Search

MoS2 is an additive used to improve the tribological properties of plastics. In this work, it was decided to verify the use of MoS2 as a modifier of the properties of PLA filaments used in the additive FDM/FFF technique. For this purpose, MoS2 was introduced into the PLA matrix at concentrations of 0.025–1.0% by weight. Through extrusion, a fibre with a diameter of 1.75 mm was obtained. 3D printed samples with three different filling patterns were subjected to comprehensive thermal (TG, DSC and HDT), mechanical (impact, bending and strength tests), tribological and physicochemical characteristics. The mechanical properties were determined for two different types of fillings, and samples with the third type of filling were used for tribological tests. Tensile strength has been significantly increased for all samples with longitudinal filling with improvement up to 49%. In terms of tribological properties, higher values of the addition (0.5%) caused a significant increase of up to 457% of the wear indicator. A significant improvement in processing properties in terms of rheology was obtained (416% compared to pure PLA with the addition of 1.0%), which translated into more efficient processing, increased interlayer adhesion and mechanical strength. As a result, the quality of printed objects has been improved. Microscopic analysis was also carried out, which confirmed the good dispersion of the modifier in the polymer matrix (SEM-EDS). Microscopic techniques (MO, SEM) allowed for the characterization of the effect of the additive on changes in the printing process (improvement of interlayer remelting) and to assess impact fractures. In the tribological area, the introduced modification did not bring spectacular effects.

Titanium dioxide is a commonly used ingredient in cosmetics acting as a thickening agent and inorganic UV filter. However, TiO2 is difficult to disperse, which causes problems in spreading the formulations. The solution to this problem is to modify the titanium dioxide surface to change its properties by creation of the new type of hybrid inorganic–organic UV filter. Therefore, this study aimed to functionalize titanium dioxide with organosilicon compounds and determine how this modification will affect the dispersibility of TiO2 in the colloidal system and the stability of emulsions. First, the functionalized octaspherosilicates were obtained and characterized. Next, the synthesized compounds were applied as modifiers for titanium dioxide and were analyzed by FT-IR, UV-Vis, and laser diffraction. Furthermore, the hydrophilic–hydrophobic character was assessed by measuring the contact angle. The new materials were introduced into emulsions and the formulations were analyzed in terms of particle size distribution and stability by multiple light scattering. It was found that the modification of titanium dioxide with spherosilicates significantly improved both the stability of emulsion and the dispersibility of novel materials in the colloidal system compared to nonmodified TiO2. The covalent binding of the modifier with the titanium dioxide had an impact on the stability of the emulsion.

The presented work is a continuation of research on the reactivity of unsaturated borasilsesquioxanes under the conditions of common organometallic transformations. The catalytic hydrosilylation reaction with silanes, siloxanes and silsesquioxanes in presence of platinum catalyst was explored. The majority of the products were obtained in high yields (90 %) and their structures were confirmed and characterized by spectroscopy and spectrometry, i. e. NMR and MALDI-TOF-MS. The most significant segment of the work is research on the spontaneous redistribution reaction of the alkoxy group from silane to borane moiety occurring in the obtained products, not being limited to the heterosilsesquioxane chemistry, however. The products were confirmed using GC-MS, ESI-MS methods and B3LYP exchange-correlation, in order to ascertain formation of the silicon-boron hybrid molecule.

In this study, a series of cage siloxanes (CS), e.g., three polyhedral oligomeric silsesquioxanes (SSQs) and one spherosilicate (SS) derivative, were applied as functional additives for the preparation of poly(lactic acid)-based (PLA) nanofibrillar membranes with an electrospinning technique utilizing an efficient spinning wire electrode setup. The impact of the additives’ structure, chemistry, and electrospinning parameters on the obtained materials’ morphology (scanning electron microscopy) and physicochemical (thermogravimetry, differential scanning calorimetry, contact angle analysis, air flow analysis) properties is discussed. It is presented that applying organosilicon additives may extend the already tuneable properties of the membranes produced by electrospinning performed under different conditions and that they enable to obtain nanofibres of smaller diameter, which in turn increases the membrane porosity. Furthermore, the solvent-assisted electrospinning method allowed for unparalleled mixing of the PLA matrix with the CS additives, as no traces of free additives were visible on the membranes by scanning electron microscopy (SEM) imaging. The resulting membranes can be utilized as filter materials.

