We investigate the short and long term wettability of laser textured stainless steel samples in order to better understand the interplay between surface topography and chemistry. Very different 1D and 2D periodic as well as non-periodic surface patterns were produced by exploiting the extreme flexibility of a setup consisting of five rotating birefringent crystals, which allows generating bursts of up to 32 femtosecond laser pulses with fixed intra-burst delay of 1.5 ps. The change of the surface morphology as a function of the pulse splitting, the burst polarization state and the fluence was systematically studied. The surface topography was characterized by SEM and AFM microscopy. The laser textured samples exhibited, initially, superhydrophilic behaviour which, during exposure to ambient air, turned into superhydrophobic with an exponential growth of the static contact angle. The dynamic contact angle measurements revealed a water adhesive character which was explained by XPS analyses of the surfaces that showed an increase of hydrocarbons and more oxidized metal species with the aging. The characteristic water adhesiveness and superhydrophobicity of laser textured surfaces can be exploited for no loss droplet reversible transportation or harvesting.

In this work, we report on the fabrication of laser induced periodic surface structures (LIPSS) on stainless steel, using bursts of 200 fs sub-pulses at a wavelength of 1030 nm. A cascade of birefringent crystals was used to generate the bursts with tunable number of sub-pulses and intra-burst delays varying between 1.5 ps and 24 ps. Being such a delay shorter than the typical electron-lattice relaxation time in metals, the sub-pulses impinge on the sample surface when the material is still in a transient state after excitation from the first sub-pulse, thus allowing peculiar structures to be generated depending on the burst features. We obtained 1-D and 2-D periodic surface structures and investigated the influence of number of sub-pulses and polarization on their morphology. In particular, when bursts composed by all-aligned linearly polarized sub-pulses were used, 1-D LIPSS were obtained with different periodicity and depths depending on the number of sub-pulses. Bursts with crossed linear polarization or circular polarization sub-pulses produced 2-D LIPSS with morphology varying from triangular structures arranged in hexagonal lattice to pillar-like ordered or disordered structures depending on the bursts features. In most cases these structures exhibit a superhydrophobic behavior, as assessed by static contact angle measurements, which is achieved after a time of exposition to laboratory air. By XPS analysis we investigated the chemical variations occurring on the surfaces over this time.