Abstract Combining thin film deposition with in situ heating electron microscopy allows to understand the thermal stability of complex solid solution nanomaterials. From a CrMnFeCoNi alloy target a thin film with an average thickness of ~10 nm was directly sputtered onto a heating chip for in situ transmission electron microscopy. We investigate the growth process and the thermal stability of the alloy and compare our results with other investigations on bulk alloys or bulk-like films thicker than 100 nm. For the chosen sputtering condition and SiNx substrate, the sputter process leads to the Stranski–Krastanov growth type (i.e., islands forming on the top of a continuous layer). Directly after sputtering, we detect two different phases, namely CoNi-rich nanoscale islands and a continuous CrMnFe-rich layer. In situ annealing of the thin film up to 700°C leads to Ostwald ripening of the islands, which is enhanced in the areas irradiated by the electron beam during heating. Besides Ostwald ripening, the chemical composition of the continuous layer and the islands changed during the heating process. After annealing, the islands are still CoNi-rich, but lower amounts of Fe and Cr are observed and Mn was completely absent. The continuous layer also changed its composition. Co and Ni were removed, and the amount of Cr lowered. These results confirm that the synthesis of a CrMnFeCoNi thin film with an average thickness of ~10 nm can lead to a different morphology, chemical composition, and stability compared to thicker films (>100 nm). Impact statement Exploring stability of a complex solid solution thin film by in situ heating transmission electron microscopy is a study of the thermal stability of sputtered complex solid solution thin films with thicknesses of ~10 nm. Complex solid solution materials have a promising electrocatalytic behavior due to the interplay of multi-element active sites. In order to understand their catalytic properties, it is important to identify the different structure-composition-activity correlations. Thus, our investigation helps to clarify and to understand the stability of nanoscale complex solid solution with an average film thickness of ~10 nm. Graphic abstract Combining sputter deposition with in situ heating transmission electron microscopy allows to understand the thermal stability of nanoscale complex solid solution thin films.

The formation of nanoparticles by sputtering on ionic liquids could occur at the surface or in the volume of the liquid. To clarify which process occurs, Cu was sputtered in inert and oxidative pla...

Complex solid‐solution electrocatalysts (also referred to as high‐entropy alloy) are gaining increasing interest owing to their promising properties which were only recently discovered. With the capability of forming complex single‐phase solid solutions from five or more constituents, they offer unique capabilities of fine‐tuning adsorption energies. However, the elemental complexity within the crystal structure and its effect on electrocatalytic properties is poorly understood. We discuss how addition or replacement of elements affect the adsorption energy distribution pattern and how this impacts the shape and activity of catalytic response curves. We highlight the implications of these conceptual findings on improved screening of new catalyst configurations and illustrate this strategy based on the discovery and experimental evaluation of several highly active complex solid solution nanoparticle catalysts for the oxygen reduction reaction in alkaline media., Elementary: The effect of changing elements within high‐entropy electrocatalysts with respect to changes in adsorption energies and the correlated characteristic activity curves is analyzed. This concept is verified for the oxygen reduction reaction (ORR) in alkaline media. A targeted design of complex solid‐solution electrocatalysts is significantly enhanced by only screening equiatomic alloys without the need to scan the whole composition range.

Non-equilibrium synthesis methods allow to alloy bulk-immiscible elements into multinary nanoparticles, which broadens the design space for new materials.Whereas sputtering onto solid substrates can combine immiscible elements into thin film solid solutions, this is not clear for sputtering of nanoparticles in ionicliquids. Thus, the suitability of sputtering in ionic liquids for producing nanoparticles of immiscible elements is investigated by co-sputtering the systems Au-Cu (miscible), Au-Ru and Cu-Ru (both immiscible), and Au-Cu-Ru on the surface of the ionic liquid 1-butyl-3-methylimidazolium bis-trifluoromethylsulfonyl)imide [Bmim][(Tf)2N]. The sputtered nanoparticles were analyzed to obtain (i) knowledge concerning the general formation process ofnanoparticles when sputtering onto ionic liquid surfaces and (ii) information, if alloy nanoparticles of immiscible elements can be synthesized as well as (iii)evidence if the Hume-Rothery rules for solid solubility are valid for sputtered nanoparticles. Accompanying atomistic simulations using density-functional theoryfor clusters of different size and ordering confirm that the miscibility of Au-Cu and the immiscibility of Au-Ru and Cu-Ru govern the thermodynamic stabilityof the nanoparticles. Based on the matching experimental and theoretical results for the NP/IL-systems concerning NP stability, a formation model of multinaryNPs in ILs was developed.

