Search

This work evaluates mortars using sewage sludge calcined at temperatures of 600°C and 700°C as a hydraulic binder replacing the cement. The percentages incorporated by mass to replace the Portland cement were 10%, 20% and 30%, using the 1:3:0,60 (cement: sand: factor a/c) trace. Sludge ash was characterized and tensile strength at flexion as well as tensile strength (pullout test) were evaluated. As a way of performing a comparison with conventional mortars, the same tests were carried out using reference mortar. The results of the flexural tensile strength tests indicated that results were higher than the reference traces of the mortars with the calcined sludge at a temperature of 700°C, a factor related to the increase of the calcination temperature and the incorporated percentage. With respect to the tests on the determination of tensile strength, it was observed that the specimens submitted to the test suffered rupture in the mortar, and that the calcination temperature of the sewage sludge was not influenced. The results obtained with the mortars using sewage sludge ash with partial replacement of the cement are shown within the normative standards and approximate to the results obtained with the tests executed with the reference mortar.

Based on the environmental assumptions that permeate the role of researchers in enabling the use of waste in consumer goods, using sewage sludge in human consumption material has become the object of worldwide study because of the potential that it carries. Aiming to fulfill the sustainable role through the creation of mechanisms that favor the ecological coexistence between environment and human beings, the use of the calcined sewage sludge as a potentiator in the properties of the material is made possible through the construction materials, behavior. Coating mortars are currently evaluated by exposing, from the replacement of the cement by the calcined material, an effective applicability with respect to its resistance to deleterious agents. It is understood that to idealize unconventional materials with the use of residues that have high degradation power to the environment, ratifies the attempt to mitigate large and irreversible environmental impacts arising from improper and poorly planned disposal. A partir das premissas ambientas que permeiam por entre a atuação dos pesquisadores em possibilitar o uso de resíduos em bens de consumo, utilizar o lodo de esgoto em material de consumo humano tornou-se objeto de estudo mundial pelo potencial que o mesmo carrega. Objetivando cumprir o papel sustentável mediante a criação de mecanismos que favorecem a convivência ecológica entre meio ambiente e seres humanos, viabiliza-se através dos materiais de construção, ditos como convencionais, o uso do lodo de esgoto calcinado como potencializador nas propriedades do material, melhorando significativamente o comportamento frente aos esforços mecânicos. As argamassas de revestimento são avaliadas na atualidade por exporem, a partir da substituição do cimento pelo material calcinado, uma efetiva aplicabilidade no que concerne sua resistência à agentes deletérios. Entende-se que idealizar materiais não convencionais com o uso de resíduos que possuem alto poder degradativo ao meio ambiente, ratifica-se a tentativa de mitigar grandes e irreversíveis impactos ambientais advindos do descarte impróprio e mal planejado. Partiendo de las premisas ambientales que permean el trabajo de los investigadores para posibilitar el aprovechamiento de los residuos en bienes de consumo, el aprovechamiento de los lodos de depuradora en material de consumo humano se ha convertido en objeto de estudio a nivel mundial por el potencial que conlleva. Con el objetivo de cumplir el rol sustentable a través de la creación de mecanismos que favorezcan la convivencia ecológica entre el medio ambiente y el ser humano, se viabiliza a través de los materiales de construcción, dicho como convencional, el uso de lodos de depuradora calcinados como potenciador de las propiedades de los materiales, mejorando significativamente el comportamiento frente a esfuerzos mecánicos. Los morteros de revestimiento se evalúan actualmente por presentar, a partir de la sustitución del cemento por material calcinado, una efectiva aplicabilidad en cuanto a su resistencia a los agentes deletéreos. Se entiende que idealizar materiales no convencionales con el uso de residuos que tienen un alto poder degradante para el medio ambiente, ratifica el intento de mitigar los grandes e irreversibles impactos ambientales derivados de la disposición inadecuada y mal planificada.

