Search

In this research work, raw poultry manure biochar (RPM-B) was post-modified by two metal salts and then evaluated for P recovery from aqueous solutions in batch mode. The modified biochar characterization showed that RPM-B impregnation with aluminum and manganese salts led to a significant improvement of their surface properties through the pH-zero charge reduction as well as the specific surface areas and the functional group contents increase. Phosphorus recovery tests indicated that the post-treated biochar with AlCl3 (RPM-B-Al) and with KMnO4 (RPM-B-Mn) exhibited relatively high recovery efficiencies with Langmuir’s adsorption capacities of 23.5 and 8.4 mg g−1, respectively. Kinetics and isothermal data modeling, as well as the in-depth analytical characterization of the post-modified biochars before and after adsorption, indicates that P recovery occurs homogeneously on monolayer surfaces through mainly anion exchange, precipitation, and electrostatic interactions. On the other hand, P desorption efficiency increases with the desorbing solution pH values. The best P desorption yields were observed for an initial pH of 9.0 to 78% and 80% for RPM-B-Al-P and RPM-B-Mn-P, respectively. All these results suggest that RPM-B-Al and RPM-B-Mn could be considered promising materials for phosphorus recovery from wastewaters with a possible reuse in agriculture as potential soil amendments.

In this study, nutrients release/adsorption from/by raw poultry manure-derived biochar produced at a pyrolysis temperature of 600 &deg, C (RPM-B) was assessed under static and dynamic conditions. Batch sequential leaching experiments of RPM-B for a total contact time of 10 days showed that both phosphorus and potassium were slowly released but with higher amounts compared to various other animal- and lignocellulosic-derived biochars. The cumulated released P and K amounts were assessed to 93.6 and 17.1 mg g&minus, 1, which represent about 95% and 43% of their original contents in the RPM-B, respectively. The column combined leaching/adsorption experiments showed that amending an alkaline sandy agricultural soil with two doses of RPM-B (at 5% and 8% w:w) resulted in an efficient retention of NO3-N and NH4-N, and on the contrary, important leached amounts of PO4-P, K+, Mg2+, and Ca2+ but with relatively slow kinetic release rates for a long period. Even after 40 days of dynamic leaching, these latter nutrients continued to be released with kinetic rates lower than 10 mg kg&minus, 1 d&minus, 1. Thus, compared to synthetic fertilizers, RPM-B valorization as organic amendment for poor semiarid soils could be considered as an attractive, eco-friendly, and sustainable waste recycling option.

Raw poultry manure (RPM) and its derived biochars at temperatures of 400 (B400) and 600 &deg, C (B600) were physico-chemically characterized, and their ability to release nutrients was assessed under static conditions. The experimental results showed that RPM pyrolysis operation significantly affects its morphology, surface charges, and area, as well as its functional groups contents, which in turn influences its nutrient release ability. The batch experiments indicated that nutrient release from the RPM as well as biochars attains a pseudo-equilibrium state after a contact time of about 48 h. RPM pyrolysis increased phosphorus stability in residual biochars and, in contrast, transformed potassium to a more leachable form. For instance, at this contact time, P- and K-released amounts passed from 5.1 and 25.6 mg g&minus, 1 for RPM to only 3.8 and more than 43.3 mg g&minus, 1 for B400, respectively. On the other hand, six successive leaching batch experiments with a duration of 48 h each showed that P and K release from the produced biochars was a very slow process since negligible amounts continued to be released even after a total duration of 12 days. All these results suggest that RPM-derived biochars have specific physico-chemical characteristics allowing them to be used in agriculture as low-cost and slow-release fertilizers.