A series of fine-grained FeCoNi(CuAl)x (x = 0, 0.4, 0.6, 0.8, 1.0) medium-entropy alloy (MEA) and high-entropy alloys (HEAs) were fabricated by Mechanical Alloying (MA) and Spark Plasma Sintering (SPS). The effect of Al and Cu content (x) on phase composition, microstructure, and mechanical properties of the alloys was investigated. Experimental results show that the crystal structure of FeCoNi(CuAl)x alloy transforms from single (face-centered cubic) FCC phase for x = 0 to FCC + BCC duplex phases for x = 0.4∼1.0, with the fraction of (body-centered cubic) BCC phase gradually increasing with the increase of x. Adding a low content of Al and Cu elements to FeCoNi alloy can significantly hinder the grain growth during sintering process, the average grain size of FCC phase decreases from 0.95 to 0.30 µm at x = 0.4. However, the grain sizes of FCC and BCC phases gradually grow up when x increases from 0.4 to 1.0. The variation in grain size indicates that the atomic diffusion rate of sintered alloy may be influenced by the sluggish diffusion effect in HEA as well as the content of Al and Cu with lower melting points. Mechanical properties of the HEAs are mainly affected by the volume fraction of BCC phase. The compressive yield strength and hardness of HEAs are improved at first and then slightly reduced, while the plasticity drops down continuously with the increase of x. The bulky HEA achieved excellent comprehensive mechanical properties with a compressive yield strength of 1,467.7 MPa and plastic strain to failure of 24.9% at x = 0.6, due to the fine duplex microstructure.

From the very beginning, the research of Material Life Cycle Assessment (MLCA) has been an important part of the ecomaterials research in China, and large numbers of researchers have been focusing their efforts on it. From 1998, and supported by the National High-tech Program-863 Projects, the study of some typical materials has been put into practice. Thus far, the first phase of the project has been finished smoothly. The practical MLCA methods have been developed, and the manufacturing technologies and processes of the steel and iron, aluminum, cement, ceramic, polymer and construction coatings have been assessed. The relevant assessment software has been developed. Reference systems are being set up for evaluation by studying typical materials. In this paper, the main achievements are reviewed. Some other developments of MLCA in China are also introduced.