Search

Objectives: The development of dental adhesives with enhanced bond strength has assisted minimally invasive dentistry. The aim of this study was to evaluate the fracture load and stress distribution pattern of two retainer designs for posterior cantilever resin bonded fixed dental protheses (RBFDPs). Materials and Methods: Forty human mandibular molars were divided into two groups according to the retainer design; lingual coverage (LC) and occlusal coverage (OC) retainers. Each main group was then divided according to the number of inlay boxes (n = 10); one inlay and two inlay boxes. High translucency (3Y) zirconia was used to manufacture all restorations, and a dual‐polymerizing adhesive resin cement was used for bonding. All specimens underwent 10,000 cycles of thermocycling (5–55°C), 240,000 cycles of dynamic loading (50 N, descending speed v = 30 mm/second, frequency = 1.6 Hz), and failure load test. Both one‐way and two‐way ANOVA tests were used to analyze the data. The four models included in the in‐vitro study are part of the finite element analysis (FEA). When the restorations failed, maximal principal stress values on restorations, enamel, dentin, and luting resin were investigated. Results: A statistically significant (p = 0.018) higher failure load was recorded for OC1 (627.00 ± 153.4 N) than the other groups; (548.0 ± 75.6 N, 521.20 ± 11.3 N, and 509.20 ± 14.9 N for LC1, LC2, and OC2, respectively). With regard to failure mode, one inlay box designs showed more favorable failure pattern than those of two inlay boxes. FEA showed higher stress magnitude transmitted to the tooth structure in models LC2 and OC2. Conclusions: Lingual coverage and occlusal coverage retainers are promising designs capable to withstand the normal occlusal force for cantilever RBFDP in premolar area. The use of two inlay boxes decreased the fracture load of the two retainer designs and increased the stress transmitted to the tooth and resulted in high incidence of catastrophic failure. Clinical Significance: Monolithic high translucent zirconia RBFDP could be considered as a viable treatment option to substitute missing posterior tooth, with improved esthetics and biocompatibility. [ABSTRACT FROM AUTHOR]

Purpose: To evaluate the influence of retainer design and ceramic materials on the durability of minimally invasive cantilever resin-bonded fixed dental prostheses (RBFDPs) after artificial aging. Methods: One hundred caries-free human mandibular molars were prepared as abutments for all-ceramic cantilevered fixed dental prostheses using the following retainer designs: One wing (OW), Two wings (TW), Inlay ring (IR), Lingual coverage (LC), and Occlusal coverage (OC). Two ceramic materials were used: monolithic high translucent zirconia(z) and zirconia-reinforced lithium disilicate (ZLS2) (n=10). All restorations were adhesively bonded with resin cement. The thermocycling of the specimens were performed between 5°C and 55°C for 10,000 cycles and then exposed to 240.000 cycles of dynamic loading on a chewing simulator. All surviving specimens were loaded onto the pontic until failure using a universal testing machine. Results: The mean failure load ranged from 124.00 to 627.00 N for the zirconia groups and from 133.30 to 230.00 N for the ZLS2 groups. Regarding the materials, a significantly higher failure load was recorded in the zirconia groups than in the ZLS2 groups (P<0.001), except for OW (P=0.748). Regarding the retainer designs, a significant different failure load was recorded between the different designs except for IR and LC in the zirconia groups, IR and OC, OW and TW, and TW and LC in the ZLS2 groups (P<0.001). Conclusions: Zirconia IR, LC, and OC can be used as cantilever RBFDP in the premolar region. The fracture resistance of the ZLS2 design was below the normal bite force and should not be recommended as the first option. [ABSTRACT FROM AUTHOR]

Purpose: To evaluate the fracture load and stress magnitude of different retainer designs of minimally invasive cantilever resin‐bonded fixed dental prostheses (RBFDPs) after artificial aging. Materials and methods: Fifty caries‐free human mandibular molars were prepared as abutments for cantilever fixed dental prostheses using different retainer designs: one wing (OW), two wings (TW), inlay ring (IR), lingual coverage (LC), and occlusal coverage (OC). Computer‐aided design and computer‐aided manufacturing were used for milling the RBFDPs using fiber‐reinforced composite (FRC), and the restorations were adhesively bonded. The specimens were then subjected to thermomechanical aging and loaded until failure. The 3D finite element analysis (FEA) was performed with five models of retainer designs similar to the in vitro test. Modified von Mises stress values on enamel, dentine, luting resin, and restorations were examined. Data were analyzed with Kruskal–Wallis and Mann–Whitney U tests (p < 0.001). Results: A statistically significant difference (p < 0.001) was found between all groups except between IR and LC and between OW and TW designs, with the highest mean failure load detected for OC (534.70 N) and the lowest detected for OW (129.80 N). With regard to failure mode, OW, TW, and LC showed more incidences of favorable failure patterns than IR and OC designs. FEA showed that FRC transmitted low stresses in tooth structure and high stresses to the luting resin. Conclusions: LC and OC designs can be used to design cantilever RBFDPs in premolar area. IR design transmitted more stresses to the tooth structure and resulted in 30% catastrophic failure. OW and TW were below the normal occlusal force and should be carefully used. [ABSTRACT FROM AUTHOR]