Search

High crystalline quality coaxial GaInN/GaN multiple quantum shells (MQSs) grown on dislocation-free nanowires are highly in demand for efficient white-/micro-light-emitting diodes (LEDs). Here, we propose an effective approach to improve the MQS quality during the selective growth by metal-organic chemical vapor deposition. By increasing the growth temperature of GaN barriers, the cathodoluminescent intensity yielded enhancements of 0.7 and 3.9 times in the samples with GaN and AlGaN spacers, respectively. Using an AlGaN spacer before increasing the barrier temperature, the decomposition of GaInN quantum wells was suppressed on all planes, resulting in a high internal quantum efficiency up to 69%. As revealed by scanning transmission electron microscopy (STEM) characterization, the high barrier growth temperature allowed to achieve a clear interface between GaInN quantum wells and GaN quantum barriers on the c-, r-, and m-planes of the nanowires. Moreover, the correlation between the In incorporation and structure features in MQS was quantitatively assessed based on the STEM energy-dispersive X-ray spectroscopy mapping and line-scan profiles of In and Al fractions. Ultimately, it was demonstrated that the unintentional In incorporation in GaN barriers was induced by the evaporation of predeposited In-rich particles during low-temperature growth of GaInN wells. Such residual In contamination was sufficiently inhibited by inserting low Al fraction (∼6%) AlGaN spacers after each GaInN well. During the growth of AlGaN spacers, AlN polycrystalline particles were deposited on the surrounding dummy substrate, which suppressed the evaporation of the predeposited In-rich particles. Thus, the presence of AlGaN spacers certainly improved the uniformity of In fraction through five GaInN quantum wells and reduced the diffusion of point defects from n-core to MQS active structures. The superior coaxial GaInN/GaN MQS structures with the AlGaN spacer are supposed to improve the emission efficiency in white-/micro-LEDs.

Here, we systematically investigated the growth conditions of an n-GaN cap layer for nanowire-based light emitters with a tunnel junction. Selective-area growth of multiple quantum shell (MQS)/nanowire core-shell structures on a patterned n-GaN/sapphire substrate was performed by metal-organic vapor phase epitaxy, followed by the growth of a p-GaN, an n++/ p++-GaN tunnel junction, and an n-GaN cap layer. Specifically, two-step growth of the n-GaN cap layer was carried out under various growth conditions to determine the optimal conditions for a flat n-GaN cap layer. Scanning transmission electron microscopy characterization revealed that n++-GaN can be uniformly grown on the m-plane sidewall of MQS nanowires. A clear tunnel junction, involving 10-nm-thick p++-GaN and 3-nm-thick n++-GaN, was confirmed on the nonpolar m-planes of the nanowires. The Mg doping concentration and distribution profile of the p++-GaN shell were inspected using three-dimensional atom probe tomography. Afterward, the reconstructed isoconcentration mapping was applied to identify Mg-rich clusters. The density and average size of the Mg clusters were estimated to be approximately 4.3 × 1017 cm-3 and 5 nm, respectively. Excluding the Mg atoms contained in the clusters, the remaining Mg doping concentration in the p++-GaN region was calculated to be 1.1 × 1020 cm-3. Despite the lack of effective activation, a reasonably low operating voltage and distinct light emissions were preliminarily observed in MQS nanowire-based LEDs under the optimal n-GaN cap growth conditions. In the fabricated MQS-nanowire devices, carriers were injected into both the r-plane and m-plane of the nanowires without a clear quantum confinement Stark effect.

Multi-color emission from coaxial GaInN/GaN multiple-quantum-shell (MQS) nanowire-based light-emitting diodes (LEDs) was identified. In this study, MQS nanowire samples for LED processes were selectively grown on patterned commercial GaN/sapphire substrates using metal–organic chemical vapor deposition. Three electroluminescence (EL) emission peaks (440, 540, and 630 nm) were observed, which were primarily attributed to the nonpolar m-planes, semipolar r-planes, and the polar c-plane tips of nanowire arrays. A modified epitaxial growth sequence with improved crystalline quality for MQSs was used to effectively narrow the EL emission peaks. Specifically, nanowire-based LEDs manifested a clear redshift from 430 nm to 520 nm upon insertion of AlGaN spacers after the growth of each GaInN quantum well. This demonstrates the feasibility of lengthening the EL emission wavelength since an AlGaN spacer can suppress In decomposition of the GaInN quantum wells during ramping up the growth temperature for GaN barriers. EL spectra showed stable emission peaks as a function of the injection current, verifying the critical feature of the non-polarization of GaN/GaInN MQSs on nanowires. In addition, by comparing EL and photoluminescence spectra, the yellow-red emission linked to the In-fluctuation and point defects in the c-plane MQS was verified by varying the activation annealing time and lowering the growth temperature of the GaInN quantum wells. Therefore, optimization of MQS nanowire growth with a high quality of c-planes is considered critical for improving the luminous efficiency of nanowire-based micro-LEDs/white LEDs.

GaInN/GaN multiple quantum shells (MQS) nanowires and p-GaN shells were embedded with n-GaN layers through tunnel junction (TJ) shells using metalorganic chemical vapor deposition (MOCVD) method. The MQS nanowires were selectively grown on n-GaN/sapphire or GaN substrates. The fabrication process of laser structures with different resonators of 600500, 750, 1000 μm, and cavity widths of 7, 12, and 17 μm were investigated with insulating layer on the sidewalls of the ridge. The structures of the fabricated devices were characterized by scanning electron microscope (SEM) and current-voltage-light output characteristics were evaluated. Two different methods for mirror formation, etching and cleavage, were developed for the laser devices. During the investigation, a superior mirror formation suffered from the difference in etching rate between GaInN and GaN, generating concaves in the MQS region. Bluegreen light emission was observed from the entire ridge surface of the MQS index-guided laser structures. A maximum current density of emission at 17.9 kA/cm2 has been confirmed in the devices. The electroluminescence and cathodoluminescence measurements demonstrated that the r-plane and c-plane at the top of the MQS are dominant at low current densities, and the m-plane emission becomes stronger as the current density increases.

A tunnel junction and a n-GaN cap layer grown on the multi-quantum shells (MQS) /nanowires are introduced to decrease the resistivity and optical loss. The selective-area growth of the MQS/nanowire core-shell structures on the template was performed by metalorganic vapour phase epitaxy (MOVPE). Further, the MQS structure was covered with the tunnel junction and the n-GaN cap layer. Here, the growth conditions of the n-GaN cap layer were systemically investigated. The effect of p-GaN shape on the morphology of grown n-GaN cap layer was also assessed.

The selective-monolithic growth of coaxial GaInN/GaN NWs was investigated by changing the TEG flow rate, barrier and well growth temperature during MQS growth. In incorporation increased with a higher TEG flow rate. However, In-rich flakes were formed the NWs resulting in the deterioration of crystal quality. Using a higher growth temperature of quantum barriers, abnormal growth at the top of NWs was eliminated. As a result, the CL emission intensity was enhanced. Furthermore, the occurrence of In desorption was suppressed by decreasing the growth temperature of quantum wells. Therefore, these results are promising for NW-based white LEDs.

In this study, the growth mechanisms of n-type gallium nitride (GaN) cap layers for embedding nanowire-based multi-quantum-shell (NW-MQS) with a tunnel junction were investigated using the metal–organic vapor-phase epitaxy method. Herein, instead of a p-type GaN layer, n-type GaN cap layers were applied as a contact layer to the anode electrode via a tunnel junction. NW-MQSs were prepared in a rectangular grid arrangement aligning with the m- and a-axis of GaN. The growth mode of the cap layers was controlled in three stages using different growth pressures and temperatures. The first cap layer was a faceted growth mode primarily comprising the r-plane, the second was a lateral growth mode that expanded the area of the c-plane, and the third was an acceleration of lateral growth. Finally, cap layers with a flat surface were realized. Void formation in the cap layers occurred only between the NW-MQSs along the m-axis of GaN. This observation can be attributed to the difference in the coalescence of the cap layers in the a- and m-axis directions. We believe that the NW-MQS structure with the cap layer that was optimized in this study can be used as a highly efficient optical device.

This study aimed to investigate and analyze the impurity doping characteristics in tunnel junctions (TJs) grown on core–shell structures, comprising GaInN/GaN multiple-quantum-shells (MQSs) and GaN nanowires. To this end, the impurity, structural, and electrical properties of the samples were characterized by scanning electron microscopy, scanning transmission electron microscopy, atom probe tomography (APT), nanoscale secondary ion mass spectrometry (NanoSIMS), and electroluminescence of the device which was fabricated for a prototype laser device to demonstrate an electrical operation of the MQSs layer. From the experimental results of NanoSIMS and APT, we demonstrated that the Mg-related problems in the TJ, such as the diffusion to the n++-GaN layer from the p+-GaN layer and formation of clusters in p+-GaN, are critical. Consequently, they cause a high operating voltage and dot-like spot emission of the light-emitting device. Based on the analysis, we suggested remedies and strategies to further improve the TJs that work well.

In this study, we discuss the influence of SiH4 flow rates on the structural and optical properties of GaN nanowires (NWs) with multiple-quantum-shells (MQSs). To this end, we prepared two n-GaN core NW samples with different SiH4 flow rates. Subsequently, MQS active layers of the same structure were grown on each n-GaN core NW under identical growth conditions. The samples were characterized by scanning electron microscopy, scanning transmission electron microscopy, energy-dispersive X-ray, and cathodoluminescence (CL) mapping. From the experimental results, we ascertained that a Si-rich layer was created between the sidewall of the NWs and MQSs, in which the number of Si atoms was mainly determined by the SiH4 flow rate. These Si atoms diffused into the MQSs during the growth, and significantly impacted the structural and optical properties, such as the shape and crystalline quality of the MQSs and NWs, and the CL intensity of the MQSs. On the basis of experimental results, we conclude that the SiH4 flow rate during the NW growth plays a critical role in the performance of an MQS-based optoelectronic semiconductor device.

Tunable emission wavelengths from 415 nm to 600 nm were demonstrated in coaxial GaInN/GaN multiple quantum shells (MQS) grown on three-dimensional nanostructures. Uniform aperture arrays with different diameters and pitches were patterned on GaN/sapphire substrates by nanoimprint and e-beam lithography. Thereafter, the coaxial GaInN/GaN MQS structures were selectively grown on the nanostructures using metalorganic chemical vapor deposition (MOCVD). To achieve long wavelength emissions, a detailed investigation in terms of height, filling factor, diameter of apertures, and pitch was performed for clarifying the In incorporation in nanostructures. Scanning transmission electron microscopy (STEM) features demonstrate that the diffusion of precursors on SiO2 mask area plays an important role in the coaxially growth of MQS structures on naonopyramids. A growth model based on the diffusion length and pitch was proposed to explain the experimental results. It was clarified that the probability of In incorporation was promoted in nanopyramids with a small pitch (less than 3 times of the diffusion length), wherein direct impinged adatoms on nanopyramids also diffused and participated in the growth on the neighbor. With a decrease in the intervals of aperture patterns, emission longer than 600 nm can be achieved for white and micro light-emitting diodes.