Through environmental policies that provide a gradual discussion about the disposal of waste produced in the most diverse industrial sectors, sewage sludge is emphasized by the problematic destination of the toxic compounds that compose it, compromising its disposal. Based on the need to implement measures to mitigate environmental impacts through the production of eco-efficient materials, the application of the ashes of sanitary sewage sludge as a partial substitute for Portland cement is currently being used as a coating mortars study. This replacement has a focus, besides reducing the large volume of sludge generated by Sewage Treatment Plants, to allow an attenuation in the consumption of cement, a large CO2 generator during its manufacturing process. It could be observed that the use of the calcined residue applied in mortar, ratifies a relevant physical-mechanical performance to the material, which compared to the material without the use of it, has better results coming from its reactivity provided by action of the thermal process of degradation. A través de políticas ambientales que propicien una discusión gradual sobre el destino de los residuos producidos en los más diversos sectores industriales, los lodos de depuradora se enfatizan por el destino problemático derivado de la cantidad de compuestos tóxicos que los componen, comprometiendo su disposición final. Partiendo de la necesidad de implementar medidas para mitigar los impactos ambientales a través de la producción de materiales ecoeficientes, actualmente se utiliza como estudio en morteros de revestimiento la aplicación de cenizas de lodos de depuradora sanitaria como sustituto parcial del cemento Portland. Esta sustitución tiene como objetivo, además de reducir el gran volumen de lodos generados por las Estaciones Depuradoras de Aguas Residuales, permitir una atenuación en el consumo de cemento, importante generador de CO2 durante su proceso de fabricación. Se pudo observar que, mediante el uso del residuo calcinado aplicado en morteros, se ratifica un comportamiento físico-mecánico relevante al material, el cual, comparado con el material sin el uso del mismo, tiene mejores resultados derivados de su reactividad proporcionada por la acción de la temperatura de degradación del proceso. Através das políticas ambientais que proporcionam uma paulatina discussão a respeito da destinação dos rejeitos produzidos nos mais diversos setores industriais, o lodo de esgoto é posto em ênfase pela problemática destinação advinda da quantidade de compostos tóxicos que o compõe, comprometendo o seu descarte. A partir da necessidade de implantar medidas mitigadoras dos impactos ambientais através da produção de materiais ecoeficientes, utiliza-se atualmente como estudo, em argamassas de revestimento, a aplicação das cinzas do lodo de esgoto sanitário como substituto parcial do cimento Portland. Essa substituição possui enfoque, além da redução do grande volume de lodo gerado pelas Estações de Tratamento de Esgoto, de possibilitar uma atenuação no consumo de cimento, um grande gerador de CO2 durante seu processo de fabricação. Pôde-se observar que por meio do uso do resíduo calcinado aplicado em argamassas, ratifica-se uma relevante performance físico-mecânica ao material, que comparando ao material sem o uso do mesmo, possui melhores resultados advindos da sua reatividade proporcionada mediante ação do processo térmico de degradação.

Portland cement concrete manufacturing techniques in the world have an immense variability, since each location concentrates natural resources with unique characteristics, sometimes similar, but with always different process conditions, such as: labor, equipment, environmental conditions, processing, storage, among others. The aim of this work is to develop cementitious composites partially replacing mineral admixtures by powdered glass residues, evaluating the physical-mechanical behavior through axial compression strength, as well as the production of hydrated phases through x-ray diffraction, both at 28 days. Cement, silica fume, metakaolin, powder glass residue, polycarboxylic ether-based superplasticizer, and low temperature water were used to prepare different compositions of ultra-high performance concrete. The preparation took place with the aid of a mechanical bench mixer, and the densification was carried out with the aid of an immersion vibrator in cylindrical molds 50 x 100 mm. After unshaped, the specimens received heat treatment, with isotherm at 60°C for 36 hours, followed by wet curing in a tank saturated with calcium hydroxide, until the tests of compression strength and x-ray diffraction were carried out. The results show that