Search

We investigated the possibility of synthesizing Co nanoparticles in CoZrnH/AlOx(OH)y/Al ceramic–metal catalysts and controlling the catalytic properties of these nanoparticles in syngas conversion by changing the Co/Zr ratio. The CoZr nanocomposites were obtained from metal powders by mechanochemical activation in a high-energy mill under an argon atmosphere, followed by treatment with hydrogen at high pressure and room temperature. Ceramic–metal catalysts were prepared by mixing the corresponding CoZrnH powder nanocomposite (30 wt%) with powdered aluminum (70 wt%), hydrothermal treatment of the mixture and subsequent calcination. The materials were characterized with a set of physicochemical methods: powder X-ray diffraction, scanning electron microscopy, 59Co internal field nuclear magnetic resonance spectroscopy, and temperature programmed reduction. Catalytic studies were performed in a laboratory fixed-bed flow reactor at 2 MPA and 210–270 °C. It is shown that the activity in syngas conversion to C5+ hydrocarbons and selectivity to methane and C2–C4 hydrocarbons depend on the Co/Zr ratio. Thus, with an increase in the zirconium content in the samples, the interaction of metal cobalt with metal zirconium improves in the process of mechanical activation and subsequent treatment with hydrogen. The destruction of the agglomerates of crystallites of metallic cobalt in the form of β-Co (Cofcc) occurs as well as their transformation to α-Co (Cohcp) particles active in the syngas conversion to C5+ hydrocarbons. This can explain the highest specific yield of C5+ hydrocarbons on a cermet with the lowest Co/Zr ratio. [ABSTRACT FROM AUTHOR]

The paper presents the results of the synthesis and study of CuAl layered double hydroxides (LDHs) as well as their application as catalysts for the selective hydrogenation of crotonaldehyde. Phase-homogeneous LDHs were obtained by co-precipitation and mechanochemical methods, and critical parameters ensuring the formation of the target product were identified. In the case of coprecipitation, the formation of LDH is most affected by the pH of the reaction medium and the CO32−/Al3+ ratio. The optimal CO32−/Al3+ ratio is ca. 0.5–0.8 and pH 9.5–10.0. When mechanochemical synthesis is used, at 500 m·s−2 and 60 min, it is possible to obtain a single-phase CuAl LDH, whereas at higher energies, LDH is destroyed. The mechanochemical method makes it possible not only to reduce the synthesis time and the amount of alkaline wash water but also to obtain more dispersed copper particles with a higher hydrogenating activity. The conversion of 2-butenal (T = 80 °C, P = 0.5 MPa, 180 min, ethanol) for this sample was 99.9%, in contrast to 50.5% for the catalyst obtained by co-precipitation. It is important that, regardless of the conversion, both catalysts showed high selectivity (S = 90–95%) for the double bond hydrogenation. [ABSTRACT FROM AUTHOR]

We investigated the possibility of synthesizing Co nanoparticles in CoZr n H/AlO x (OH) y /Al ceramic-metal catalysts and controlling the catalytic properties of these nanoparticles in syngas conversion by changing the Co/Zr ratio. The CoZr nanocomposites were obtained from metal powders by mechanochemical activation in a high-energy mill under an argon atmosphere, followed by treatment with hydrogen at high pressure and room temperature. Ceramic-metal catalysts were prepared by mixing the corresponding CoZr n H powder nanocomposite (30 wt%) with powdered aluminum (70 wt%), hydrothermal treatment of the mixture and subsequent calcination. The materials were characterized with a set of physicochemical methods: powder X-ray diffraction, scanning electron microscopy, 59 Co internal field nuclear magnetic resonance spectroscopy, and temperature programmed reduction. Catalytic studies were performed in a laboratory fixed-bed flow reactor at 2 MPA and 210-270 °C. It is shown that the activity in syngas conversion to C 5+ hydrocarbons and selectivity to methane and C 2 -C 4 hydrocarbons depend on the Co/Zr ratio. Thus, with an increase in the zirconium content in the samples, the interaction of metal cobalt with metal zirconium improves in the process of mechanical activation and subsequent treatment with hydrogen. The destruction of the agglomerates of crystallites of metallic cobalt in the form of β-Co (Co fcc ) occurs as well as their transformation to α-Co (Co hcp ) particles active in the syngas conversion to C 5+ hydrocarbons. This can explain the highest specific yield of C 5+ hydrocarbons on a cermet with the lowest Co/Zr ratio.