermediate sintering stages. As a consequence, both the pore distribution and microstructure in the NS area were more uniform, which accelerated the elimination of pores in the subsequent sintering stage. This observation suggests that particle rearrangement in the early sintering stage is one of the main reasons for the enhancement in the ultimate densification of the ceramics. The NC area could be fully densified by using hot isostatic pressing (HIP). After HIP, the Ho:Y 2 O 3 ceramics have high in-line transmittance of 80% at the wavelength of 500 nm. [ABSTRACT FROM AUTHOR]

Highly transparent Ho:Y2O3 ceramics for laser diode lighting were prepared using the vacuum sintering method with 0.3 at.% Nb2O5 as a sintering additive. The microstructures, transmittance, and luminescence properties of the Ho:Y2O3 ceramic samples were investigated in detail. The transmittance levels of all samples with various Ho3+ concentrations reached ~81.5% (2 mm thick) at 1100 nm. Under the excitation of 363 nm (ultraviolet) or 448 nm (blue) light, Ho:Y2O3 transparent ceramic samples showed that green emission peaked at 550 nm. The emission intensity was strongly affected by the concentration of Ho3+ ions, reaching its highest level in the sample doped with 1 at.% Ho3+. The CIE coordinates of the luminescence were in the green region (i.e., the CIE coordinates of the sample doped with 1 at.% Ho3+ were [0.27, 0.53] and [0.30, 0.69], under the excitation of 363 nm and 448 nm light, respectively). The possibility of its application as laser diode lighting was reported. Under the excitation of 450 nm blue laser, the sample doped with 0.5 at.% Ho3+ had the best performance: the saturated luminous flux, lumen efficiency, and the luminescence saturation power densities were 800 lm, 57.7 lm/W, and 17.6 W/mm2, respectively. Furthermore, the materials have high thermal conductivity and mechanical strength due to their host of rare-earth sesquioxide. Thus, Ho:Y2O3 transparent ceramics are expected to be a promising candidate for green-light-emitting devices for solid-state lighting, such as laser diode lighting.