the composition added with the residue, replacing metakaolin, behaved in an adequate manner, with compressive strength equivalent to the reference composition (silica fume + metakaolin), as well as the production of the same hydrated compounds. However, the application of only the glass residue or metakaolin reduced the intensity of the pozzolanic reactions, justified by the presence of a high content of calcium hydroxide in the compositions, which allows us to conclude that the powder glass residue presents viability as a filler, when replacing metakaolin in the presence of silica fume, as it does not compromise the performance of the mixtures made. Las técnicas de fabricación de concreto de cemento Portland en el mundo tienen una inmensa variabilidad, ya que cada ubicación concentra recursos naturales con características únicas, a veces similares, pero con condiciones de proceso siempre diferentes, tales como: mano de obra, equipos, condiciones ambientales, procesamiento, almacenamiento, entre otros. El objetivo de este trabajo es desarrollar composites cementosos mediante la sustitución parcial de adiciones minerales por residuo de vidrio en polvo, evaluando el comportamiento físico-mecánico mediante resistencia a la compresión axial, así como la producción de fases hidratadas mediante difracción de rayos X, ambos a 28 días. Se utilizaron cemento, sílice activa, metacaolín, residuos de vidrio, superplastificante a base de éter policarboxílico y agua a baja temperatura para hacer diferentes composiciones de hormigón de ultra alto rendimiento. La preparación se realizó con la ayuda de un mezclador mecánico de mesa y la densificación se realizó con la ayuda de un vibrador de inmersión en moldes cilíndricos de 50 x 100 mm. Después del desmoldeo, las probetas recibieron tratamiento térmico, con isoterma a 60 °C durante 36 horas, seguido de curado húmedo en un tanque de hidróxido de calcio saturado, hasta que se realizaron las pruebas de resistencia a la compresión y difracción de rayos X. Los resultados muestran que la composición añadida con el residuo, en sustitución del metacaolín, se comportó correctamente, con una resistencia a la compresión equivalente a la composición de referencia (sílice activa + metacaolín), así como la producción de los mismos compuestos hidratados. Sin embargo, la aplicación de solo el residuo de vidrio o metacaolín, redujo la intensidad de las reacciones puzolánicas, debido a la presencia de un alto contenido de hidróxido de calcio en las composiciones, lo que nos permite concluir que el residuo de polvo de vidrio es viable como relleno, al reemplazar el metacaolín en presencia de sílice activa, ya que no compromete el rendimiento de las mezclas realizadas. As técnicas de fabricação de concreto de cimento Portland no mundo possuem uma variabilidade imensa, uma vez que cada localidade concentra recursos naturais com características únicas, as vezes similares, mas com condições de processo sempre diferentes, como: mão de obra, equipamentos, condições ambientais, processamento, armazenamento, entre outros. Objetiva-se com esse trabalho desenvolver compósitos cimentícios substituindo parcialmente as adições minerais por resíduos de vidro em pó, avaliando o comportamento físico-mecânico por meio de resistência à compressão axial, bem como a produção de fases hidratadas através de difração de raios-x, ambos aos 28 dias. Utilizou-se cimento, microssílica, metacaulim, resíduo de vidros, superplastificante de base éter policarboxílico, e água em baixa temperatura para confeccionar diferentes composições de concreto de ultra alto desempenho. A preparação ocorreu com auxílio de misturador mecânico de bancada, e o adensamento foi realizado com auxílio de vibrador de imersão em moldes cilíndricos 50 x 100 mm. Após desmolde, os corpos de prova receberam tratamento térmico, com isoterma à 60°C por 36 horas, seguido de cura úmida em tanque saturado de hidróxido de cálcio, até a realização dos ensaios de resistência à compressão e difração de raios-x. Os resultados apontam que, a composição aditivada com o resíduo, substituindo o metacaulim, comportou-se de forma adequada, com resistência à compressão equivalente à composição de referência (microssílica + metacaulim), bem como a produção dos mesmos compostos hidratados. No entanto, a aplicação de apenas o resíduo de vidro ou metacaulim, reduziu a intensidade das reações pozolânicas, justificado pela presença de elevado teor de hidróxido de cálcio nas composições, o que permite concluir que o resíduo do vidro em pó apresenta viabilidade como fíler, ao substituir o metacaulim na presença de microssílica, por não comprometer o desempenho das misturas confeccionadas.

