Search

Thermoplastic polyimide (PI) matrixes, including PI-a (cc-34ODA) and PI-b (ct-34ODA) were prepared via the hot-pressing procedures of the resins derived from the 3,4′-oxydianiline (34ODA) and two alicyclic dianhydrides of 1S,2R,4S,5R-hydrogenated pyromellitic dianhydride (ccHPMDA) and 1R,2S,4S,5R-hydrogenated pyromellitic dianhydride (ctHPMDA), respectively. The resins exhibited thermoplastic features with good formability at higher temperatures. The afforded semi-alicyclic PI sheets exhibited enhanced properties in comparison to commercially available, wholly aromatic thermoplastic PIs, such as PI-ref1, which are derived from 3,3′,4,4′-oxydiphthalic anhydride (ODPA) and 4,4′-oxydianiline (44ODA), as well as PI-ref2, which is based on pyromellitic dianhydride (PMDA) and 4,4′-bis(3-aminophenoxy)biphenyl (mBAPB). In addition, the developed PI sheets exhibited high heat deflection temperatures (HDT) of 267.4 °C for PI-a and 268.6 °C for PI-b. There values were significantly higher when compared with those of PI-ref1 (Ratem® YS20, HDT: 239.0 °C), PI-ref2 (Aurum® PL450C, HDT: 238.0 °C), PI-ref3 (Ultem® 1000, HDT: 206.0 °C), PI-ref4 (Therplim® TO65, HDT: 180.0 °C), and PI-ref5 based on phthalic anhydride-terminated fluorinated PIs (HDT: 215.0 °C). In terms of mechanical properties, the current PI sheets showed superior flexural properties among the polymers with the flexural strength of 189.0 ± 11.7 MPa (PI-a) and 200.5 ± 4.2 MPa (PI-b), respectively. In addition, the PI sheets exhibited comparable compression properties, inferior impact strength, and tensile properties compared with the referenced PI counterparts. Basically, the PI-b sheet showed better comprehensive properties than those of the stereoisomeric PI-a analog. [ABSTRACT FROM AUTHOR]

Optically transparent polyimide (PI) films with good atomic oxygen (AO) resistance have been paid extensive attention as thermal controls, optical substrates for solar cells or other components for low Earth orbit (LEO) space applications. However, for common PI films, it is usually quite difficult to achieve both high optical transparency and AO resistance and maintain the intrinsic thermal stability of the PI films at the same time. In the current work, we aimed to achieve the target by using the copolymerization methodology using the fluorinated dianhydride 9,9-bis(trifluoromethyl)xanthene-2,3,6,7-tetracarboxylic dianhydride (6FCDA), the fluorinated diamine 2,2-bis [4-(4-aminophenoxy)phenyl]hexafluoropropane (BDAF) and the polyhedral oligomeric silsesquioxane (POSS)-containing diamine N-[(heptaisobutyl-POSS)propyl]-3,5-diaminobenzamide (DABA-POSS) as the starting materials. The fluoro-containing monomers were used to endow the PI films with good optical and thermal properties, while the silicon-containing monomer was used to improve the AO resistance of the afforded PI films. Thus, the 6FCDA-based PI copolymers, including 6FCPI-1, 6FCPI-2 and 6FCPI-3, were prepared using a two-step chemical imidization procedure, respectively. For comparison, the analogous PIs, including 6FPI-1, 6FPI-2 and 6FPI-3, were correspondingly developed according to the same procedure except that 6FCDA was replaced by 4,4′-(hexafluoroisopropylidene)diphthalic anhydride (6FDA). Two referenced PI homopolymers were prepared from BDAF and 6FDA (PI-ref1) and 6FCDA (PI-ref2), respectively. The experimental results indicated that a good balance among thermal stability, optical transparency, and AO resistance was achieved by the 6FCDA-PI films. For example, the 6FCDA-PI films exhibited good thermal stability with glass transition temperatures (Tg) up to 297.3 °C, good optical transparency with an optical transmittance at a wavelength of 450 nm (T450) higher than 62% and good AO resistance with the erosion yield (Ey) as low as 1.7 × 10−25 cm3/atom at an AO irradiation fluence of 5.0 × 1020 atoms/cm2. The developed 6FCDA-PI films might find various applications in aerospace as solar sails, thermal control blankets, optical components and other functional materials. [ABSTRACT FROM AUTHOR]

As triboelectric nanogenerator (TENG) technology continue to evolve, its application in harsh environments has increasingly captivated the interest of researchers. However, the current research on heat-resistant triboelectric materials remains predominantly focused on the development of tribo-negative materials, with scant attention given to their equally crucial tribo-positive counterparts. In this study, the tribo-positive polyimide (PI) material with enhanced tribo-positivity is developed by integrating amide groups with electron-donating effects into the molecular chain. Furthermore, the TENG devices based on this series of tribo-positive PI materials have demonstrated an open-circuit voltage (VOC) of 242 V, a short-circuit current (ISC) of 8.13 μA, and a transferred charge (QSC) of 117 nC. Notably, these devices also demonstrate the capability to efficiently generate electricity even under elevated temperature conditions. This work not only proposes a potential molecular design strategy for developing high-performance tribo-positive PI materials applicable in TENGs, but also markedly propels the advancement of robust energy-harvesting devices engineered for operation at elevated temperatures. [ABSTRACT FROM AUTHOR]

Calcium hydroxide was used as a swelling agent and grinding aid to grind together with cellulose raw materials to prepare microfibrillated cellulose (MFC). Carbon dioxide was introduced to obtain MFC coated with calcium carbonate (CMFC). The effect of calcium hydroxide dosage on the fibrillation process of cellulose materials and the characteristics of MFCs and CMFCs were studied. Results show that when the dosage of calcium hydroxide was 5 % (based on cellulose materials), calcium hydroxide could be completely dissolved in water and had a swelling effect on cellulose materials. When the dosage reached 10 %, undissolved calcium hydroxide particles could serve as grinding media to assist in the fibrillation of cellulose materials. When the dosage exceeded 50 %, the auxiliary grinding effect of calcium hydroxide was more obvious. After accelerated carbonation, the generated calcium carbonate nanoparticles were coated on the surface of MFC, which increased its viscosity and decreased water retention value. The presence of calcium carbonate also facilitated the concentration, redispersion, and drying of MFC. The pretreatment, mechanical fibrillation, and accelerated carbonation were carried out in the same equipment without the need for heating or washing. Therefore, this study provides a in situ and one step method for the preparation of MFC. [ABSTRACT FROM AUTHOR]