Search

Abstract Background Sealing materials are used to fill abutment screw access holes (SAH) to prevent microleakage and protect the central screws in oral implant restoration. However, thus far, no consensus has been reached on sealing material selection. In this study, a comparison of the sealing efficacy and removal convenience of different sealing materials for cement-retained implant restoration was conducted. Methods Various sealing materials were classified into five groups, namely, gutta-percha (GP), temporary restorative paste (TRP), vinyl polysiloxane (VPS), polytetrafluoroethylene (PTFE) tape, and onlay resin (OR), and 35 sets of analog-abutments were allocated into five groups of seven specimens. A sealing efficacy test was conducted using a modified dye-penetration method, in which a lower absorbance indicated better sealing efficacy. For the removal-convenience test, the materials were removed from each SAH after solidification, and the retrieval time was recorded. Results On days 1 and 10, PTFE exhibited the highest absorbance value with significant differences compared to the other groups. On day 30, TRP and PTFE showed significantly higher absorbance values than GP, VPS, and OR, but no significant difference was detected between TRP and PTFE (p = 0.424). The absorbance values of TRP and PTFE from days 1, 10, and 30 showed significant intragroup differences, while those of the other groups did not. In terms of the removal convenience on days 1, 10, and 30, VPS achieved the best performance, followed by PTFE, OR, TRP, and GP. Conclusion Within the limitations of this experiment, VPS and OR showed better sealing efficacy against microleakage and a more convenient removal than the other materials; thus, VPS and OR are recommended for clinical use.

Abstract Background This in vitro study aimed to provide evidence regarding the selection of hole diameters of implant crowns to reduce excess cement extrusion at the abutment margin, and to examine the maintenance of their retention capacity in anterior and posterior cement-retained implant crowns. Methods Six groups of implant crowns were prepared according to the position of the teeth and the size of their holes as follows: anterior crown without hole (ANH), anterior crown with 1-mm mini venting hole (AMH), anterior crown with 2.5-mm regular screw access hole (ARH), posterior crown without hole (PNH), posterior crown with 1-mm mini venting hole (PMH), and posterior crown with 2.5-mm regular screw access hole (PRH). Temporary cement was used to bond the crowns to the abutments. The mean amount of excess cement extrusion among the different groups at the abutment margin was calculated. Retentive strength under different hole designs was measured as the dislocation force of the crown using a universal testing machine. One-way ANOVA and Welch’s t-test were used to analyze the results. Results The average amounts of extruded excess cement were 18.96 ± 0.64, 1.78 ± 0.41, and 1.30 ± 0.41 mg in the ANH, AMH, and ARH groups, respectively, and 14.87 ± 0.36, 1.51 ± 0.40, and 0.82 ± 0.22 mg in the PNH, PMH, and PRH groups, respectively. The hole opening in the crowns could significantly reduce residual cement regardless of its size (p

Although placing a vent hole on the occlusal surface of the implant crown can reduce cervical marginal cement extrusion, it has disadvantages. Transferring the hole to the buccal or lingual surface of the posterior implant crown could therefore be an alternative solution. This study investigated the effect of transferring the vent hole to the lateral side of the implant posterior crown on the hydrodynamics of excess cement extrusion and the crown’s retention ability. Specially fabricated posterior implant crowns were divided into five groups: crowns with an occlusal hole (OH), occlusal lateral hole (OLH), middle lateral hole (MLH), cervical lateral hole (CLH), and no hole (NH). Each set of implant analog-abutment-crown specimens was wrapped in a polymethylacrylate base. The base of the implant crown was divided into four 90-degree quadrants along the diagonal of the square base with a pen mark. Cement was used to bond the crowns and the abutments, and the weight of cement extrusions at the vent holes and the abutment cervical margins were calculated. The distribution of cement extrusion at the margin was photographed in each quadrant, and the areas of surface coverage of cement extrusion were compared with ImageJ software. Retentive strength was measured as the dislocation force using a universal testing machine. One-way analysis of variance was used for result analysis. The cervical marginal cement extrusions of crowns with lateral holes (OLH, MLH, and CLH) were significantly less than that of NH crowns (P