Search

A calculation is presented for the direct conversion of a measured luminescence signal to the implied open circuit voltage. The effects of re-absorption, spectral dependence, and interference with front and back interfaces are all included, so long as the optical properties of the structure are known. The method is validated through a comparison of the terminal open-circuit voltage with the photoluminescence intensity of Cu(In,Ga)Se2 solar cells, each as a function of illumination intensity. [ABSTRACT FROM AUTHOR]

CdSeTe/CdMgTe double heterostructures were produced with both n-type and unintentionally doped absorber layers. Measurements of the dependence of photoluminescence intensity on excitation intensity were carried out, as well as measurements of time-resolved photoluminescence decay after an excitation pulse. It was found that decay times under very low photon injection conditions are dominated by a non-radiative Shockley-Read-Hall process described using a recombination center with an asymmetric capture cross section, where the cross section for holes is larger than that for electrons. As a result of the asymmetry, the center effectively extends photoluminescence decay by a hole trapping phenomenon. A reduction in electron capture cross section appeared at doping densities over 1016cm-3. An analysis of the excitation intensity dependence of room temperature photoluminescence revealed a strong relationship with doping concentration. This allows estimates of the carrier concentration to be made through a non-destructive optical method. Iodine was found to be an effective n-type dopant for CdTe, allowing controllable carrier concentrations without an increased rate of non-radiative recombination. [ABSTRACT FROM AUTHOR]

Soil samples from a wetland in Woburn, Massachusetts are spiked with different phases of arsenic in order to measure the mobility and transport of arsenic in sediment and soil. Sequential extraction procedures are charted with verification through acid digestion.

Variable magnetic-field Hall and transient photoconductance-lifetime measurements were performed on a series of undoped, In-doped, and As-doped HgCdTe samples grown by molecular beam epitaxy (MBE). Use of quantitative mobility-spectrum analysis (QMSA) combined with multiple carrier-fitting (MCF) techniques indicates that the majority of samples contain an interfacial n-type layer that significantly influences the interpretation of the electrical measurements. This n-type layer completely masks the high-quality electrical properties of undoped or low n-type In-doped HgCdTe, as well as complicating the interpretation of activation in As-doped p-type HgCdTe. Introduction of an intentional n-type background, typically created through doping with In to "recover" high mobility, is actually shown to increase the "bulk" layer conductivity to a level comparable to the interface layer conductivity. Photoconductance-lifetime measurements suggest that In-doping may introduce Shockley-Read-Hall (SRH) recombination centers. Variable-field Hall analysis is shown to be essential for characterizing p-type material. Photoconductance-lifetime measurements suggest that trapping states may be introduced during the incorporation and activation of As. Two distinctly different types of temperature dependencies were observed for the lifetimes of As-doped samples. [ABSTRACT FROM AUTHOR]

Variable magnetic field Hall and transient photoconductance lifetime measurements were performed on a series of undoped, In-doped, and As-doped HgCdTe samples grown by molecular beam epitaxy and metalorganic chemical vapor deposition. Temperature variation and, in the case of Hall, magnetic-field variation are needed to give a more complete picture of the mechanisms that control lifetimes in HgCdTe samples. Recent predictions of recombination lifetimes from full band structure calculations were compared to experimental lifetimes at various doping levels at long-wave infrared (LWIR) and mid-wave infrared (MWIR) compositions. For n-type material, lifetimes from low doping levels fall well below the predictions, implying that Shockley-Read-Hall (SRH) recombination is still dominant. MWIR samples have a lifetime that increases somewhat with carrier concentration, suggesting that In doping passivates the SRH defects for that composition. Lifetimes in p-type MWIR material appear to be well-explained by recent theoretical calculations. In p-type material, trapping states may be introduced during the incorporation and activation of As, since some samples with unusually long lifetimes had a distinctly different type of temperature dependence. [ABSTRACT FROM AUTHOR]

The first writings of curare appeared about 1500. Two hundred and fifty years later the first real experimentation took place with the drug and an additional two hundred years elapsed before the drug found its true place in medicine. During the past decade it has become a valuable drug in anesthesia. The muscle relaxants have been divided into two groups according to their action - the curare-like or competitive inhibition blocking group, and the C-10-like or depolarizing blocking group. They act at the myoneural junction to produce relaxation with very little effect on the remainder of the body. In recent years the synthetic curare-like drugs have overshadowed purified curare.