The InAlN alloy system has bandgap energies that span the entire visible range and is a promising candidate for bandgap engineering. To facilitate bandgap engineering, the bandgap bowing for the entire composition range must be well characterized. In rich InxAl1−xN (x > 0.60), films were grown via plasma assisted molecular beam epitaxy on freestanding GaN substrates. The InxAl1−xN film compositions were determined using high resolution X-ray diffraction. On-axis 0002 ω-2θ scans were used to determine the c spacing of the films, reciprocal space maps of the 1 ¯ 015 peaks were used to determine that the films were completely relaxed, and the film compositions were calculated from that information assuming Vegard's law. The bandgaps were independently measured using absorbance spectroscopy and fitting to the linear region of a Tauc plot (dependence of α2 hν on hν) as determined by interpolating the second derivative of the data and selecting a region of low curvature. Compared with the literature, the data were fit to a composition-independent bandgap bowing model, and a bowing parameter of b = 4.0 ± 0.2 eV was calculated, which is consistent with previous results. [ABSTRACT FROM AUTHOR]

The dependence of electron mobility on growth conditions and threading dislocation density (TDD) was studied for n--GaN layers grown by ammonia-based molecular beam epitaxy. Electron mobility was found to strongly depend on TDD, growth temperature, and Si-doping concentration. Temperature-dependent Hall data were fit to established transport and charge-balance equations. Dislocation scattering was analyzed over a wide range of TDDs (∼2×106 cm-2 to ∼2×1010 cm-2) on GaN films grown under similar conditions. A correlation between TDD and fitted acceptor states was observed, corresponding to an acceptor state for almost every c lattice translation along each threading dislocation. Optimized GaN growth on free-standing GaN templates with a low TDD (∼2×106 cm-2) resulted in electron mobilities of 1265 cm2/Vs at 296K and 3327 cm2/Vs at 113 K. [ABSTRACT FROM AUTHOR]