Transition metal ferrites, such as CoFe2O4 (CFO) and NiFe2O4 (NFO), have gained increasing attention as potential materials for supercapacitors. Since chemical vapor deposition (CVD) offers advantages like interface quality to the underlying substrates and the possibility for coverage of 3D substrates, two CVD processes are reported for CFO and NFO. Growth rates amount to 150 to 200 nm h−1 and yield uniform, dense, and phase pure spinel ferrite films according to X-ray diffraction (XRD), Raman spectroscopy, Rutherford backscattering spectrometry and nuclear reaction analysis (RBS/NRA) and scanning electron microscopy (SEM). Atom probe tomography (APT) and synchrotron X-ray photoelectron spectroscopy (XPS) give insights into the vertical homogeneity and oxidation states in the CFO films. Cation disorder of CFO is analyzed for the first time from synchrotron-based XPS. NFO is analyzed via lab-based XPS. Depositions on conducting Ni and Ti substrates result in electrodes with pseudocapacitive behavior, as evidenced by cyclovoltammetry (CV) experiments. The interfacial capacitances of the electrodes are up to 185 µF cm−2.

Complex solid solution (CSS) nanoparticles were recently discovered as efficient electrocatalysts for a variety of reactions. As one of many advantages, they exhibit the potential to replace noble-metal catalysts with multinary combinations of transition metals because they offer formation of new unique and tailorable active sites of multiple elements located next to each other. This Perspective reports on the current state and on challenges of the (combinatorial) synthesis of multinary nanoparticles and advanced electron microscopy characterization techniques for revealing structure–activity correlations on an atomic scale. We discuss what distinguishes this material class from common catalysts to highlight their potential to act as electrocatalysts and rationalize their nontypical electrochemical behavior. We provide an overview about challenges in synthesis, characterization, and electrochemical evaluation and propose guidelines for future design of CSS catalysts to achieve further progress in this res...

Upscaling of nanoparticle fabrication by sputtering into an ionic liquid is shown for the example of Cu. Long-time sputtering (24 h) into a large amount (50 mL) of the ionic liquid 1-butyl-3-methylimidazolium bis-(trifluoromethylsulfonyl)imide [Bmim][(Tf)2 N] yields an amount of approximately 1 g Cu nanoparticles (mean spherical diameter (2.6 ± 1.1) nm), stabilized in ionic liquid without agglomerations. Extraction of Cu nanoparticles from the stabilizing ionic liquid was performed with the capping agent hexadecylamine. Extracted particles could be redispersed in other solvents, thus enabling applications of sputtered nanoparticles beyond ionic liquids.

Up-scaling of nanoparticle fabrication by sputtering into an ionic liquid is shown for the example of Cu. Long-time sputtering (24 h) into a large amount (50 mL) of the ionic liquid 1-butyl-3-methylimidazolium bis-(trifluoromethylsulfonyl)imide [Bmim][(Tf)2N] yields an amount of approximately 1 g Cu nanoparticles (mean spherical diameter (2.6 ± 1.1) nm), stabilized in ionic liquid without agglomerations. Extraction of Cu nanoparticles from the stabilizing ionic liquid was performed with the capping agent hexadecylamine. Extracted particles could be redispersed in other solvents, thus enabling applications of sputtered nanoparticles beyond ionic liquids.

Bottom-up and top-down approaches are described for the challenging synthesis of Fe/Al nanoparticles (NPs) in ionic liquids (ILs) under mild conditions. The crystalline phase and morphology of the metal nanoparticles synthesized in three different ionic liquids were identified by powder X-ray diffractometry (PXRD), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), selected-area electron diffraction (SAED) and fast Fourier transform (FFT) of high-resolution TEM images. Characterization was completed by scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDX) for the analysis of the element composition of the whole sample consisting of the NPs and the amorphous background. The bottom-up approaches resulted in crystalline FeAl NPs on an amorphous background. The top-down approach revealed small NPs and could be identified as Fe

Complex solid solution electrocatalysts (often called high-entropy alloys) present a new catalyst class with highly promising features due to the interplay of multi-element active sites. One hurdle is the limited knowledge about structure-activity correlations needed for targeted catalyst design. We prepared Cr-Mn-Fe-Co-Ni nanoparticles by magnetron sputtering a high entropy Cantor alloy target simultaneously into an ionic liquid library. The synthesized nanoparticles have a narrow size distribution but different sizes (from 1.3 ± 0.1 nm up to 2.6 ± 0.3 nm), different crystallinity (amorphous, face-centered cubic or body-centered cubic) and composition (i.e. high Mn versus low Mn content). The Cr-Mn-Fe-Co-Ni complex solid solution nanoparticles possess an unprecedented intrinsic electrocatalytic activity for the oxygen reduction reaction in alkaline media, some of them even surpassing that of Pt. The highest intrinsic activity was obtained for body-centered cubic nanoparticles with a low Mn and Fe content which were synthesized using the ionic liquid 1-etyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide [Emimi][(Tf)2N].

