Marianne Gunell,1,2 Janne Haapanen,3 Kofi J Brobbey,4 Jarkko J Saarinen,4 Martti Toivakka,4 Jyrki M Mäkelä,3 Pentti Huovinen,1 Erkki Eerola1,2 1Department of Medical Microbiology and Immunology, University of Turku, 2Department of Clinical Microbiology and Immunology, Microbiology and Genetics Service Area, Turku University Hospital, Turku, 3Aerosol Physics Laboratory, Department of Physics, Tampere University of Technology, Tampere, 4Laboratory of Paper Coating and Converting, Center for Functional Materials, Åbo Akademi University, Turku, Finland Abstract: Bacterial infections, especially by antimicrobial resistant (AMR) bacteria, are an increasing problem worldwide. AMR is especially a problem with health care-associated infections due to bacteria in hospital environments being easily transferred from patient to patient and from patient to environment, and thus, solutions to prevent bacterial transmission are needed. Hand washing is an effective tool for preventing bacterial infections, but other approaches such as nanoparticle-coated surfaces are also needed. In the current study, direct and indirect liquid flame spray (LFS) method was used to produce silver nanoparticle-coated surfaces. The antimicrobial properties of these nanoparticle surfaces were evaluated with the “touch test” method against Escherichia coli and Staphylococcus aureus. It was shown in this study that in glass samples one silver nanoparticle-coating cycle can inhibit E. coli growth, whereas at least two coating cycles were needed to inhibit S. aureus growth. Silver nanoparticle-coated polyethylene (PE) and PE terephthalate samples did not inhibit bacterial growth as effectively as glass samples: three nanoparticle-coating cycles were needed to inhibit E. coli growth, and more than 30 coating cycles were needed until S. aureus growth was inhibited. To conclude, with the LFS method, it is possible to produce nanostructured large-area antibacterial surfaces which show antibacterial effect against clinically relevant pathogens. Results indicate that the use of silver nanoparticle surfaces in hospital environments could prevent health care-associated infections in vivo. Keywords: silver, nanoparticle, E. coli, S. aureus, LFS, HAI

Corona, flame, atmospheric plasma, and liquid flame spray (LFS) techniques were used to create highly hydrophilic surfaces for pigment-coated paper and board and machine-glossed paper. All the surface modification techniques were performed continuously in ambient atmosphere. The physical changes on the surfaces were characterized by field emission gun-scanning electron microscopy (FEG-SEM), atomic force microscopy and Parker Print-Surf surface roughness. The chemical changes were analysed by X-ray photoelectron spectroscopy. The superhydrophilic surfaces, i.e. contact angle of water (CAW) <10°, were created mainly by modifying the surface chemistry of the paper and board by argon plasma or SiO2coating. The nano- and microscale roughness existing on paper and board surfaces enabled the creation of the superhydrophilic surfaces. Furthermore, the benefits and limitations of the surface modification techniques are discussed and compared. For example, the SiO2coating maintained its extreme hydrophilicity for at least six months, whereas the CAW of argon plasma-treated surface increased to about 20° already in one day. [ABSTRACT FROM AUTHOR]

The target of this study is to investigate the correlation between surface properties and heat sealability of flame-treated low-density polyethylene (LDPE) coating because it is vital to know how to modify the surface properties of LDPE coating without losing the heat sealing properties. Flame treatment showed a significant effect on the heat sealing properties of LDPE-coated paper. For example, the heat sealing temperature of LDPE coating decreased or alternatively doubled, depending on the equivalence ratio (air-propane ratio) of flame treatment. In addition, the hot tack strength was significantly enhanced by flame treatment, which broadened the hot tack window of LDPE-coated paper. The reason for the heat sealing performance of flame-treated LDPE coating was believed to be related to the simultaneous reactions, that is, cross-linking and chain scission, occurring on the LDPE surface. The molecular weight of LDPE surface increased or decreased, depending on the dominating reaction during flame treatment. This affected the chain mobility and the amount of chain interdiffusion across the seal interface and finally defined the heat sealing performance of LDPE-coated paper. Copyright © 2012 John Wiley & Sons, Ltd. [ABSTRACT FROM AUTHOR]

Rheology of Microfibrillated Cellulose (MFC) suspensions is useful for designing equipment to transport, mix, or process them. Pressure-driven flow behavior is particularly important for MFC suspensions if they are to be pumped, extruded or coated. Herein, we report use of slot and pipe geometries for determination of MFC suspension rheology and compare the results to boundary-driven flows. MFC flow behavior in a slot with varying gaps was studied at mass concentrations of 1, 2, and 3% and up to shear rates of 100 000 s-1. The suspensions exhibited yield stress and were highly shear thinning (pseudo-plastic) with apparent power law indices of 0.22 - 0.43. The shear thinning behavior can be explained by a microstructural picture in which a non-yielding center plug is surrounded by a yielded layer and a fiber-depleted water rich boundary layer.