Concrete is a material used in various applications, involving paving, sanitation, infrastructure and superstructure works, dams, bridges, and architectural elements, but for certain applications their physical and mechanical properties are affected by intense degradation agents, motivating the search for artifacts that improve these properties and increase the useful life and durability of matrix materials cement industry. The objective of this work is to clarify the influence of different mix of superplasticizer, steel fibers, water/cement factor, different types of mineral admixtures, besides the type of thermal treatment and method of cylindrical concrete molds of reactive powders, evaluating the resistance to axial compression at the ages of 7 and 14 days. 17 compositions were defined, by mass, for the manufacture of concretes, divided into two stages: the first composed of 10 compositions, and the second by 7 compositions. It was used CP-V ARI cement, sand, metakaolin, silica fume, superplasticizer and kneading water with temperature between 1 and 3°C. After the conformation of the cylindrical molds of dimensions 5x10cm with the aid of a portable immersion vibrator, the specimens were unmolded after 24 hours and received thermal treatment with periods of pre-cure and isotherm that varied according to the defined trait. According to the results obtained, the reduction of the w/c factor and the superplasticizer additive presented higher resistance to compression, however, this reduction in an excessive way impairs the hydration process, implying in the incomplete hydration of all the cement particles, resulting in less resistance. It was observed that the application of thermal treatment and densification by means of layer immersion vibrators acted as essential factors in the increase of the resistances, and that the isotherm time of the composite corroborates the respective increase, until its stabilization, in the temperatures studied. El hormigón es un material utilizado en diversas aplicaciones, que involucran pavimentación, saneamiento, obras de infraestructura y superestructura, presas, puentes y elementos arquitectónicos, pero para determinadas aplicaciones, sus propiedades físicas y mecánicas se ven afectadas por agentes de degradación intensos, motivando la búsqueda de artificios que mejoren dichas propiedades y aumenten la vida útil y durabilidad de los materiales de matriz cementosa. Como objetivo, este trabajo busca estudiar las influencias, en diferentes composiciones, relacionadas con el uso en diferentes cantidades de aditivos y adiciones minerales, fibras de acero, factor agua / cemento, además del tipo de tratamiento térmico y método de densidad adoptado para conformar los moldes. Hormigón cilíndrico a partir de polvos reactivos, evaluando la resistencia a la compresión axial a las edades de 7 y 14 días. Se definieron 17 composiciones, en masa, para la fabricación del material, divididas en dos etapas: la primera compuesta por 10 composiciones, y la segunda por 7 composiciones. Se utilizó cemento CP-V ARI, arena, metacaolín, sílice activa, aditivo superplastificante y agua de amasado con temperatura entre 1 y 3°C. Luego de conformar moldes cilíndricos de dimensiones 5x10cm con la ayuda de un vibrador de inmersión portátil, las probetas fueron tratadas térmicamente con períodos de pre-curado e isoterma que variaban según la línea definida. De acuerdo con los resultados obtenidos, con la reducción del factor a/c el respectivo aumento del aditivo, se obtuvieron mayores resistencias a la compresión, sin embargo, esta reducción excesiva perjudica el proceso de hidratación, implicando la hidratación completa de todas las partículas de cemento, lo que resulta en una menor resistencia. Se observó que la aplicación de tratamiento térmico y densificación mediante vibrador de inmersión estratificado actuó como factores esenciales en el aumento de las resistencias, y que el tiempo de isoterma del composite corrobora el respectivo aumento, hasta su estabilización, en las temperaturas estudiadas. O concreto é um material utilizado em variadas aplicações, envolvendo obras de pavimentação, saneamento, infraestrutura e superestrutura, barragens, pontes, e elementos de arquitetura, porém para determinadas aplicações, as suas propriedades físicas e mecânicas são acometidas por intensos agentes de degradação, motivando a busca de artifícios que melhorem tais propriedades e eleve a vida útil e durabilidade dos materiais de matriz cimentícia. Como objetivo, este trabalho busca estudar as influências, em diferentes composições, relacionadas ao emprego em diferentes quantidades de aditivo e adições minerais, fibras de aço, fator água/cimento, além do tipo de tratamento térmico e método de adensamento adotado para conformação dos moldes cilíndricos de concreto de pós reativos, avaliando a resistência à compressão axial nas idades de 7 e 14 dias. Foram definidas 17 composições, em massa, para fabricação do material, divididas em duas etapas: a primeira composta por 10 composições, e a segunda por 7 composições. Utilizou-se cimento CP-V ARI, areia, metacaulim, microssílica, aditivo superplastificante e água de amassamento com temperatura entre 1 e 3°C. Após a conformação dos moldes cilíndricos de dimensões 5x10cm com auxílio de vibrador de imersão portátil, os corpos de prova foram receberam tratamento térmico com períodos de pré-cura e de isoterma que variaram de acordo com o traço definido. De acordo com os resultados obtidos, com a redução do fator a/c e respectivo aumento do aditivo obteve-se maiores resistências à compressão, todavia essa redução de forma excessiva prejudica o processo de hidratação, implicando na não completa hidratação de todas as partículas de cimento, resultando em menores resistências. Foi observado que a aplicação de tratamento térmico e adensamento por meio de vibrador de imersão em camadas agiram como fatores essenciais no aumento das resistências, e que o tempo de isoterma do compósito corrobora o respectivo aumento, até sua estabilização, nas temperaturas estudadas.