Binary alloy nanoparticles were fabricated by two combinatorial methods: (I) cosputtering from elemental targets into the ionic liquid 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide ...

The synthesis of nanoparticles by combinatorial sputtering in ionic liquids is a versatile approach for discovering new materials. Whereas the influence on nanoparticle formation of different pure ionic liquids has been addressed, the influence of (I) dilution of ionic liquid with solvents and (II) different mixtures of ionic liquids is less known. Therefore, mixtures of the ionic liquid [Bmim][(Tf)2N] with the organic solvent anisole and other ionic liquids ([Bmim][(Pf)2N], [BmPyr][(Tf)2N]) were used as liquid substrates for the sputter synthesis of nanoparticles, in order to investigate the influence of these mixtures on the size of the nanoparticles. First, mixtures of anisole with a suspension of sputtered Ag nanoparticles in [Bmim][(Tf)2N] were prepared in different volumetric steps to investigate if the stabilization of the NPs by the ionic liquid could be reduced by the solvent. However, a continuous reduction in nanoparticle size and amount with increasing anisole volume was observed. Second, Ag, Au and Cu were sputtered on ionic liquid mixtures. Ag nanoparticles in [Bmim][(Tf)2N]/[Bmim][(Pf)2N] mixtures showed a decrease in size with the increasing volumetric fraction of [Bmim][(Tf)2N], whereas all nanoparticles obtained from [Bmim][(Tf)2N]/[BmPyr][(Tf)2N] mixtures showed increasing size and broadening of the size distribution. Maximum sizes of sputtered Ag and Au NPs were reached in mixtures of [Bmim][(Tf)2N] with 20 vol.% and 40 vol.% [BmPyr][(Tf)2N]. The results indicate that ionic liquid mixtures with different portions of cations and anions have the capability of influencing the ionic liquid stabilization characteristics with respect to, e.g., nanoparticle size and size distribution.

The development of antibacterial implant surfaces is a challenging task in biomaterial research. We fabricated a highly antibacterial bimetallic platinum (Pt)/silver(Ag) nanopatch surface by short time sputtering of Pt and Ag on titanium. The sputter process led to a patch-like distribution with crystalline areas in the nanometer-size range (1.3–3.9 nm thickness, 3–60 nm extension). Structural analyses of Pt/Ag samples showed Ag- and Pt-rich areas containing nanoparticle-like Pt deposits of 1–2 nm. The adhesion and proliferation properties of S. aureus on the nanopatch samples were analyzed. Consecutively sputtered Ag/Pt nanopatches (Pt followed by Ag) induced enhanced antimicrobial activity compared to co-sputtered Pt/Ag samples or pure Ag patches of similar Ag amounts. The underlying sacrificial anode mechanism was proved by linear sweep voltammetry. The advantages of this nanopatch coating are the enhanced antimicrobial activity despite a reduced total amount of Ag/Pt and a self-limited effect due the rapid Ag dissolution.

A high-throughput method is presented for the efficient assessment of the formation and stability of nanoparticle suspensions in ionic liquids which differ in their cations and anions. As a proof of principle, Ag was sputtered on a cavity array filled with 9 different ionic liquids. Not all nanoparticle ionic liquid combinations form a stable suspension with separated nanoparticles. Directly after synthesis, the formation of nonagglomerated nanoparticle suspensions with sizes from 4 to 9 nm is observed by transmission electron microscopy as well as different time dependencies of the suspension stabilities. Only 3 out of the tested 9 nanoparticle ionic liquid suspensions show long-term stability: Stable suspension of spherical nanoparticles are formed in the ionic liquids 1-butyl-3-methylimidazolium bis(perfluoroethylsulfonyl)imide [Bmim][(Pf)2N], 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide [Bmim][(Tf)2N], and 1-butyl-1-methylpyrrolidinum bis(trifluoromethylsulfonyl)imide [BmPyr][(Tf)2N].