This study evaluated the effect of topical fluoride application on enamel hardness after in-office bleaching. Twelve human incisors were cut along the long axis, resulting in 24 halves used in four treatment groups ( n = 6 in each group): (i) untreated group (C); (ii) in-office bleaching material (B); (iii) treatment with surface reaction-type prereacted glass-ionomer varnish after in-office bleaching (B+ PRG); and (iv) treatment with acidulated phosphate fluoride solution after bleaching (B+F). All specimens were subjected to pH-cycling for 4 wk. Knoop hardness was measured using a Cariotester. The decalcification of enamel was assessed quantitatively by measuring the integrated mineral loss (Δ IML). Games-Howell analysis was used to assess statistical significance of between-group differences. The Knoop hardness decreased significantly after bleaching for all groups. In treatment groups B+ PRG and B+F, the Knoop hardness returned to the original unbleached values after the first pH cycle and did not change afterwards. In treatment groups C and B there was a gradual decrease in the Knoop hardness until the fourth pH cycle. The integrated mineral loss, Δ IML, was significantly higher in treatment group B+F after 2 wk than in the other treatment groups. After 4 wk, the Δ IML in treatment group B was significantly higher than in treatment group B+ PRG. The application of fluoride-containing materials after bleaching results in recuperation of hardness to levels similar to those of unbleached enamel. [ABSTRACT FROM AUTHOR]

Background: This study aimed to evaluate the color matching, light transmittance, and reflectance characteristics of the novel flowable resin composite OCF-001 (OCF). Methods: Fifty-four resin composite molds were made with simulated class I cavities of A2, A3, and A4 shades by filling the rubber mold interspace with Estelite Sigma Quick (ESQ), Gracefil Putty (GP) and Filtek Supremme Ultra (FSU). After applying the adhesive, three different flowable resin composites (n = 6), OCF, Gracefil LoFlo (GLF), and Supreme Ultra Flowable (SUF), were used to fill the cavities. A colorimeter was used to measure the color parameters (CIEDE2000). The color measurements were taken immediately and after 28 days. Data were analyzed using the nonparametric Kruskal–Wallis (α = 0.05) and Wilcoxon tests. The light transmittance and reflection characteristics were measured with a black background using a spectrophotometer under D65 illumination. Results: The ΔE00, and ΔC of OCF was lower than other tested materials in A2 and A3 shades both immediately and after 28 days. OCF showed the highest transmittance characteristic, and a relatively stable reflectance curve in all the wavelengths. Conclusions: OCF showed better shade matching with the surrounding shades of A2 and A3, a relative uniform reflectance and higher light transmission properties. [ABSTRACT FROM AUTHOR]