Search

The catalytic and electrochemical properties of carbon-supported Pd catalysts (Pd-C, Pd-CNT), prepared by the technique of deposition reduction, are presented in this paper. Single-walled and multiwalled (nitrogen doped, carboxylated, noncarboxylated) carbon nanotubes with different specific surface areas as well as activated carbon (NORIT®) were used. Prepared catalysts were evaluated using cyclic voltammetry. Voltammetric characterization of the catalysts evaluated on the basis of nitrobenzene reduction reaction reveals increasing reactivity of catalysts with increasing Pd concentration from 1 up to 5% Pd and decreasing reactivity from 5 to 10% Pd. Influence of support properties on the reactivity of catalyst was also observed. Prepared catalysts were compared with four commercially produced catalysts. [ABSTRACT FROM AUTHOR]

Copyright of Archives of Metallurgy & Materials is the property of Polish Academy of Sciences and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Copyright of Archives of Metallurgy & Materials is the property of Polish Academy of Sciences and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Very low density eutectic Ca 72 Mg 28 at.% metallic glass was produced by a rapid solidification melt-spinning process. The glass is considered as being a precursor of more complex ternary Ca-Mg-Zn alloys consisting solely of biocompatible elements with the view to its potential use as bioresorbable alloy for orthopaedic applications. Density, elastic modulus, hydrogen storage capacity, thermal properties of the metallic glass, such as the glass transition, crystallization and melting temperatures, as well as heats of crystallization and melting are reported. The devitrification process of the amorphous alloy up to its melt is fully described. [ABSTRACT FROM AUTHOR]

This work deals with the effects of two individual isothermal aging experiments (450 °C/5000 h and 700 °C/2500 h) and the subsequent room-temperature electrolytic hydrogen charging of TP316H stainless steel on its Charpy V-notch (CVN) impact toughness and fracture behavior at room temperature. Microstructural analyses revealed that aging at 700 °C resulted in the abundant precipitation of intermediary phases, namely, the Cr 23 C 6- based carbide phase and Fe 2 Mo-based Laves phase, whereas aging at 450 °C resulted in much less pronounced precipitation of mostly intergranular Cr 23 C 6 -based carbides. The matrix phase of 700 °C-aged material was completely formed of austenitic solid solution with a face-centered cubic (FCC) crystal structure, whereas an additional formation of ferritic phase with a base-centered cubic (BCC) structure was detected in 450 °C-aged material. The performed microstructure observations correlated well with the obtained values of CVN impact toughness, i.e., a sharp drop in the impact toughness was observed in the material aged at 700 °C, whereas negligible property changes were observed in the material aged at 450 °C. The initial, solution-annealed (precipitation-free) TP316H material exhibited a notable hydrogen toughening effect after hydrogen charging, which has been attributed to the hydrogen-enhanced twinning-induced plasticity (TWIP) deformation mechanism of the austenitic solid solution. In contrast, both aging expositions resulted in significantly lowered hydrogen embrittlement resistance, which was likely caused by hydrogen trapping effects at the precipitate/matrix interfaces in thermally aged materials, leading to a reduced TWIP effect in the austenitic phase.

The as-cast microstructure, alloying element segregation, solidification behavior, and thermal stability of model superalloys based on Inconel 740 with various Al/Ti ratios (0.7, 1.5, 3.4) and Ta (2.0, 3.0, 4.0 wt%) concentrations were investigated via ThermoCalc simulations, scanning and transmission electron microscopy, energy-dispersive X-ray spectroscopy, dilatometry, and differential scanning calorimetry. The solidification of the superalloys began with the formation of primary γ dendrites, followed by MC carbides. The type of subsequently formed phases depended on the superalloys' initial Al/Ti ratio and Ta concentration. The results obtained from solidification simulations were compared to the obtained microstructures. For all castings, the dendritic regions consisted of fine γ' precipitates, with their size mainly depending on the initial Al/Ti ratio, whereas in the interdendritic spaces, (Nb, Ta, Ti)C carbides and Nb-rich Laves phase precipitates were present. In high Al/Ti ratio superalloys, β-NiAl precipitates, strengthened by η and α-Cr phases, were observed. Based on dilatometric results, the dissolution of γ' precipitates was accompanied by a substantial increase in the coefficient of thermal expansion. The end of the dilatation effect took place around the γ' solvus temperature, as determined via calorimetry. Moreover, the bulk solidus temperature was preceded by the dissolution of the Laves phase, which may be accompanied by local melting.

In situ X-ray diffraction and transmission electron microscopy has been used to investigate René 108 Ni-based superalloy after short-term annealing at high-homologous temperatures. Current work is focused on characterisation of γ' precipitates, their volume fraction, evolution of the lattice parameter of γ and γ' phases and misfit parameter of γ' in the matrix. Material in the initial condition is characterised by a high-volume fraction (over 63%) of γ' precipitates. Irregular distribution of alloying elements was observed. Matrix channels were strongly enriched in Cr, Co, W and Mo, whereas precipitates contain large amount of Al, Ti, Ta and Hf. Exposure to high-homologous temperatures in the range 1100-1250 °C led to the dissolution of the precipitates, which influenced the change of lattice parameter of both γ and γ' phases. The lattice parameter of the matrix continuously grew during holding at high temperatures, which had a dominant influence on the more negative misfit coefficient.

The chemical composition of standard Inconel 740 superalloy was modified by changes in the Al/Ti ratio (0.7, 1.5, 3.4) and addition of Ta (2.0, 3.0, 4.0%). Remelted Inconel 740 (A0) and nine variants with various chemical compositions were fabricated by lost-wax casting. The microstructure, microsegregation, phase transformation temperatures, thermal expansion coefficients and hardness of the superalloys were investigated by scanning electron microscopy, energy dispersive X-ray spectroscopy, differential scanning calorimetry, dilatometry and Vickers measurements. Typical dendritic microstructure was revealed with microsegregation of the alloying elements. Segregation coefficient k i for Ti, Nb and Ta did not exceed unity, and so precipitates enriched mainly in these elements were found in interdendritic spaces. The Nb-rich blocky precipitates, MC carbides, MN nitrides, oxides, and fine γ' was in all modified castings. Presence of other microstructural features, such as Ti-rich needles, eutectic γ-γ' islands, small Al-rich and Cr-rich precipitates depended on the casting composition. The lowest solidus and liquidus temperatures were observed in superalloys with a high Al/Ti ratio. Consequently, in A7-A9 variants, the solidification range did not exceed 100 °C. In the A0 variant the difference between liquidus and solidus temperature was 138 °C. Hardness of all modified superalloys was at least 50% higher than for the remelted Inconel 740 (209 HV10).

The main goal of this study was to develop a new processing technology for a high-strength low-alloy (HSLA) steel in order to maximize the mechanical properties attainable at its low alloy levels. Samples of the steel were processed using thermal deformation schedules carried out in single-phase (γ) and dual-phase (γ + α) regions. The samples were rolled at unconventional finishing temperatures, their final mechanical properties were measured, and their strength and plasticity behavior was analyzed. The resulting microstructures were observed using optical and transmission electron microscopy (TEM). They consisted of martensite, ferrite and (NbV)CN precipitates. The study also explored the process of ferrite formation and its influence on the mechanical properties of the material.