Search

Pb(Zr,Ti)O3 (PZT) is the most common ferroelectric (FE) material widely used in solid‐state technology. Despite intense studies of PZT over decades, its intrinsic band structure, electron energy depending on 3D momentum k, is still unknown. Here, Pb(Zr0.2Ti0.8)O3 using soft‐X‐ray angle‐resolved photoelectron spectroscopy (ARPES) is explored. The enhanced photoelectron escape depth in this photon energy range allows sharp intrinsic definition of the out‐of‐plane momentum k and thereby of the full 3D band structure. Furthermore, the problem of sample charging due to the inherently insulating nature of PZT is solved by using thin‐film PZT samples, where a thickness‐induced self‐doping results in their heavy doping. For the first time, the soft‐X‐ray ARPES experiments deliver the intrinsic 3D band structure of PZT as well as the FE‐polarization dependent electrostatic potential profile across the PZT film deposited on SrTiO3 and LaxSrMn1−xO3 substrates. The negative charges near the surface, required to stabilize the FE state pointing away from the sample (P+), are identified as oxygen vacancies creating localized in‐gap states below the Fermi energy. For the opposite polarization state (P−), the positive charges near the surface are identified as cation vacancies resulting from non‐ideal stoichiometry of the PZT film as deduced from quantitative XPS measurements. [ABSTRACT FROM AUTHOR]

The effect of Ni-Nb co-doping on the structural, electromechanical, and dielectric properties of lead titanate (PT) ceramics is examined. The studies have shown that Ni-Nb co-doping has both softening and hardening effects as a function of donor or acceptor behavior of different amounts of Ni-Nb and the segregation of a small amount of a secondary phase has occurred, lattice constants and tetragonality has decreased and the resulting ceramic has become very hard.

Electrocaloric effect is the adiabatic temperature change in a dielectric material when an electric field is applied or removed, and it can be considered as an alternative refrigeration method. Materials with ferroelectric order exhibit large temperature variations in the vicinity of a phase transition, while antiferroelectrics and relaxors may exhibit a negative electrocaloric effect. In this study, the temperature variation in polarization was investigated for epitaxial ferroelectric thin film structures based on PbZrTiO3 materials in simple or complex multilayered structures. We propose the intriguing possibility of a giant negative electrocaloric effect (ΔT = −3.7 K at room temperature and ΔT = −5.5 K at 370 K) in a simple epitaxial Pb(ZrTi)O3 capacitor. Furthermore, it was shown that abnormal temperature variation in polarization is dependent on the non-FE component introduced in a multilayered structure. No significant variation in polarization with temperature was obtained for PZT/STON multilayered structures around room temperature. However, for PZT/BST or PZT/Nb2O5 multilayers, an abnormal temperature variation in polarization was revealed, which was similar to a simple PZT layer. The giant and negative ∆T values were attributed to internal fields and defects formed due to the large depolarization fields when the high polarization of the FE component was not fully compensated either by the electrodes or by the interface with an insulator layer. The presented results make Pb(ZrTi)O3-based structures promising for cooling applications operating near room temperature. [ABSTRACT FROM AUTHOR]

The ferroelectric and pyroelectric properties of bismuth ferrite (BFO) epitaxial thin film have been investigated. The ferroelectric epitaxial thin layer has been deposited on strontium titanate (STO) (001) substrate by pulsed laser deposition, in a capacitor geometry using as top and bottom electrode a conductive oxide of strontium ruthenate (SRO). The structural characterizations performed by X-ray diffraction and atomic force microscopy demonstrate the epitaxial character of the ferroelectric thin film. The macroscopic ferroelectric characterization of BFO revealed a rectangular shape of a polarization-voltage loop with a remnant polarization of 30 μC/c m2 and a coercive electric field of 633 KV/cm at room temperature. Due to low leakage current, the BFO capacitor structure could be totally pooled despite large coercive fields. A strong variation of polarization is obtained in 80–400 K range which determines a large pyroelectric coefficient of about 10−4 C/m2 K deduced both by an indirect and also by a direct method. [ABSTRACT FROM AUTHOR]

Fe (acceptor) and Nb (donor) doped epitaxial Pb(Zr0.2Ti0.8)O3 (PZT) films were grown on single crystal SrTiO3 substrates and their electric properties were compared to those of un-doped PZT layers deposited in similar conditions. All the films were grown from targets produced from high purity precursor oxides and the doping was in the limit of 1% atomic in both cases. The remnant polarization, the coercive field and the potential barriers at electrode interfaces are different, with lowest values for Fe doping and highest values for Nb doping, with un-doped PZT in between. The dielectric constant is larger in the doped films, while the effective density of charge carriers is of the same order of magnitude. An interesting result was obtained from piezoelectric force microscopy (PFM) investigations. It was found that the as-grown Nb-doped PZT has polarization orientated upward, while the Fe-doped PZT has polarization oriented mostly downward. This difference is explained by the change in the conduction type, thus in the sign of the carriers involved in the compensation of the depolarization field during the growth. In the Nb-doped film the majority carriers are electrons, which tend to accumulate to the growing surface, leaving positively charged ions at the interface with the bottom SrRuO3 electrode, thus favouring an upward orientation of polarization. For Fe-doped film the dominant carriers are holes, thus the sign of charges is opposite at the growing surface and the bottom electrode interface, favouring downward orientation of polarization. These findings open the way to obtain p-n ferroelectric homojunctions and suggest that PFM can be used to identify the type of conduction in PZT upon the dominant direction of polarization in the as-grown films. [ABSTRACT FROM AUTHOR]