Search

The temperature-dependent intensities of the exciton (X) and biexciton (XX) peaks from single GaAs cone–shell quantum dots (QDs) are studied with micro photoluminescence (PL) at varied excitation power and QD size. The QDs are fabricated by filling self-assembled nanoholes, which are drilled in an AlGaAs barrier by local droplet etching (LDE) during molecular beam epitaxy (MBE). This method allows the fabrication of strain-free QDs with sizes precisely controlled by the amount of material deposited for hole filling. Starting from the base temperature T = 3.2 K of the cryostat, single-dot PL measurements demonstrate a strong enhancement of the exciton emission up to a factor of five with increasing T. Both the maximum exciton intensity and the temperature Tx,max of the maximum intensity depend on excitation power and dot size. At an elevated excitation power, Tx,max becomes larger than 30 K. This allows an operation using an inexpensive and compact Stirling cryocooler. Above Tx,max, the exciton intensity decreases strongly until it disappears. The experimental data are quantitatively reproduced by a model which considers the competing processes of exciton generation, annihilation, and recombination. Exciton generation in the QDs is achieved by the sum of direct excitation in the dot, plus additional bulk excitons diffusing from the barrier layers into the dot. The thermally driven bulk-exciton diffusion from the barriers causes the temperature enhancement of the exciton emission. Above Tx,max, the intensity decreases due to exciton annihilation processes. In comparison to the exciton, the biexciton intensity shows only very weak enhancement, which is attributed to more efficient annihilation processes. more...

The optical emission of cone-shell quantum structures (CSQS) under vertical electric (F) and magnetic (B) fields is studied by means of simulations. A CSQS has a unique shape, where an electric field induces the transformation of the hole probability density from a disk into a quantum-ring with a tunable radius. The present study addresses the influence of an additional magnetic field. A common description for the influence of a B-field on charge carriers confined in a quantum dot is the Fock-Darwin model, which introduces the angular momentum quantum number l to describe the splitting of the energy levels. For a CSQS with the hole in the quantum ring state, the present simulations demonstrate a B-dependence of the hole energy which substantially deviates from the prediction of the Fock-Darwin model. In particular, the energy of exited states with a hole lh> 0 can become lower than the ground state energy with lh= 0. Because for the lowest-energy state the electron le is always zero, states with lh> 0 are optically dark due to selection rules. This allows switching from a bright state (lh= 0) to a dark state (lh> 0) or vice versa by changing the strength of the F or B field. This effect can be very interesting for trapping photoexcited charge carriers for a desired time. Furthermore, the influence of the CSQS shape on the fields required for the bright to dark state transition is investigated. more...

Strain-free GaAs cone–shell quantum structures (CSQS) with widely tunable wave functions (WF) are fabricated using local droplet etching (LDE) during molecular beam epitaxy (MBE). During MBE, Al droplets are deposited on an AlGaAs surface, which then drill low-density (about 1 × 107 cm−2) nanoholes with adjustable shape and size. Subsequently, the holes are filled with GaAs to form CSQS, where the size can be adjusted by the amount of GaAs deposited for hole filling. An electric field is applied in growth direction to tune the WF in a CSQS. The resulting highly asymmetric exciton Stark shift is measured using micro-photoluminescence. Here, the unique shape of the CSQS allows a large charge–carrier separation and, thus, a strong Stark shift of up to more than 16 meV at a moderate field of 65 kV/cm. This corresponds to a very large polarizability of 8.6 × 10−6 eVkV −2 cm2. In combination with simulations of the exciton energy, the Stark shift data allow the determination of the CSQS size and shape. Simulations of the exciton–recombination lifetime predict an elongation up to factor of 69 for the present CSQSs, tunable by the electric field. In addition, the simulations indicate the field-induced transformation of the hole WF from a disk into a quantum ring with a tunable radius from about 10 nm up to 22.5 nm. more...

Strain-free GaAs quantum dots (QDs) are fabricated by filling droplet-etched nanoholes in AlGaAs. Using a template of nominally identical nanoholes, the QD size is precisely controlled by the thickness of the GaAs filling layer. Atomic force microscopy indicates that the QDs have a cone-shell shape. From single-dot photoluminescence measurements, values of the exciton emission energy (1.58...1.82 eV), the exciton–biexciton splitting (1.8...2.5 meV), the exciton radiative lifetime of bright (0.37...0.58 ns) and dark (3.2...6.7 ns) states, the quantum efficiency (0.89...0.92), and the oscillator strength (11.2...17.1) are determined as a function of the dot size. The experimental data are interpreted by comparison with an atomistic model. more...

In this submission, we discuss the growth of charge-controllable GaAs quantum dots embedded in an n-i-p diode structure, from the perspective of a molecular beam epitaxy grower. The QDs show no blinking and narrow linewidths. We show that the parameters used led to a bimodal growth mode of QDs resulting from low arsenic surface coverage. We identify one of the modes as that showing good properties found in previous work. As the morphology of the fabricated QDs does not hint at outstanding properties, we attribute the good performance of this sample to the low impurity levels in the matrix material and the ability of n- and p-doped contact regions to stabilize the charge state. We present the challenges met in characterizing the sample with ensemble photoluminescence spectroscopy caused by the photonic structure used. We show two straightforward methods to overcome this hurdle and gain insight into QD emission properties. more...

Epitaxially grown quantum dots (QDs) are established as quantum emitters for quantum information technology, but their operation under ambient conditions remains a challenge. Therefore, we study photoluminescence (PL) emission at and close to room temperature from self-assembled strain-free GaAs quantum dots (QDs) in refilled AlGaAs nanoholes on (001)GaAs substrate. Two major obstacles for room temperature operation are observed. The first is a strong radiative background from the GaAs substrate and the second a significant loss of intensity by more than four orders of magnitude between liquid helium and room temperature. We discuss results obtained on three different sample designs and two excitation wavelengths. The PL measurements are performed at room temperature and at T = 200 K, which is obtained using an inexpensive thermoelectric cooler. An optimized sample with an AlGaAs barrier layer thicker than the penetration depth of the exciting green laser light (532 nm) demonstrates clear QD peaks already at room temperature. Samples with thin AlGaAs layers show room temperature emission from the QDs when a blue laser (405 nm) with a reduced optical penetration depth is used for excitation. A model and a fit to the experimental behavior identify dissociation of excitons in the barrier below T = 100 K and thermal escape of excitons from QDs above T = 160 K as the central processes causing PL-intensity loss. more...