Abstract: The impact of water, linseed oil and mineral oil solvents on the viscoelastic properties of calcium carbonate-caboxylated styrene buradiene (CaCO3-SBR) porous coatings has been investigated using a dynamic mechanical thermal analysis (DMTA) technique in single cantilever mode from −30°C to 70°C. Water and oils reduce the glass transition temperature (Tan Delta peak) of pure latex. Oils increase the rubbery storage modulus which may be due to oxidation leading to entangled chains that contribute to resistance to deformation. Scanning electron microscopy (SEM) was used to visualise the porous structure of these composites. Further analysis using Image J software showed that increasing the latex content results in the development of small circular (2D) pores. The effect of solvents on the elastic response of coating depends on the chemical nature of the solvent and its molecular size. Linseed oil and water decreased the composite’s storage modulus for 5, 10 and 15pph coatings, in contrast to mineral oil which had a negative impact at relatively higher latex content (50pph). The drop in the strength and storage modulus of solvent saturated latex coatings is proportional to the solvent surface tension to viscosity ratio. The low values of storage modulus were interpreted as low adhesion between CaCO3 particles and the carboxylated styrene- butadiene matrix. For low latex content coatings, low storage modulus is due to porosity which forms suitable sites for cracks initiation and propagation through the coatings. At higher latex volume fraction coatings the composite behaviour approaches that of pure latex. [Copyright &y& Elsevier]

Abstract: The viscoelastic properties of carbonate-based coatings in ambient and water saturated conditions have been investigated using dynamic mechanical thermal analysis (DMTA). At low frequencies, viscous flow is suggested to be due to the reorientation of polymer chains at particle interfaces. At higher frequencies the composite storage modulus, as normalised to that of the latex, decreases due to the conjoint action of increased heat and decreased molecular chain mobility at the interfaces. Water is found to weaken interfacial pinning of the polymer molecules. Water is able to conduct heat away from the solid component of the microstructure more effectively than air, and reduces the effect of temperature on the softening of latex. Pore space allows greater microstructural mobility and consequently polymer chains at interfaces can orient more easily to the loading direction. The glass transition temperature, the normalised storage modulus and the normalised loss modulus were found to depend on both the latex fraction and on the porosity. This paper highlights and explains particular conditions that may arise during processing by which carbonate-based coatings soften. [Copyright &y& Elsevier]

Abstract: The effect of CaCO3 pigment surface modifications on the rheology, microstructure and the thermomechanical properties of porous particle–polymer composites are investigated. The incorporation of (random copolymerised) acrylamido-2-methyl-propane sulphonate (AMPS) and ethylene glycol methyl ether (mPEG) into poly(acrylic acid) dispersant reduced the dispersing efficiency. Similarly, the composite microstructure showed the concentration and size of particle aggregates were strongly dependant on the chemical nature of the dispersing agent. Dynamic mechanical thermal analysis (DMTA) showed that the incorporating of mPEG segments within the dispersant chain improves the dispersant-latex compatibility, which results in better adhesion as was confirmed through SEM imaging. The composite storage modulus of dry and water saturated samples showed a strong dependency on the properties of the latex. Composites made of high glass transition temperature (Tg), styrene acrylate (SA) latex exhibited high stiffness in dry samples. Contrarily, the cross-linking of the styrene butadiene latex (SBR) induced a low drop in stiffness under conditions of water saturation. [Copyright &y& Elsevier]

