Search

Using two different hydrosilylation methods, low temperature thermal and UV initiation, silicon (111) hydrogenated surfaces were functionalized in presence of an OH-terminated alkyne, a CF 3 -terminated alkyne and a mixed equimolar ratio of the two alkynes. XPS studies revealed that in the absence of premeditated surface radical through low temperature hydrosilylation, the surface grafting proceeded to form a Si-O-C linkage via nucleophilic reaction through the OH group of the alkyne. This led to a small increase in surface roughness as well as an increase in hydrophobicity and this effect was attributed to the surficial etching of silicon to form nanosize pores (∼1-3 nm) by residual water/oxygen as a result of changes to surface polarity from the grafting. Furthermore in the radical-free thermal environment, a mix in equimolar of these two short alkynes can achieve a high contact angle of ∼102°, comparable to long alkyl chains grafting reported in literature although surface roughness was relatively mild (rms = ∼1 nm). On the other hand, UV initiation on silicon totally reversed the chemical linkages to predominantly Si-C without further compromising the surface roughness, highlighting the importance of surface radicals determining the reactivity of the silicon surface to the selected alkynes.

In this letter, we report results of a hydrosilylation carried out on bifunctional molecules by using two different approaches, namely through thermal treatment and photochemical treatment through UV irradiation. Previously, our group also demonstrated that in a mixed alkyne/alcohol solution, surface coupling is biased towards the formation of Si-O-C linkages instead of Si-C linkages, thus indirectly supporting the kinetic model of hydrogen abstraction from the Si-H surface (Khung, Y. L. et al. Chem. - Eur. J. 2014, 20, 15151-15158). To further examine the probability of this kinetic model we compare the results from reactions with bifunctional alkynes carried out under thermal treatment (<130°C) and under UV irradiation, respectively. X-ray photoelectron spectroscopy and contact angle measurements showed that under thermal conditions, the Si-H surface predominately reacts to form Si-O-C bonds from ethynylbenzyl alcohol solution while the UV photochemical route ensures that the alcohol-based alkyne may also form Si-C bonds, thus producing a monolayer of mixed linkages. The results suggested the importance of surface radicals as well as the type of terminal group as being essential towards directing the nature of surface linkage.

In a stringent and near oxygen-free environment, Si-H surfaces were introduced to a trifluoroalkyne, an alcohol-derivatized alkyne, as well as an equal mixture of both alkynes at a temperature of 130°C. Contact angle measurements, high-resolution X-ray photoelectron spectroscopy (XPS), and angle-resolved XPS were performed to examine the system. Si-H surfaces were found to have a strong preference towards the formation of Si-O-C rather than Si-C bonds when the alcohol and alkyne reactivities were compared.

Smart surfaces presenting both antifouling molecules with a charged functional group at their distal end, and molecules that are terminated by RGD peptides for cell adhesion, were fabricated and characterized (see picture). By applying potentials of +300 or −300 mV, the surfaces could be dynamically switched to make the peptide accessible or inaccessible to cells.