Search

This work is devoted to evaluating the corrosion behaviors of SS 304L and SS 316L in monoethanolamine solutions (MEA) containing SOX and NOX pollutants, examining both lean and CO2-loaded conditions at 25 °C and 40 °C. Electrochemical techniques (potentiodynamic and cyclic polarization) were used along with Scanning Electron Microscopy, Confocal Microscopy and weight loss measurements. The results reveal that the introduction of SOX and NOX pollutants increased the corrosion rate, whereas CO2 loading primarily reduced the corrosion resistance in the lean MEA solution, while its impact on solutions with SOX and NOX was less pronounced. This suggests that SOX and NOX play primary roles in the metal's dissolution. Also, SS 316L demonstrated superior corrosion resistance compared to 304L in nearly all of the cases examined. Elevated temperatures were also found to intensify the corrosion rate, indicating a correlation between the corrosion rate and temperature. A microscopic observation and EDX analysis revealed that corrosion products are characterized by high concentrations of iron (Fe) and oxygen (O) as well as carbon (C). There is also an indication of the possible formation of amine complexes, suggesting a potential for amine degradation. No pitting corrosion was observed in SS 304L and SS 316L across any tested solution. Finally, the immersion results expose a tendency for passivity in all amine solutions and at both temperatures after several days of exposure. Moreover, they confirm the very low corrosion rate calculated from potentiodynamic curves due to minimal weight loss after 24 days of immersion. [ABSTRACT FROM AUTHOR]

The thermoelectric materials community has made significant progress on nanostructured and processable materials to improve efficiency and flexibility, reducing manufacturing costs. Selenide compounds, such as Ag2Se and Cu2Se, have received a lot of attention because of their promising capabilities in thermoelectric applications. Additionally, Se is significantly more abundant than Te, with approximately ten times higher availability. High-energy ball milling (HEBM) process is a powerful solid-state synthesis/powder mechanical alloying method. The objective of this work is to form selenide compounds at different milling times (1–20 h) by HEBM process. The structural characterization of the compounds was studied by X-ray Diffraction and X-ray Photoelectron Spectroscopy, while the thermal stability of the prepared samples was examined by Thermogravimetric Analysis. The experimental results show that the Ag2Se sample synthesized at 20 h presents lower thermal stability because of the higher specific surface area and the increased porosity as a result of the hardening effect. Additionally, Cu2Se presents Cu2O(SeO3) as the main phase at low temperatures, while at higher temperatures, CuO is the dominant phase. Therefore, as the heating temperature increases, there is a complete evaporation of Se and a conversion of the remaining copper into copper oxide. The present study demonstrates a simple method for the synthesis of Ag2Se and Cu2Se thermoelectric materials with high oxidation resistance. [ABSTRACT FROM AUTHOR]

Nano-composite (NCD) and multi-layered (MLD) diamond coatings were deposited on cemented carbide tools using hot filament chemical vapour deposition (HFCVD) techniques. Appropriate annealings were conducted on the examined diamond coatings in order to be characterized by the same level of residual stresses. The crystalline structure of the employed diamond coatings was investigated by conducting Raman spectra. Inclined impact tests at ambient and elevated temperatures were carried out for assessing their temperature-dependent fatigue strength. Moreover, the wear behaviour of diamond coated inserts was investigating in milling aluminum foam. Raman spectra were also conducted on the treated diamond coatings for capturing potential crystalline changes developed due to the exercised thermal and dynamic mechanical loads during cutting. According to the attained results, the coexistence of sp2– and sp3-bonded phases in the cases of MLD diamond coatings results in an accelerated wear development, despite their structure capability to decelerate the crack propagation. As a result, nano-crystalline diamond coatings characterized only by sp3-bonded phase exhibit an improved wear behaviour. The cutting performance of the NCD coated inserts is further improved due to the enhanced tribological properties of the NCD coatings.

Hydrophobic films were produced on a copper surface by chemical methods. The whole process consisted of three stages. Initially the hierarchical structure of the surface was achieved by in situ reduction of Ag+ ions to Ag using silver nitrate solution, thereby creating a nanostructured surface. The copper surface was then coated with polydopamine by a simple immersion procedure. Finally, it was decorated with thiols, to achieve a hydrophobic surface. The wetting angle was used to evaluate the hydrophobicity of the produced surfaces. The anti-corrosion behavior of the produced hydrophobic films, were evaluated on the specimens that showed higher hydrophobicity by electrochemical methods. Electrochemical techniques (potentiodynamic polarization and resistance spectroscopy tests) were performed in 3.5% NaCl solution. Morphology was investigated by scanning electron microscopy (SEM). All experimental results showed a clear improvement in the corrosion behavior of the hydrophobic copper surfaces while the hydrophobicity was maintained after the corrosion tests.

Material removal processes like milling, leave only a small process window to minimally distort the surface of Aluminum foams. Wire-EDM arises as a suitable alternative. Closed-cell aluminum foams were produced and processed at various conditions through wire-EDM to investigate their effect on the foams' surface integrity. Microstructural analysis, porosity assessment and mechanical testing were employed to evaluate the footprint of the manufacturing process. Depending on the process parameters and especially on the working fluid, severe surface and pores damage may occur, affecting the mechanical response under quasistatic and high-velocity impact loads. A process optimization loop offered a distortion-free surface.

Different manufacturing and surface modification treatments distinctively affect the surface characteristics and microstructure of the workpiece, having a different impact on their effective life-span. The corrosion-fatigue behavior of as-machined (wire-EDM), blasted and anodized aluminum alloy 7075-T651 was investigated using 3.5wt% NaCl aqueous solution and distilled water as corrosive media. An in-situ corrosion-fatigue device capable of producing cyclic loads in a corrosive solution was employed, coupled with FEM analysis. Blasting process offered a prolongation of the corrosion-fatigue life-span in both corrosive media, when compared to the as-machined samples under identical conditions. Anodizing had a deleterious effect in all the examined cases.

The corrosion behavior of two stainless steels (316L and 304L) was evaluated using a CO2-loaded aqueous solution of 30 wt.% monoethanolamine (MEA) with a view to simulating corrosion related mechanisms in amine treatment procedures. Corrosion behavior was experimentally evaluated as a function of CO2 loading and solution temperature, using electrochemical techniques (polarization curves, cyclic polarization, and EIS measurement). The results reveal that the aqueous MEA solution containing CO2 creates a favorable environment for the corrosion of both stainless steels. The rate of corrosion is accelerated when the temperature of the loaded MEA solution rises, which was attributed to the thermal degradation of the loaded MEA, thus causing higher kinetics of the cathodic reactions at higher temperatures. More specifically, for the SS 304L the corrosion rate is almost doubled when the solution temperature is increased from 25 °C to 40 °C and is quadrupled when the solution temperature rises to 80 °C. For the SS 316L, the corrosion rate becomes almost threefold and sixfold upon increasing temperature of the load amine solution to 40 °C and 80 °C, respectively. The overall corrosion rate of SS 316L is lower with respect to the SS 304L for the same temperature and loading conditions. The essential dependency of corrosion rate on solution type (unloaded and loaded MEA solution) demonstrates that the corrosion process and reactions are controlled by a diffusion mechanism. [ABSTRACT FROM AUTHOR]