There is a growing interest in utilizing renewable biomass resources to manufacture environmentally friendly active food packaging, against the petroleum-based polymers. Cellulose nanofibers (CNFs) have received significant attention recently due to their sustainability, biodegradability, and widely available sources. CNFs are generally obtained through chemical or physical treatment, wherein the original surface chemistry and interfacial interactions can be changed if the functionalization process is applied. This review focuses on promising and sustainable methods of functionalization to broaden the potential uses of CNFs in active food packaging. Novel aspects, including functionalization before, during and after cellulose isolation, and functionalization during and after material processing are addressed. The CNF-involved structural construction including films, membranes, hydrogels, aerogels, foams, and microcapsules, is illustrated, which enables to explore the correlations between structure and performance in active food packaging. Additionally, the enhancement of CNFs on multiple properties of active food packaging are discussed, in which the interaction between active packaging systems and encapsulated food or the internal environment are highlighted. This review emphasizes novel approaches and emerging trends that have the potential to revolutionize the field, paving the way for advancements in the properties and applications of CNF-involved active food packaging., Competing Interests: Declaration of competing interest There are no conflicts to declare., (Copyright © 2024. Published by Elsevier B.V.)

Increasing evidence suggests mammalian Argonaute (Ago) proteins partition into distinct complexes within cells, but there is still little biochemical or functional understanding of the miRNAs differentially associated with these complexes. In naïve T cells, Ago2 is found almost exclusively in low molecular weight (LMW) complexes which are associated with miRNAs but not their target mRNAs. Upon T-cell activation, a proportion of these Ago2 complexes move into a newly formed high molecular weight (HMW) RNA-induced silencing complex (RISC), which is characterized by the presence of the GW182 protein that mediates translational repression. Here, we demonstrate distinct partitioning of miRNAs and isomiRs in LMW versus HMW RISCs upon antigen-mediated activation of CD8 + T cells. We identify miR-7 as highly enriched in HMW RISC and demonstrate that miR-7 inhibition leads to increased production of IL-2 and up-regulation of the IL-2 receptor, the transferrin receptor, CD71 and the amino acid transporter, CD98. Our data support a model where recruitment of miR-7 to HMW RISC restrains IL-2 signaling and the metabolic processes regulated by IL-2., (© 2024 Toivakka et al.; Published by Cold Spring Harbor Laboratory Press for the RNA Society.)

Fabricating bio-latex colloids with core-shell nanostructure is an effective method for obtaining films with enhanced mechanical characteristics. Nano-sized lignin is rising as a class of sustainable nanomaterials that can be incorporated into latex colloids. Fundamental knowledge of the correlation between surface chemistry of lignin nanoparticles (LNPs) and integration efficiency in latex colloids and from it thermally processed latex films are scarce. Here, an approach to integrate self-assembled nanospheres of allylated lignin as the surface-activated cores in a seeded free-radical emulsion copolymerization of butyl acrylate and methyl methacrylate is proposed. The interfacial-modulating function on allylated LNPs regulates the emulsion polymerization and it successfully produces a multi-energy dissipative latex film structure containing a lignin-dominated core (16% dry weight basis). At an optimized allyl-terminated surface functionality of 1.04 mmol g -1 , the LNPs-integrated latex film exhibits extremely high toughness value above 57.7 MJ m -3 . With multiple morphological and microstructural characterizations, the well-ordered packing of latex colloids under the nanoconfinement of LNPs in the latex films is revealed. It is concluded that the surface chemistry metrics of colloidal cores in terms of the abundance of polymerization-modulating anchors and their accessibility have a delicate control over the structural evolution of core-shell latex colloids., (© 2023 Wiley-VCH GmbH.)

To date, the energy-intensive production and high-water content severely limits nanocellulose applications on a large scale off-site. In this study, adding water-soluble polysaccharides (PS) to achieve an integrated process of water-redispersible nanocellulose production was well established. The addition of PS, in particular carboxymethylated-galactoglucomannan (cm-GGM), facilitates fibre fibrillation enabling homogenization at a higher solid content at 1.5 wt% compared with around 0.4 wt% for neat fibre. More importantly, the addition of cm-GGM saved 73 % energy in comparison without PS addition. Good water redispersibility of thus-prepared nanocellulose was validated in viewpoints of size distribution, morphology, viscosity and film properties as compared with neat nanocellulose. The tensile strength and optical transmittance of nanocellulose films increased to 116 MPa and 77 % compared to those without PS addition of 62 MPa and 74 %, respectively. Collectively, this study provides a new avenue for large-volume production of redispersible nanocellulose at a high solid content with less energy-consumption., Competing Interests: Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2022. Published by Elsevier Ltd.)

