Structural and electrical properties of nonpolar m-GaN films grown on m-SiC using standard metalorganic chemical vapor deposition (MOCVD) and two versions of sidewall epitaxial lateral overgrowth were studied. It is shown that lateral overgrowth allows one to dramatically reduce the dislocation density from over 109 cm-2 to ∼107 cm-2. In good correlation with that we observed a strong reduction in the density of electron traps Ec-0.25 eV and Ec-0.6 eV from over 1015 cm-3 to ∼1014 cm-3, respectively, in MOCVD m-GaN and in laterally overgrown m-GaN. Preliminary studies of the effects of changing the V/III ratio and of Si doping were performed. The MOCVD m-GaN films grown with high V/III ratio of 1000 were semi-insulating, with the Fermi level pinned near the 0.6 eV traps. Decreasing the V/III value to 250 shifted the Fermi level upward, close to the level of the 0.25 eV traps. Si doping in laterally overgrown samples strongly suppressed the formation of major electron traps but enhanced the formation of hole traps near Ev+0.9 eV. We also report on electrical properties of the GaN interface with the AlN buffer used to facilitate good quality growth on SiC. These properties are dominated by a high concentration of 0.15 eV traps. [ABSTRACT FROM AUTHOR]

The electrical and structural properties of AlN/GaN heterostructures grown by molecular beam epitaxy on sapphire are compared with those of AlGaN/GaN heterostructures. The structural characteristics as assessed by x-ray diffraction show little difference but the electron density in the two-dimensional electron gas is about twice higher for AlN/GaN structures with only slightly lower mobility than in AlGaN/GaN. By proper choice of the Fe doping in GaN(Fe) and the thickness of unintentionally doped GaN layers, the composite buffer of the structure can be made semi-insulating. The current through the AlN/GaN structures is determined by tunneling through the AlN barrier and is much higher than that for AlGaN/GaN films due to the lower thickness of AlN compared to AlGaN. Increasing the thickness of AlN from 3 to 4 nm decreases the leakage current by about an order of magnitude. [ABSTRACT FROM AUTHOR]