Search

It is an attributed fact that magnesium, in normal conditions, behaves as active or anodic material and steel as a noble or cathodic material in a galvanic cell. In the current study, various experiments have been conducted to investigate the electrochemical behavior of magnesium and mild steel galvanic couples in tap water and 0.1M NaHCO3corrosive environments at different temperatures (40 ℃ to 80 ℃). The potentiodynamic results have confirmed that in tap water, magnesium acts as an anode as it corrodes itself and protects steel surfaces under the influence of galvanic action at selected temperatures. However, magnesium became passive under 0.1M NaHCO3making steel anodic, which deteriorates aggressively at higher temperatures in 0.1M NaHCO3. The polarity reversal phenomenon was also observed in the magnesium-steel couple when exposed to this environment. The microstructural examination has shown that passivation occurred due to the formation of an oxide layer that grew towards the steel side in the galvanic couple as the temperature increased. Thus, the study revealed that the magnesium would be more damaging to steel in a NaHCO3environment if utilized in the temperature range of 60 ℃to 80 ℃. Es un hecho confirmado que el magnesio, en condiciones normales, se comporta como material activo o anódico y el acero como material noble o catódico en una celda galvánica. En el estudio actual, se realizaron varios experimentos para investigar el comportamiento electroquímico de los pares galvánicos de magnesio y acero dulce en agua del grifo y ambientes corrosivos de NaHCO30.1M a diferentes temperaturas (40 ℃ a 80 ℃). Los resultados potenciodinámicos han confirmado que, en el agua del grifo, el magnesio actúa como un ánodo a medida que se corroe y protege las superficies de acero bajo la influencia de la acción galvánica a temperaturas seleccionadas. Sin embargo, el magnesio se volvió pasivo bajo NaHCO30.1M, lo que hizo anódico al acero, que se deteriora agresivamente a temperaturas más altas en NaHCO30.1M. El fenómeno de inversión de polaridad también se observó en la pareja de magnesio-acero cuando se expuso a este ambiente. El examen microestructural ha demostrado que la pasivación se produjo debido a la formación de una capa de óxido que creció hacia el lado del acero en el par galvánico a medida que aumentaba la temperatura. Por lo tanto, el estudio reveló que el magnesio sería más dañino para el acero en un entorno de NaHCO3si se utiliza en el rango de temperatura de 60 ℃ a 80 ℃.

This work studies the feasibility of the periodic polarity reversal strategy (PRS) in a combined electrokinetic-biological process for the remediation of clayey soil polluted with a herbicide. Five two-weeks duration electrobioremediation batch experiments were performed in a bench scale set-up using spiked clay soil polluted with oxyfluorfen (20 mg kg. Additionally, two complementary reference tests were done: single bioremediation and single electrokinetic. The microbial consortium used was obtained from an oil refinery wastewater treatment plant and acclimated to oxyfluorfen degradation. Main soil conditions (temperature, pH, moisture and conductivity) were correctly controlled using PRS. On the contrary, the electroosmotic flow clearly decreased as increased. The uniform soil microbial distribution at the end of the experiments indicated that the microbial activity remained in every parts of the soil after two weeks when applying PRS. Despite the adapted microbial culture was capable of degrade 100% of oxyfluorfen in water, the remediation efficiency in soil in a reference test, without the application of electric current, was negligible. However, under the low voltage gradients and polarity reversal, removal efficiencies between 5% and 15% were obtained, and it suggested that oxyfluorfen had difficulties to interact with the microbial culture or nutrients and that PRS promoted transport of species, which caused a positive influence on remediation. An optimal, Este trabajo estudia la viabilidad de la estrategia de inversión periódica de polaridad (PRS) en un proceso combinado electrocinético-biológico para la remediación de suelos arcillosos contaminados con un herbicida. Se realizaron cinco experimentos por lotes de electrobiorremediación de dos semanas de duración en una instalación a escala de banco utilizando suelo arcilloso con púas contaminado con oxifluorfeno (20 mg kg. Adicionalmente, se realizaron dos pruebas complementarias de referencia: biorremediación simple y electrocinética simple . El consorcio microbiano utilizado fue obtenido de una planta de tratamiento de aguas residuales de una refinería de petróleo y aclimatado a la degradación del oxifluorfeno. Las principales condiciones del suelo (temperatura, pH, humedad y conductividad) se controlaron correctamente mediante PRS. Por el contrario, el flujo electroosmótico disminuyó claramente a medida que aumentado. La distribución microbiana uniforme del suelo al final de los experimentos indicó que la actividad microbiana permaneció en todas las partes del suelo después de dos semanas al aplicar PRS. A pesar de que el cultivo microbiano adaptado fue capaz de degradar el 100% del oxifluorfeno en el agua, la eficiencia de remediación en el suelo en una prueba de referencia, sin la aplicación de corriente eléctrica , fue insignificante. Sin embargo, bajo los gradientes de bajo voltaje y la inversión de polaridad, se obtuvieron eficiencias de remoción entre el 5% y el 15%, y sugirió que el oxifluorfeno tenía dificultades para interactuar con el cultivo microbiano o los nutrientes y que el PRS promovió el transporte de especies, lo que provocó una influencia positiva. sobre la remediación. Un óptimo

In this work, it is studied the effect of the electric fields (within the range 0.0–1.5 V cm−1) on the performance of electrobioremediation with polarity reversal, using a bench scale plant with diesel-spiked kaolinite with 14-d long tests. Results obtained show that the periodic changes in the polarity of the electric field results in a more efficient treatment as compared with the single electro-bioremediation process, and it does not require the addition of a buffer to keep the pH within a suitable range. The soil heating was not very important and it did not cause a change in the temperature of the soil up to values incompatible with the life of microorganisms. Low values of water transported by the electro-osmosis process were attained with this strategy. After only 14 d of treatment, by using the highest electric field studied in this work (1.5 V cm−1), up to 35.40% of the diesel added at the beginning of the test was removed, value much higher than the 10.5% obtained by the single bioremediation technology in the same period., En este trabajo se estudia el efecto de los campos eléctricos (en el rango 0,0–1,5 V cm −1) sobre el desempeño de la electrobiorremediación con inversión de polaridad, utilizando una planta a escala de banco con caolinita enriquecida con diesel con pruebas largas de 14 días. Los resultados obtenidos muestran que los cambios periódicos en la polaridad del campo eléctrico dan como resultado un tratamiento más eficiente en comparación con el proceso único de electrobiorremediación, y no requiere la adición de un tampón para mantener el pH dentro de un rango adecuado. El calentamiento del suelo no fue muy importante y no provocó un cambio en la temperatura del suelo hasta valores incompatibles con la vida de los microorganismos. Con esta estrategia se lograron valores bajos de agua transportada por el proceso de electroósmosis. Después de solo 14 d de tratamiento, usando el campo eléctrico más alto estudiado en este trabajo (1.5 V cm −1), se eliminó hasta un 35,40% del diesel agregado al inicio de la prueba, valor muy superior al 10,5% obtenido por la tecnología de biorremediación sola en el mismo período.