In this work, silsesquioxane and spherosilicate compounds were assessed as novel organosilicon coupling agents for surface modification of TiO2 in a green process, and compared with their conventional silane counterparts. The surface-treated TiO2 particles were then applied in preparation of epoxy (EP) composites and the aspects of pigment dispersion, suspension stability, hiding power, as well as the composite mechanical and thermal properties were discussed. The studied compounds loading was between 0.005–0.015% (50–150 ppm) in respect to the bulk composite mass and resulted in increase of suspension stability and hiding power by over an order of magnitude. It was found that these compounds may be an effective alternative for silane coupling agents, yet due to their low cost and simplicity of production and manipulation, silanes and siloxanes are still the most straight-forward options available. Nonetheless, the obtained findings might encourage tuning of silsesquioxane compounds structure and probably process itself if implementation of these novel organosilicon compounds as surface treatment agents is sought for special applications, e.g., high performance coating systems.

The first report of using limonene derivative of a spherosilicate as a modifier of polylactide used for 3D printing and injection moulding is presented. The paper presents the use of limonene-functionalized spherosilicate derivative as a functional additive. The study compared the material characteristics of polylactide modified with SS-Limonene (0.25&ndash, 5.0% w/w) processed with traditional injection moulding and 3D printing (FFF, FDM). A significant improvement in the processing properties concerning rheology, inter-layer adhesion, and mechanical properties was achieved, which translated into the quality of the print and reduction of waste production. Moreover, the paper describes the elementary stages of thermal transformations of the obtained hybrid systems.

The fractionation of diatomaceous earth (DE) using sedimentation made it possible to obtain separate unbroken diatom fractions from broken or agglomerated bodies with a range of particle sizes. The produced filler was used to prepare polylactide (PLA)/diatomaceous earth biocomposite samples containing different particle sizes, which were subjected to mechanical testing (tensile strength, flexural strength, impact strength), colloidal testing (contact angle, color change test, SEM/EDS), and thermal testing (TGA, DSC, DMA). Modification of the PLA containing the smallest particle size with diatomaceous earth (Fraction 5) resulted in a higher impact strength compared to both the pure PLA and the PLA/DE composite that contained base diatomaceous earth. Furthermore, the melt flow rate was improved by more than 80 and 60% for the composite modified with fractionated diatomaceous earth (Fraction 4) compared to pure PLA and base diatomaceous earth, respectively. The elasticity of the composite was also improved from 3.3 GPa for pure polylactide to 4.4 GPa for the system containing the smallest diatomaceous earth particles (Fraction 5).

The aim of this study was to investigate the restorative connections of composite materials after fracture, under controlled conditions of treating the materials with novel, spherosilicate-based (SS) primers bearing both methacryl (MA) and trimethoxysilyl (TMOS) groups. The chemistry of methacrylate group insertion and reactive groups hydrolysis has been studied with the aid of 1H NMR (Nuclear Magnetic Resonance) spectroscopy. The light-cured resin composites were repaired by activating the connection site with the obtained primers and, for comparison, a silane (methacryloxypropyltrimethoxysilane, MATMOS) as a conventional coupling agent bearing the same reactive groups. The resistance of such a joint was tested in a three-point bending test after 24 h and 28 days period of sample conditioning. The effect of bond application was also studied, showing that spherosilicate-based primers may be used more effectively than MATMOS for two-step (primer-composite) restorative process, while for silane, the three-step process with bond application is crucial for satisfactory joint quality. The joint failure mode was determined by microscopic analysis and it was found that SS-4MA-4TMOS and SS-2MA-6TMOS application resulted in mostly composite, and not joint, failure. After 28 days of conditioning, the flexural strength of the joint repaired with SS-4MA-4TMOS was at 94% of the neat, solid material under the same procedure. However, the strength of the neat composite was observed to decline during the conditioning process by ~30%. The joint behavior was explained on the basis of the gradual hydrolysis effect (the greatest decrease being observed for silane).