Search

Nanocrystalline apatites with different Ca/P ratios were synthesized using eggshell as a calcium source by microwave processing. The apatites were found to have a minor amount of Mg, Sr, Si and Na ions inherited from the eggshells. The presence of several foreign ions results in a perturbed lattice structure indicated by an increase in lattice constants and shift in vibrational frequencies of the functional groups. The apatites were heat treated to investigate the influence of foreign ions on thermal stability. The minor amounts of ions do not affect the thermal stability. The differences in thermal behaviour of these apatites were due to the presence of HPO(2-)(4) ions only and not due to other ions because of their low content.

Anodic TiO coatings were produced on Ti-6Al-4V substrates using aqueous electrolytes containing dissolved calcium and phosphorus. Two baths containing Ca and P compounds, in the molar ratios 5 and 15 were used. Different coatings were produced by electrolysis for 3 and 10 h at a constant current density of 10 mA/cm(2). X-ray diffraction and X-ray fluorescence were used to identify the phases and chemical composition respectively. Thickness of the coatings was measured using ellipsometry. Electrochemical polarization and AC impedance studies were performed on the coatings by exposing them to simulated body fluid (SBF) for a period of 1 week. The coating produced by 10-h electrolysis from bath of Ca/P ratio 15 showed low corrosion current and high impedance to the week-long attack of SBF.

Use of titanium as biomaterial is possible because of its very favorable biocompatibility with living tissue. Titanium implants having calcium phosphate coatings on their surface show good fixation to the bone. This review covers briefly the requirements of typical biomaterials and narrowly focuses on the works on titanium. Calcium phosphate ceramics for use in implants are introduced and various methods of producing calcium phosphate coating on titanium substrates are elaborated. Advantages and disadvantages of each type of coating from the view point of process simplicity, cost-effectiveness, stability of the coatings, coating integration with the bone, cell behavior, and so forth are highlighted. Taking into account all these factors, the efficient method(s) of producing these coatings are indicated finally.

The eggshell waste has been value engineered to a nanocrystalline hydroxyapatite (HA) by microwave processing. To highlight the advantages of eggshell as calcium precursor in the synthesis of HA (OHA), synthetic calcium hydroxide was also used to form HA (SHA) following similar procedure and were compared with a commercially available pure HA (CHA). All the HAs were characterized by X-ray powder diffraction (XRD) method, Fourier transform infrared (FT-IR) spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and specific surface area measurements. Nanocrystalline nature of OHA is revealed through characteristic broad peaks in XRD patterns, platelets of length 33-50 nm and width 8-14 nm in TEM micrograph and size calculations from specific surface area measurements. FT-IR spectra showed characteristic bands of HA and additionally peaks of carbonate ions. The cell parameter calculations suggest the formation of carbonated HA of B-type. The OHA exhibits superior sinterability in terms of hardness and density than both SHA and CHA may be due to larger surface area of its spherulite structure. The in vitro dissolution study shows longer stability in phosphate buffer and cell culture test using osteoblast cells establishes biocompatibility of OHA.

Electrodeposited anodic oxide coatings were produced on Ti-6Al-4V substrates using aqueous electrolytes containing dissolved calcium and phosphorus. Different coatings were produced by varying the time periods. The coatings were characterised by XRD technique and TEM. The coatings were exposed to Simulated Body Fluid (SBF). Electrochemical polarisation and ac impedance studies too were performed on the coatings in SBF. Pins were coated and run against wooden disc in pin-on-disc type of wear tests. Coatings produced from long time electrolysis showed very good resistance to the attack of SBF and less wear compared to those produced from short time exposure.

Rapid synthesis of calcium deficient hydroxyapatite (CDHA, Ca(10-x)(HPO4)x(PO4)(6-x)(OH)(2-x)) with Ca/P ratio 1.5 was done by precipitation using calcium nitrate tetra-hydrate and phosphoric acid and subsequently subjecting to microwave irradiation in a domestic microwave oven for 15 min. Transmission electron microscopy analysis shows needle like morphology of CDHA having length 16-39 nm and width 7-16 nm. The synthesized CDHA has the characteristic HPO4(2-) vibration band at 875 cm(-1) in Fourier transform infrared (FT-IR) spectra. The X-ray powder diffraction (XRD) analysis shows a pattern corresponding to stoichiometric hydroxyapatite (HA) with broad peaks suggesting that CDHA particles were nanosized. Fourier transform Raman spectroscopy (FT-Raman) do not indicate any fluorescence band that is characteristic of non-stoichiometric HA. The thermal decomposition of CDHA to beta tricalcium phosphate (beta-TCP) was also studied for the additional confirmation. The nanosized CDHA was found to be stable up to 600 degrees C.