Search

Bi2O3–PbO–CdO–B2O3 glass samples were prepared via melt quenching. The substitution of Bi2O3 for B2O3 resulted in a continuous increase in density from 4.334 to 5.742 g/cm3. The molar volume (V m) gradually increased from 37.197 to 38.429 cm3/mol when the Bi2O3 level increased from 10 to 25 mol%. With the addition of Bi2O3 from 10 to 25 mol%, Young’s, bulk, shear, and longitudinal modulus reduced from 40.80 to 35.07 GPa, 22.92 to 19.97 GPa, 16.95 to 14.52 GPa, and 45.53 to 39.33 GPa, respectively. These glasses are bendable rather than elongated and can withstand longitudinal stress over shear stress. Radiation protection qualities were investigated using EpiXS software, which is based on the ENDF/B-VIII EPICS2017 library, between 122 and 1275 keV. The mass attenuation coefficients are substantially higher at low energies. The radiation shielding properties of Bi2O3–PbO–CdO–B2O3 glasses were improved by replacing B2O3 with Bi2O3. Quantifying this improvement is critical in developing compact radiation shielding employing this glass system.

In this study, four tellurite–germanate glasses containing zinc, lithium, and bismuth with varied Bi2O3 and TeO2 amounts were investigated. The mechanical qualities of sample glasses were investigated and associated with their structural properties. Furthermore, the radiation-shielding capabilities of N1–N4 glasses were evaluated at 0.662 MeV using EPICS2017. The radiation-shielding characteristics were compared with the radiation-shielding parameters published in the literature for various glass systems. When TeO2 was replaced with Bi2O3, Young’s and bulk moduli of the material decreased. The L values of glasses were higher than their S values (14–13 GPa), indicating that they can tolerate longitudinal stress better than shear stress and can be bent rather than elongated readily. The MACs calculated were comparable to those obtained using WinXcom. The tenth-value layer (TVL) of all of the sample glasses was higher than that of the bismuth aluminosilicate glasses. All of the borate glass systems containing bismuth, sodium, and antimony had lower TVLs than N1–N3 glasses. The half-value layer was more in the N4 glass with the greatest Bi2O3 content than those in 50 and 60 mol% PbO-containing strontium borate glasses.

This paper presents a comprehensive examination of the thermoluminescence properties of BaMgAl10O17: Ce (BAM: Ce) phosphors, which were synthesized via the combustion method. The study employs five distinct approaches to determine the kinetic parameters for individual traps. To investigate the structural, morphological, and elemental composition of the samples, X-ray diffraction, scanning electron microscopy, and energy-dispersive X-ray spectroscopy were utilized. The photoluminescence spectra revealed a broad emission centered around 420 nm upon 330 nm excitation. By subjecting the phosphors to γ doses ranging from 5 to 5 kGy and conducting TL glow curve analysis, the kinetic characteristics of the BAM: Ce phosphors were determined. The linear dose–response was observed for 5–50 Gy, indicating a high sensitivity value. Additionally, there is a consistent estimation of trap energy across various methods. It is also worth noting that the phosphor exhibits a very low minimum detectable dose, estimated to be in the microgray range, making BAM: Ce a strong candidate for low gamma dosimetry applications. [ABSTRACT FROM AUTHOR]

A novel glass system B2O3–SiO2–Bi2O3–TeO2–BaO–ZnO doped with Eu2O3 (x = 0–4 mol%) is fabricated through melt-quench technique and coded as BiTeEu-x. Density and refractive index measurements done on the glasses resulted in the increase up to 5.4377 gcm−3 and 1.99, respectively, for 4 mol% addition of Eu2O3. Vickers micro-indentation measurements done on synthesized glasses gave increasing microhardness values with Eu3+ doping due to higher bond strength of Eu–O bond compared to Te–O bond. The Phy-X/PSD simulation software utilized for obtaining radiation shielding parameters produced highest range of mass attenuation coefficient (63.878–0.036 cm2/g) and lowest range of half-value layer (0.002–3.551 cm) for the same glass proving its superiority in radiation attenuating capacity. This article addresses the theoretical analysis of photon buildup occurring inside the fabricated glasses in 0.015–15 MeV energy range with respect to different penetration depths. Neutron shielding ability of BiTeEu-4 glass was found to be impressive with fast neutron removal cross section (FNR) value of 0.10362 cm−1. [ABSTRACT FROM AUTHOR]

Trivalent erbium ions doped (48 – x) AlPO4 + 15K2O + 12MgF + 20Na2O + 5NaF + xEr2O3 glass samples have been prepared utilizing the melt-quench process and studied to understand the efficacy of Er3+ ions content on physical, structural and luminescence attributes of host glass. The functional groups of the glass structure such as metaphosphate, orthophosphate and pyrophosphate have been elucidated through Fourier Transform Infrared (FTIR) spectroscopic investigation. The least-square approach was used to calculate the Judd–Ofelt parameter from the oscillator strength of the Er3+ ion transitions. The luminescence emission data captured in the visible and near-infrared (NIR) province using 380 and 980 nm excitation wavelengths. The up-conversion (recorded at the excitation at 980 nm) of 0.5 Er glass exhibited emission at 664, 550 and 488 nm wavelengths. The decay plots of the studied glass specimens were measured at 980 nm excitation. The McCumber (MC) theory has been implemented to calculate the gain coefficient of the 0.5 Er glass and flat gain curve was drawn for S-band, C-band and L-band. The attributes for optical amplification were ascertained, including the quality factor (0.85), branching ratio (1), stimulated emission cross-section (1.3 × 10–20 cm2), gain bandwidth (1.26 × 10–25 cm3) and optical gain (0.394 × 10–23 cm2 s) for 0.5 Er glass. The yellowish green light emission ability of the 0.5 Er glass after 980 nm excitation evident through CIE co-ordinates position (x 0.36, y 0.58) at 1931 CIE chromaticity diagram. The spectroscopic and luminescence results endorse that the alumino–phosphate glass specimens loaded with 0.5 mol% of Er2O3 are beneficial for NIR and green light emission applications. [ABSTRACT FROM AUTHOR]

Ultra‐high thermally stable Ca2MgWO6:xSm3+ (x = 0.5, 0.75, 1, 1.25, and 1.5 mol%) double perovskite phosphors were synthesized through solid‐state reaction method. Product formation was confirmed by comparing the X‐ray diffraction (XRD) patterns of the phosphors with the standard reference file. The structural, morphological, thermal, and optical properties of the prepared phosphor were examined in detail using XRD, Fourier transform infrared spectra, scanning electron microscopy, diffused reflectance spectra, thermogravimetric analysis (TGA), photoluminescence emission, and temperature‐dependent PLE (TDPL). It was seen that the phosphor exhibited emission in the reddish region for the near‐ultraviolet excitation with moderate Colour Rendering Index values and high colour purity. The optimized phosphor (x = 1.25 mol%) was found to possess a direct optical band gap of 3.31 eV. TGA studies showed the astonishing thermal stability of the optimized phosphor. Additionally, near‐zero thermal quenching was seen in TDPL due to elevated phonon‐assisted radiative transition. Furthermore, the anti‐Stokes and Stokes emission peaks were found to be sensitive toward the temperature change and followed a Boltzmann‐type distribution. All these marked properties will make the prepared phosphors a suitable candidate for multifield applications and a fascinating material for further development. [ABSTRACT FROM AUTHOR]