The leakage issue and inferior heat conduction of organic phase change materials (PCMs) limit their actual applications. In the present study, cellulose nanofibril (CNF)-based foams were prepared as the porous scaffolds for polyethylene glycol (PEG) and paraffin wax (Pw) to prevent their leakage, and multiwalled carbon nanotubes (CNTs) were incorporated to improve the heat transfer performance. The prepared foams had low density (<67.3 kg/m 3 ) and high porosity (>94.5 %). Selective chemical modifications of nanocellulose foams enhanced their shape-stability and compatibility with PCMs. The highly porous foam structure and favorable compatibility resulted in high PCM loading levels (93.63 % for PEG and 91.77 % for Pw) and negligible PCM leakage (<2 %). CNTs improved the heat transfer performance of PCMs, as evidenced by the improved thermal conductivities and boosted temperature rises during solar heating. Meanwhile, the composite PCMs exhibited improved thermal stability over the control. PEG-based composite PCM exhibited a phase change enthalpy of 143 kJ/kg with a melting temperature of 25.2 °C; Pw-based composite PCM exhibited a phase change enthalpy of 184 kJ/kg with a melting temperature of 53.4 °C. Novel PCM sandwich structures based on these composite PCMs and a thermoelectric generator were designed and displayed promising potential for solar energy harvesting and utilization., Competing Interests: Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper., (Copyright © 2022 Elsevier B.V. All rights reserved.)

This is the first time to report a facile strategy to fabricate galactoglucomannan-based latex with highly transparent, hydrophobic and flexible characteristics by combining etherification with subsequent emulsion polymerization. The allylated galactoglucomannans (A-GGM) and galactoglucomannan-based latexes (GGM-L) were prepared and their chemical structure, substitution degree, molecular weight, conversion rate, particle size and zeta potential were characterized by ATR-FTIR, 1 HNMR, quantitative 13 CNMR, HP-SEC, HPLC and zeta-sizer nanometer analyzer, respectively. Furthermore, the effects of substitution degree on film surface roughness and homogeneity, water vapor permeability (WVP) and thermal stability were evaluated by AFM, SEM, WVP and TGA, respectively. The optimal GGM-L film exhibited 91.3% transmittance and 0.43% haze, 117° water contact angle, 31.2% elongation at break and 30.9 MPa ultimate tensile stress. The bio-based content of the GGM-L may reach about 99 wt%, which provides a promising avenue for polyolefin-based latex replacement for paper and paperboard applications., (Copyright © 2022 The Authors. Published by Elsevier Ltd.. All rights reserved.)

Mineral coatings manipulate surface properties such as roughness, porosity, wettability and surface energy. Properties that are known to determine cell behaviour. Therefore, mineral coatings can potentially be used to manipulate cell fate. This paper studies mineral-cell interactions through coatings in a stacked cell culture platform. Minerals were chosen according to their influence on Human Dermal Fibroblasts (HDFs): calcium carbonate, calcium sulphates, and kaolin. Mineral coatings were formulated with the additives latex, sorbitol, polyvinyl alcohol (PVOH) and TEMPO-oxidised cellulose nanofibrils (CNF-T). The coatings were placed as a bottom or top of the device, for a direct or indirect interaction with HDFs, respectively. Cells were seeded, in various densities, to the bottom of the device; and cell density and confluency were monitored in time. Overall, results show that the coating interaction is influenced at first by the cell seeding density. Scarce cell seeding density limits adaptability to the new environment, while an abundant one encourages confluency in time. In between those densities, coating formulation plays the next major role. Calcium carbonate promoted HDFs growth the most as expected, but the response to the rest of minerals depended on the coating additive. CNF-T encouraged proliferation even for kaolin, a mineral with long-term toxicity to HDFs, while PVOH induced a detrimental effect on HDF growth regardless of the mineral. At last, the placement of the coated layer provided insights on the contact-dependency of each response. This study highlights the importance of the experimental design, including coating formulation, when investigating cellular response to biomaterials., (Copyright © 2021 The Authors. Published by Elsevier B.V. All rights reserved.)

The leakage and low thermal conductivity of paraffin phase change material (PCM) must be addressed to achieve a more efficient energy storage process. In this study, cellulose nanofibril (CNF) foams were prepared as the porous support of paraffin to prevent its leakage, and multiwalled carbon nanotubes (CNTs) were incorporated in the foams to improve heat transfer performance. