Sb- and Se-substituted CeOBiS2 single crystals have been successfully grown using CsCl/KCl flux. Sb and Se substitution dependence of the superconductivity on CeOBiS2 was investigated and the superconducting phase diagram at above 0.3 K was described. The non-linear boundary between superconductivity and non-superconductivity was revealed., Comment: 16 pages, 2 figures

Sb-substituted CeOBiS2 single crystals with 0.2-1.0 mm size have been successfully grown using CsCl/KCl flux. Sb substitution strongly suppressed the superconductivity in CeOBiS2, and the substitution of more than approximately 4 atomic percent in Bi-site disappeared the superconductivity at a measurement range of above 0.36 K. Furthermore, the drastic change of c-axis lattice parameter was observed in a neighborhood to Sb substitution amount, which maybe suggests the structural transition in CeOBiS2. The Ce valence state of the obtained single crystals was evaluated. However, the established correlations between Ce valence state and superconductivity could not be revealed.

Superconductors are influenced by high-entropy alloys (HEAs); these have been investigated in various functional materials. REOBiS$_2$ (RE = La, Ce, Pr, Nd, Sm, and Gd in different combinations) single crystals with HEAs at the RE-site were successfully grown using the flux method. The obtained crystals were plate-shaped (1 mm$^2$) with a well-developed c-plane. Ce was present in both trivalent (Ce$^{3+}$) and tetravalent (Ce$^{4+}$) electronic configurations; the concentration of Ce$^{4+}$ at the RE-site was approximately 10 at% in all single crystals. The single crystals showed superconducting transition temperature with zero resistivity within 1.2-4.2 K. The superconducting transition temperature, superconducting anisotropy, electronic specific heat coefficient, and Debye temperature of the crystals were not correlated with the mixed entropy at the RE-site. Except for the electronic specific heat coefficient, the variation of these parameters as a function of mixed entropy showed different trends for equivalent and non-equivalent RE element compositions. Thus, the configuration of RE elements influences the superconducting properties of REOBiS$_2$ single crystals, alluding to a method of modulating transition temperatures.

Single-crystal whiskers of REBa2Cu3Ox (RE-123, RE: rare earth element) cuprate superconductors were successfully grown using Te-doped precursors utilizing the concept of high-entropy-alloys (HEAs) at the RE site. The obtained whiskers were 0.5-1.0 mm length with approximately 10 um thickness. The width of the flat surface, which corresponds to the ab-plane, was 10-50 um. The RE site of the grown whiskers could be easily substituted by large ionic radius RE elements (Gd, Dy, and Ho). Substitution with small ionic radius RE elements (Tm, Yb, and Lu) resulted in the opposite trend. The superconducting transition temperature and superconducting anisotropy of the grown RE-123 whiskers were 89-93 K and 6-10, respectively. The mixed entropy at the RE site in the RE-123 whiskers did not affect the superconducting transition temperature and superconducting anisotropy., Comment: 27 pages, 8 figures, 2 tables

In object detection, data amount and cost are a trade-off, and collecting a large amount of data in a specific domain is labor intensive. Therefore, existing large-scale datasets are used for pre-training. However, conventional transfer learning and domain adaptation cannot bridge the domain gap when the target domain differs significantly from the source domain. We propose a data synthesis method that can solve the large domain gap problem. In this method, a part of the target image is pasted onto the source image, and the position of the pasted region is aligned by utilizing the information of the object bounding box. In addition, we introduce adversarial learning to discriminate whether the original or the pasted regions. The proposed method trains on a large number of source images and a few target domain images. The proposed method achieves higher accuracy than conventional methods in a very different domain problem setting, where RGB images are the source domain, and thermal infrared images are the target domain. Similarly, the proposed method achieves higher accuracy in the cases of simulation images to real images., Comment: Yuzuru Nakamura and Yasunori Ishii are equal contribution

Single crystals of Ce-doped (La,Pr)OBiS2 superconductors, multinary rare-earth elements substituted ROBiS2, were successfully grown. The grown crystals typically had a size of 1-2 mm and a plate-like shape with a well-developed c-plane. The c-axis lattice constants of the obtained (La,Ce,Pr)OBiS2 single crystals were approximately 13.6-13.7 A, and the superconducting transition temperature was 1.23-2.18 K. Valence fluctuations of Ce and Pr were detected through X-ray absorption spectroscopy analysis. In contrast to (Ce,Pr)OBiS2 and (La,Ce)OBiS2, the superconducting transition temperature of (La,Ce,Pr)OBiS2 increased with increasing concentrations of the tetravalent state at the R-site.

Sm(O,F)BiS2 superconducting single crystals with various nominal F contents have been grown using KI-KCl flux. The solid solution limit of F at the O-site in Sm(O,F)BiS2 single crystals was approximately less than 20 at%. F concentrations of Sm(O,F)BiS2 single crystals were hardly controlled by nominal F contents. It suggests the existence of intrinsic stable phase. Superconductivity was shown at around 5 K. Superconducting transition temperature with zero resistivity were increased with increasing nominal F contents within less than 70 at% in O-site, despite similar F concentration and c-axis lattice constants.

NbBiCh$_3$ (Ch = S, Se) misfit-layered superconducting single crystals were successfully grown using a CsCl/KCl flux for the first time. The obtained crystals had a well-developed habit parallel to the c-plane with a typical width of 1-2 mm and thickness of 10-40 um. The superconducting transition temperatures with zero resistivity of NbBiS$_3$ single crystals obtained from the nominal composition of Nb0.9Bi1.2S3 was 0.31 K, and that value of the NbBiSe$_3$ single crystals grown from the stoichiometry composition (NbBiSe$_3$) was 2.3 K. Sharp decreases in electric resistivity and magnetic susceptibility at approximately 3 K suggested a possible superconducting transition temperature of NbBiSe$_3$. The normal-state anisotropy values of grown NbBiS$_3$ and NbBiSe$_3$ single crystals were 2.2-2.4 and 1.5-1.6, respectively., Comment: 4 figures + 3 figures (Supplementary Materials)

Superconducting Sm(O,F)BiS2 single crystals were successfully grown using KI-KCl flux. The obtained single crystals were flat-shaped and their size was 500um. The structure and composition of the obtained single crystals were obtained using X-ray diffraction and X-ray spectroscopy. The lattice constants of the obtained Sm(O,F)BiS2 single crystals were evaluated to be a = 3.9672(4) A and c = 13.417(6) A, while their F/(O + F) molar ratio was approximately 0.17. The superconducting transition temperature of the obtained Sm(O,F)BiS2 single crystals was 4.8 K. This was different from the reported Sm(O,F)BiS2 with no superconducting transition above 2 K. The superconducting anisotropies of the upper critical field and effective mass model of the obtained Sm(O,F)BiS2 single crystals were estimated to be approximately 26 and 10, respectively., Comment: 22 pages, 7 figures

(La,Ce)OBiS2 single crystals are successfully grown using CsCl flux. The obtained single crystals have a plate-like shape with a size of 0.5-2.0 mm and a well-developed ab-plane. The thickness of the crystals increases with a decrease in the Ce content. The (La,Ce)OBiS2 single crystals exhibit superconducting properties. Moreover, the superconducting transition temperature increases with an increase in the Ce content. The obtained (La,Ce)OBiS2 single crystals exhibit a tetragonal structure and the valence state of Ce in the crystals is determined to be mixed with Ce3+ and Ce4+ based on X-ray absorption fine structure spectroscopy., Comment: 12 pages, 6 figures

PrOBiS2 single crystals were successfully grown using a KCl flux. The obtained crystals had a plate-like shape with a typical size of 0.5-1.0 mm and well-developed ab-plane. The Pr valence of the grown crystals, as determined by an X-ray absorption fine structure spectroscopy analysis, was almost trivalent. The PrOBiS2 single crystals did not exhibit superconductivity down to 0.25 K. The transport properties under high pressures up to 50 GPa ensured semiconducting behavior for 2-300 K using a diamond anvil cell., Comment: 19 pages, 5 figures