Through environmental policies that provide a gradual discussion about the destination of the tailings produced in the most diverse industrial sectors, the sewage sludge is emphasized by the problematic destination arising from the amount of toxic compounds that compose it, compromising its disposal. Aiming to fulfill the sustainable role through the creation of mechanisms that favor the ecological coexistence between environment and human beings, it is possible through the use of construction materials, considered as conventional, the use of calcined sewage sludge as an enhancer of the properties of matrix materials cement, significantly improving its performance against mechanical stresses and degradation mechanisms. Based on the need to implement measures to mitigate environmental impacts through the production of eco-efficient materials, the ashes of sanitary sewage sludge as a partial substitute for Portland cement have now been used as an input in coating mortars. This substitution focuses on reducing the large volume of sludge generated by the Sewage Treatment Plants, as well as on the reduction in the consumption of cement, a large CO2 generator during its manufacturing process. It was observed that through the use of this calcined by-product applied in mortars, a relevant physical-mechanical performance in cementitious materials is ratified, that in comparison to the material without the use of it, better results are observed, resulting from the reactivity conferred to the sludge after the thermal degradation process, making it a pozzolana. A través de políticas ambientales que brindan una discusión paulatina sobre el destino de los relaves producidos en los más diversos sectores industriales, los lodos de depuradora son enfatizados por el destino problemático derivado de la cantidad de compuestos tóxicos que lo componen, comprometiendo su disposición. Con el objetivo de cumplir con el rol sustentable mediante la creación de mecanismos que favorezcan la convivencia ecológica entre el medio ambiente y el ser humano, es posible mediante el uso de materiales de construcción, considerados como convencionales, el uso de lodos de depuradora calcinados como potenciador de las propiedades de la matriz. materiales cemento, mejorando significativamente su desempeño frente a tensiones mecánicas y mecanismos de degradación. Con base en la necesidad de implementar medidas para mitigar los impactos ambientales a través de la producción de materiales ecoeficientes, las cenizas de los lodos de depuradora sanitaria como sustituto parcial del cemento Portland se han utilizado ahora como insumo en los morteros de revestimiento. Esta sustitución se centra en la reducción del gran volumen de lodos que generan las Plantas de Tratamiento de Aguas Servidas, así como en la reducción del consumo de cemento, gran generador de CO2 durante su proceso de fabricación. Se observó que, mediante el uso de este subproducto calcinado aplicado en morteros, se ratifica un desempeño físico-mecánico relevante en materiales cementosos, que en comparación con el material sin el uso del mismo, se observan mejores resultados, producto de la reactividad conferido al lodo después del proceso de degradación térmica, convirtiéndolo en una puzolana. Através das políticas ambientais que proporcionam uma paulatina discussão a respeito da destinação dos rejeitos produzidos nos mais diversos setores industriais, o lodo de esgoto é posto em ênfase pela problemática destinação advinda da quantidade de compostos tóxicos que o compõe, comprometendo o seu descarte. Objetivando cumprir o papel sustentável mediante a criação de mecanismos que favoreçam a convivência ecológica entre meio ambiente e seres humanos, viabiliza-se através dos materiais de construção, tidos como convencionais, o uso do lodo de esgoto calcinado como potencializador das propriedades de matérias de matriz cimentícia, melhorando significativamente o seu desempenho frente aos esforços mecânicos e mecanismos de degradação. A partir da necessidade de implantar medidas mitigadoras dos impactos ambientais através da produção de materiais ecoeficientes, passou-se a utilizar atualmente como insumo, em experimentos com argamassas de revestimento, as cinzas do lodo de esgoto sanitário como substituto parcial do cimento Portland. Essa substituição possui enfoque na redução do grande volume de lodo gerado pelas Estações de Tratamento de Esgoto, como também na atenuação no consumo de cimento, um grande gerador de CO2 durante seu processo de fabricação. Pôde-se observar que por meio do uso desse subproduto calcinado aplicado em argamassas, ratifica-se uma relevante performance físico-mecânica em materiais cimentícios, que em comparação ao material sem o uso do mesmo, observam-se melhores resultados, advindos da reatividade conferida ao lodo posterior ao processo térmico de degradação, tornando-a uma pozolana.

Through the environmental perspective of producing new construction materials with the inclusion of tailings or residues that improve their properties and, at the same time, promote a practice that mitigates environmental impacts, the objective of this work is to diagnose the effect of incorporating scheelite- tailings as recycled aggregate in soil-cement bricks, partially replacing the soil, seeking to make its use feasible in interlocking pavements, as well as studying the physical-chemical properties of the mixing water used in the making of soil-cement bricks, originating from drains air conditioning system at IFPB Campus Campina Grande. The bricks produced used CP II Z-32 class cement, landfill cut-off soil for disposal, scheelite-tailings, and kneading water from air conditioning drains at the IFPB Campus Campina Grande. Conformation was performed manually with the aid of a hydraulic press, with subsequent curing at room temperature and periodic wetting during the first 7 days of cement hydration (alkaline stabilizer), until the ages of laboratory tests of compressive strength reached (28 days) and direct flexion (180 days). It was noted that the results of compressive strength exceeded the minimum limits of ABNT NBR 10834:2013, as well as the results of the flexion test demonstrated that the mechanical strength of the bricks is superior when incorporating the mineral tailings, a phenomenon also noticed through of the compressive strength test. The quality of the water used to manufacture the bricks, in addition to ensuring better chemical potential in the hydration reaction based on the state of the art, promotes a reduction in the use of water from the public supply, which comes from a relatively low water source. Mediante de la perspectiva ambiental de producir nuevos materiales de construcción con la inclusión de relaves o residuos que mejoren sus propiedades y, al mismo tiempo, promuevan una práctica que mitigue los impactos ambientales, el objetivo de este trabajo es diagnosticar el efecto de incorporar residuos de la extracción de scheelita como agregado reciclado en ladrillos sólidos suelo-cemento, reemplazando parcialmente el suelo, buscando viabilizar su uso en pavimentos entrelazados, así como estudiando las propiedades físico-químicas del agua de amasado utilizada en la fabricación de ladrillos suelo-cemento, procedente de los desagües del sistema de aire acondicionado de la IFPB Campus Campina Grande. Los ladrillos producidos utilizaron cemento clase CP II Z-32, tierra de corte de relleno sanitario para eliminación, desechos minerales de scheelita y agua de amasado de los desagües de aire acondicionado en el IFPB Campus Campina Grande. La conformación se realizó manualmente con ayuda de una prensa hidráulica, con posterior curado a temperatura ambiente y humedecimiento periódico durante los primeros 7 días de hidratación del cemento (estabilizador alcalino), hasta alcanzar las edades de los ensayos de laboratorio de resistencia a la compresión axial (28 días) y flexión directa (180 días). Se notó que los resultados de resistencia a la compresión axial excedieron los límites mínimos de ABNT NBR 10834:2013, así como los resultados del ensayo de flexión demostraron que la resistencia mecánica de los ladrillos es superior al incorporar el residuo mineral, fenómeno también notado a través de la prueba de compresión axial. La calidad del agua utilizada para fabricar los ladrillos, además de asegurar un mejor potencial químico en la reacción de hidratación basada en el estado de la técnica, promueve una reducción en el uso de agua del suministro público, que proviene de un agua relativamente baja fuente. Através da perspectiva ambiental em produzir novos materiais de construção com inclusão de rejeitos ou resíduos que melhorem suas propriedades e, ao mesmo tempo, promovam uma prática mitigadora dos impactos ambientais, objetiva-se com esse trabalho diagnosticar o efeito da incorporação do rejeito da extração da scheelita como agregado reciclado em tijolos maciços de solo-cimento substituindo parcialmente o solo, buscando viabilizar seu uso em pavimentos intertravados, bem como, estudar as propriedades físico-químicas da água de amassamento utilizada na confecção dos tijolos de solo-cimento, oriunda dos drenos de ar condicionado do IFPB Campus Campina Grande. Os tijolos produzidos utilizaram cimento de classe CP II Z-32, solo de recorte de aterro para descarte, rejeito mineral da scheelita, e água de amassamento proveniente de drenos de ar condicionado do IFPB Campus Campina Grande. A conformação foi realizada manualmente com o auxílio de prensa hidráulica, com posterior cura à temperatura ambiente e molhagem periódica durante os 7 primeiros dias de hidratação do cimento (estabilizador alcalino), até atingirem as idades de realização dos testes laboratoriais de resistência à compressão axial (28 dias) e flexão direta (180 dias). Notou-se que os resultados de resistência à compressão axial superaram os limites mínimos da ABNT NBR 10834:2013, como também, os resultados do teste de flexão demonstraram que a resistência mecânica dos tijolos é superior quando incorporado o rejeito mineral, fenômeno também notado através do teste de compressão axial. A qualidade da água utilizada para fabricar os tijolos, além de assegurar melhor potencial químico na reação de hidratação com base no estado da arte, promove a redução do uso da água do abastecimento público, que advém de manancial com aporte hídrico relativamente reduzido.

The exponential advancement of cutting-edge technologies in the scope of civil construction, seeks to give cement-based materials the eco-efficient potential linked to mechanical performance that enables different applications. This work aims to evaluate the glass residue regarding the pozzolanic potential through ABNT NBR 5752:2014, as well as to verify whether through the characterization tests of x-ray fluorescence, x-ray diffraction and laser diffraction granulometry, if it is viable of application as supplementary cementitious material (filler), in ultra-high performance concrete. The glass residue submitted to the tests proposed in this study, was crushed in a jaw crusher, milled in a bench ball mill at 47 rpm, and was sieved in a 75 µm opening mesh (ABNT nº 200 mesh). For the test of pozzolanic activity, CP II F-40 class cement, normal sand, water from the public supply network, and superplasticizer additive were used for the mix with 25% of the residue replacing cement, while for the other characterization techniques, the glass residue was applied in its processed form (after sieving), dry or wet. The evaluated glass residue did not reach the minimum rate of 75% established by ABNT NBR 5752:2014, achieving only 45.72%, being classified as non-pozzolanic, which indicates its inert behavior in the presence of calcium hydroxide. The characterization tests confirmed, based on the specialized literature on ultra-high performance concrete, its viability as a filler when adopted as an alternative raw material for presenting chemical and mineralogical composition, in addition to granulometric distribution, very close to those used in studies that demonstrated satisfactory results when using the glass residue as an input. El avance exponencial de las tecnologías de punta en el ámbito de la construcción civil, busca dotar a los materiales cementosos del potencial ecoeficiente ligado al desempeño mecánico que permite diferentes aplicaciones. Este trabajo tiene como objetivo evaluar el residuo de vidrio en cuanto al potencial puzolánico mediante ABNT NBR 5752:2014, así como verificar si a través de las pruebas de caracterización de fluorescencia de rayos X, difracción de rayos X y granulometría de difracción láser, si es viable de aplicación como material cementoso suplementario (masilla), en hormigón de ultra altas prestaciones. El residuo de vidrio sometido a las pruebas propuestas en este estudio, se trituró en trituradora de mandíbulas, se trituró en un molino de bolas de banco a 47 rpm y se tamizó en una malla de apertura de 75 µm (tamiz ABNT nº 200). Para la prueba de actividad puzolánica se utilizó cemento clase CP II F-40, arena normal, agua de la red de abastecimiento público y aditivo superplastificante para la mezcla con 25% del residuo en sustitución del cemento, mientras que, para las demás técnicas de caracterización, el residuo de vidrio se aplicó en su forma procesada (después del tamizado), seco o húmedo. El residuo de vidrio evaluado no alcanzó la tasa mínima del 75% establecida por ABNT NBR 5752:2014, logrando solo el 45,72%, siendo clasificado como no puzolánico, lo que indica su comportamiento inerte en presencia de hidróxido de calcio. Los ensayos de caracterización confirmaron, con base en la literatura especializada sobre hormigones de ultra alto rendimiento, su viabilidad como relleno al ser adoptado como materia prima alternativa para presentar composición química y mineralógica, además de distribución granulométrica, muy cercana a las empleadas en estudios que demostraron Resultados satisfactorios al utilizar el residuo de vidrio como insumo. O avanço exponencial das tecnologias de ponta no âmbito da construção civil, busca conferir aos materiais de base cimentícia o potencial ecoeficiente atrelado ao desempenho mecânico que possibilite aplicações diversas. Este trabalho objetiva avaliar o resíduo de vidro quanto ao potencial pozolânico através da ABNT NBR 5752:2014, bem como verificar se através dos ensaios de caracterização de fluorescência de raios x, difração de raios x e granulometria por difração a laser, se o mesmo possui viabilidade de aplicação como material cimentício suplementar (fíler), em concreto de ultra alto desempenho. O resíduo de vidro submetido aos ensaios propostos neste estudo, passou por trituração em britador de mandíbulas, moagem em moinho de bolas de bancada à 47rpm, e foi peneirado em malha de abertura de 75 µm (peneira ABNT n° 200). Para o teste de atividade pozolânica, utilizou-se cimento de classe CP II F-40, areia normal, água proveniente da rede de abastecimento público, e aditivo superplastificante para o traço com 25% do resíduo em substituição ao cimento, enquanto que para as demais técnicas de caracterização, o resíduo de vidro foi aplicado na sua forma beneficiada (após peneiramento), por via seca ou úmida. O resíduo de vidro avaliado não alcançou o índice mínimo de 75% estabelecido pela ABNT NBR 5752:2014, conseguindo apenas 45,72%, sendo classificado como não pozolânico, o que indica seu comportamento inerte na presenta do hidróxido de cálcio. Os ensaios de caracterização confirmaram, com base na literatura especializada sobre concreto de ultra alto desempenho, sua viabilidade como fíler ao ser adotado como matéria-prima alternativa por apresentar composição química e mineralógica, além de distribuição granulométrica, bastante próximas dos utilizados em estudos que demonstraram resultados satisfatórios ao utilizarem o resíduo de vidro como insumo.

It is noticeable the increase in the demand for non-renewable raw materials for applications in the most varied segments of civil construction, which in fact causes more significant damage to the environment, whether through the waste generated during extraction, during use, or after use. In this sense, this work aims to present the state-of-the-art corresponding to the concretes currently developed, emphasizing those of a sustainable scope that corroborate the ecological proposal in the use of residues and/or tailings from different sectors of industrial production, in order to partially settle the slag produced by converting them into raw materials for reuse. The increase in proposals to mitigate environmental impacts with a focus on using these wastes becomes evident. The corresponding study area requires greater expansion of the employment possibilities for improving the technique of incorporating waste into concrete with due observance of the dosage, consumption, packing factor when necessary, density of materials involved, and application aspect of the composite. Se nota el aumento de la demanda de materias primas no renovables para aplicaciones en los más variados segmentos de la construcción civil, lo que de hecho aporta un mayor daño al medio ambiente, ya sea por los residuos generados durante la extracción, durante el uso y después del uso. En este sentido, este trabajo tiene como objetivo hacer una presentación del estado del arte correspondiente a los hormigones actualmente desarrollados, destacando los de alcance sustentable que corroboran la propuesta ecológica en el aprovechamiento de residuos y/o relaves de diferentes sectores de la producción industrial, con el fin de sedimentar parcialmente. la escoria producida, convirtiéndola en materia prima para su reutilización. Se evidencia el incremento de propuestas de mitigación de impactos ambientales con foco en el aprovechamiento de estos residuos, lo que requiere, dentro del área de estudio correspondiente, una mayor ampliación de las posibilidades de empleo para mejorar la técnica de incorporación de residuos al hormigón, con la debida observancia. dosis, consumo, factor de empaque cuando sea necesario, densidad de los materiales involucrados y aspecto de aplicación del compuesto. É notadamente perceptível o aumento pela demanda de matérias-primas não renováveis para aplicações nos mais variados segmentos da construção civil, o que de fato proporciona maiores deteriorações ao meio ambiente, seja através dos resíduos gerados na extração, durante o uso e depois do uso. Nesse sentido, este trabalho objetiva realizar uma apresentação do estado da arte correspondente aos concretos desenvolvidos atualmente, enfatizando os de âmbito sustentável que corroborem a proposta ecológica na utilização de resíduos ou rejeitos provenientes de diferentes setores de produção industrial, a fim de dirimirem parcialmente a escória produzida, convertendo-as em matérias-primas para reuso. Torna-se evidente o aumento das propostas de mitigar os impactos ambientais com foco no uso desses rejeitos, o que necessita, dentro da correspondente área de estudo, maiores ampliações das possibilidades de emprego para aperfeiçoamento da técnica de incorporação de resíduos em concretos, com observância na dosagem, no consumo, no fator de empacotamento quando necessário, na densidade dos materiais envolvidos e no aspecto de aplicação do compósito.

O presente artigo tem o intuito de descrever a prática de extensão do EDIFICAR Escritório Modelo que atua na cidade de Campina Grande - PB com sede do Instituto Federal de Educação, Ciência e Tecnologia da Paraíba. O EDIFICAR disponibiliza de forma gratuita projetos de arquitetura e de engenharia para população de baixa renda, colocando em exercício as diretrizes da Lei 11.888/2008, que garante o direito à assistência técnica pública e gratuita para cidadãos carentes, residentes de moradias localizadas em zonas de recuperação urbana e/ou interesse social. O artigo traz à tona a importância da garantia do direito supracitado, bem como descreve os serviços prestados pelo escritório modelo, apresentando alguns casos práticos já executados dentro da comunidade em estudo, objetivando despertar no leitor a importância do seu papel social na comunidade em que vive, e a compreensão da relevância do desenvolvimento de tais projetos dentro desta temática.