Search

The paper aims to evaluate the effect of chemical composition on the Hot Cracking Susceptibility (HCS) using mechanical and non-mechanical hot cracking criteria during solidification. The criteria were SKK as a mechanical criterion. Feurer, Clyne Davis, and Katgerman as non-mechanical criteria. The criteria were implemented at various parameters to evaluate their abilities in the hot cracking susceptibility (HCS) prediction at varied chemical composition. In this study, The Mg content was varied in Al9Zn (1, 1.5, 2, 2.5 %wt.) Mg2Cu alloys and Cu content in Al9Zn2Mg (1, 1.5, 2, 2.5 %wt.) Cu alloys. The validation of the result is also conducted by comparing with the experimental data. Based on Feurer criterion, The hot cracking initiates at lower temperature and at higher critical rate of feeding and shrinkage with Cu content, and the hot cracking initiates at higher temperature with Mg content, and it initiates at higher critical rate of feeding and shrinkage from 1 up to 1.5 of Mg, and the critical rate of feeding and shrinkage remains constant from 1.5 up to 2.5 of Mg. Based on Clyne & Davies, the HCS decreases with Cu content from 1 up to 2 of Cu, and it increases from 2 up to 2.5 of Cu. The HCS decreases with Mg content from 1 up to 2 of Mg, and it remains constant from 2 up to 2.5 of Mg. Based on Katgerman criterion, the HCS decreases with Cu content from 1 up to 1.5 of Cu, it increases from 1.5 up to 2 of Cu, and it decreases from 2 up to 2.5 of Cu. The HCS decreases sequentially with Mg content. Based on SKK criterion, the HCS curves shift to the right with Cu content which means that the hot cracking initiates at lower temperature, and the HCS curves shift to the left with Mg content which means that the hot cracking initiates at higher temperature with Mg content. The Feurer, Clyne & Davies, and some specific range for SKK criteria are in agreement for the effect of Cu content on HCS of alloys, and Katgerman and some specific range for Clyne&, Green Open Access added to TU Delft Institutional Repository 'You share, we take care!' - Taverne project https://www.openaccess.nl/en/you-share-we-take-care Otherwise as indicated in the copyright section: the publisher is the copyright holder of this work and the author uses the Dutch legislation to make this work public., Team Joris Dik

Over the last 4 decades, remarkable progress has been made in the modelling of casting processes. The development of casting models is well reflected in the proceedings of the 15 Modelling of Casting, Welding and Advanced Solidification Processes (MCWASP) conferences that have been held since 1980. Computer simulations have enabled a better understanding of the physical phenomena involved during solidification. Modelling gives the opportunity to uncouple the physical processes. Furthermore, quantities that are difficult or impossible to measure experimentally can be calculated using computer simulations e.g. flow patterns and recalescence. However, when it comes to accurately predicting casting performance and in particular, the occurrence of defects like cracks, segregation and porosity there is certainly some way to go. In this paper, the current understanding of the main mechanisms of defect formation during shape and DC casting processes will be reviewed and requirements will be discussed to give a direction to making casting models more predictive and quantitative., Team Jilt Sietsma

AA7050 is an aluminum alloy with superior mechanical properties; however, it is prone to hot tearing (HT) during its production via direct-chill casting. This study focuses on extracting constitutive parameters of the alloy thermomechanical behavior in semi-solid state as well as gaining insight in its failure behavior. Tensile tests were performed using an Instron 5944 at solid fractions between 0.85 (550 °C) and 1.0 (465 °C), at deformation rates of 0.2 and 2 mm/min. The results showed that there are three mechanical behavior regimes in this solid fraction range: ductile at 1.0 (T = 465 °C) ≤ fs < 0.97 (T = 473 °C), brittle at 0.97 (T = 473 °C) ≤ fs ≤ 0.9 (T = 485 °C) and then ductile again (at 0.9 (T = 485 °C) < fs ≤ 0.85 (T = 550 °C)). Fracture surface analysis revealed that the fracture mode was mostly intergranular with fracture propagating through solid bridges as well. Semi-solid constitutive parameters were obtained by making a simple thermal model and numerical tensile tests in ALSIM software package and comparing the simulation results with experimental mechanical tests. The extracted constitutive parameters and available information from the literature support the fact that AA7050 is more susceptible to HT than AA5182 and Al-2 wt pct Cu alloys. The obtained parameters can further enhance the predictive capability of computer simulations of direct-chill casting., Green Open Access added to TU Delft Institutional Repository 'You share, we take care!' - Taverne project https://www.openaccess.nl/en/you-share-we-take-care Otherwise as indicated in the copyright section: the publisher is the copyright holder of this work and the author uses the Dutch legislation to make this work public., Team Jilt Sietsma

Hot tearing is one of the most severe and irreversible casting defects for many metallic materials. In 2004, Eskin et al. published a review paper in which the development of hot tearing of aluminium alloys was evaluated (Eskin and Suyitno, 2004). Sixteen years have passed and this domain has undergone considerable development. Nevertheless, an updated systematic description of this field has not been presented. Therefore, this article presents the latest research status of the hot tearing during the casting of aluminium alloys. The first part explains the hot tearing phenomenon and its occurrence mechanism. The second part presents a detailed description and analysis of the characterisation methods of the mushy zone mechanical properties and hot tearing susceptibility. The third part presents considerable data pertaining to the mushy zone behaviour, including those of the linear contraction and load behaviour during solidification, semi-solid strength and ductility, and characteristic points related to hot tearing. The fourth part examines the effect of the composition and casting process parameters on the hot tearing susceptibility of aluminium alloys. The fifth part describes the hot tearing simulations and the associated criteria and mechanisms. Finally, recommendations for the further development of hot tearing research are presented., Green Open Access added to TU Delft Institutional Repository 'You share, we take care!' - Taverne project https://www.openaccess.nl/en/you-share-we-take-care Otherwise as indicated in the copyright section: the publisher is the copyright holder of this work and the author uses the Dutch legislation to make this work public., Team Jilt Sietsma