Search

The goal of this work was to evaluate the electrochemical properties of TiZrNbTa thin films deposited by magnetron sputtering using an industrial physical vapor deposition system. Samples were deposited on both Si(001) and 316L stainless steel. The samples deposited on Si(001) were either crystalline (bcc reflections) or amorphous, depending on the sputtering parameters. The crystalline films were composed of thin films with two different layers. The upper layer was nanocolumnar composed of elongated nanocolumns, while the lower was dense. The amorphous films had only one nanocolumnar layer and higher porosity. Polarization curves revealed that all samples had low corrosion current densities, in the order of 10-8 A/cm2. The samples showed an extended passive region up to 3.0 V vs Ag/AgCl due to the growth of a passivating oxide. The surface of the samples consisted of Nb2O5, ZrO2, TiO2 and Ta2O5. The chronoamperometry tests showed current oscillations, related to a break-down and reformation of the passive film. Electrochemical impedance spectroscopy revealed that all samples behaved similarly in all three electrolytes, and the simulated electrical circuits were indicating no corrosion reactions. A decrease in capacitance values after polarization was observed and was related to the formed surface oxide. Samples deposited on 316L stainless steel showed a passive regime for a shorter potential window, probably related to surface defects of the films. Heat treatments at 400 and 800 Celsius for 20 hours could not trigger the phase transformation from single bcc to hcp or dual bcc, as predicted by the Thermo-Calc software.

The focus of this literary study was additive manufacturing (AM) and the purpose was to find general trends for selected materials that have been additively manufactured and compare them to results from other reviews. The raw materials studied were stainless steels 316L, 17-4 PH, 15-5 PH and 420, as well as tool steel H13 and nickel alloys 625, 718 and Hastelloy X. The AM techniques studied were selective laser melting (SLM), electron beam melting (EBM) and binder jetting (BJG). A total of 69 articles have been studied to fulfill the purpose above. The articles were used to write a summary of the techniques, compare them to each other and to conventional methods. They were also used to create a database to compile information on mechanical properties, microstructure and process parameters. Based on the database mechanical properties for SLM tend to be higher compared to EBM. This however varied somewhat depending on the processed material. Furthermore the yield and tensile strength obtained from the database for SLM seemed to be higher compared to the values in review articles for almost all materials. Unfortunately not enough values were found for BJG to compare it to SLM and EBM.AM seems to produce weaker, equal and superior products compared to conventional methods. However due to the limited nature of the project and the research found no conclusions can be drawn about any trends, how to achieve the different results or how parameters affect the finished product. To be able to say anything with more certainty more research has to be done. Not only in general concerning the AM techniques, but more studying of existing articles is needed. Finally a standardization on how to reference properties and process parameters is necessary. Currently it is very difficult to compare results or draw conclusions due to different designations, units and a lot of missing essential information.