Search

Perovskite oxides (ABO3) due to their high thermal stability and the ability to control the physico-chemical properties are considered as an alternative to traditional catalysts containing noble and transition metals. Herein, the recent research breakthroughs of GdCoO3 catalysts in experimental studies are summarized in detail. First, the perovskite-type GdCoO3 complex oxides were obtained by co-precipitation method with the various precipitators and were characterized by X-ray diffraction (XRD), low temperature nitrogen adsorption and IR spectroscopy. Physical and chemical analysis showed that the choice of precipitant doesn’t significantly affect the phase composition of the perovskites. The catalytic performance of gadolinium cobaltites was discussed. It was found that the use of cobaltites obtained by co-precipitation leads to the inhibition of the side reaction of the reverse steam reforming of carbon monoxide. Finally, the investigation of the used catalysts demonstrated the formation of Gd2O2CO3 and metallic cobalt, which indicates the nature of active centres: gadolinium is the centre of CO adsorption, while hydrogen chemisorption occurs on cobalt-sites.

The effect of strontium substitution in the structure of the complex oxide Gd2SrFe2O7 on the production of light olefins by CO hydrogenation was investigated. Perovskite-type oxides Gd2−xSr1+xFe2O7 (x = 0; 0.1; 0.2; 0.3; 0.4) were synthesized by sol–gel technology and characterized by XRD, Mössbauer spectroscopy, BET specific area, acidity testing, and SEM. The experimental data revealed a correlation between the state of iron atoms, acidity, and catalytic performance. It was found that with an increase in the content of Sr2+ in the perovskite phase, the basicity of the surface and the oxygen diffusion rate increased. This contributed to the CO dissociative adsorption, formation of active carbon, and its further interaction with atomic hydrogen. [ABSTRACT FROM AUTHOR]

The effect of the substitution of cobalt into the GdFeO3 perovskite structure on the selective hydrogenation of CO was investigated. A series of GdCoxFe1−xO3 (x = 0; 0.2; 0.5; 0.8; 1) samples were synthesized by sol-gel technology and characterized by XRD, BET specific area, DSC, TG, EDX and XPS. The experimental data made it possible to reveal a correlation between the state of iron and cobalt atoms, the fractions of surface and lattice oxygen, and catalytic characteristics. It has been found that varying the composition of GdCoxFe1−xO3 complex oxides leads to a change in the oxygen-metal binding energy in Gd-O-Me, the ratio of metals in various oxidation states, and the amount of surface and lattice oxygen, which affects the adsorption and catalytic characteristics of complex oxides. [ABSTRACT FROM AUTHOR]

KCoMoS2 was supported on various carbon support materials to study the support effect on synthesis gas conversion. Next to two activated carbons with high micropore volume, a traditional alumina (γ-Al2O3) support and its carbon coated form (CCA) were studied for comparison. Coating alumina with carbon increases the selectivity to alcohols, but the AC-supported catalysts show even higher alcohol selectivities and yields, especially at higher temperatures where the conversions over the AC-supported catalysts increase more than those over the γ-Al2O3-based catalysts. Increasing acidity leads to decreased CO conversion yield of alcohols. The two activated-carbon-supported catalysts give the highest yield of ethanol at the highest conversion studied, which seems to be due to increased KCoMoS2 stacking and possibly to the presence of micropores and low amount of mesopores. [ABSTRACT FROM AUTHOR]

Perovskite oxides (ABO3) due to their high thermal stability and the ability to control the physico-chemical properties are considered as an alternative to traditional catalysts containing noble and transition metals. Herein, the recent research breakthroughs of GdCoO3 catalysts in experimental studies are summarized in detail. First, the perovskite-type GdCoO3 complex oxides were obtained by co-precipitation method with the various precipitators and were characterized by X-ray diffraction (XRD), low temperature nitrogen adsorption and IR spectroscopy. Physical and chemical analysis showed that the choice of precipitant doesn't significantly affect the phase composition of the perovskites. The catalytic performance of gadolinium cobaltites was discussed. It was found that the use of cobaltites obtained by co-precipitation leads to the inhibition of the side reaction of the reverse steam reforming of carbon monoxide. Finally, the investigation of the used catalysts demonstrated the formation of Gd2O2CO3 and metallic cobalt, which indicates the nature of active centres: gadolinium is the centre of CO adsorption, while hydrogen chemisorption occurs on cobalt-sites. [ABSTRACT FROM AUTHOR]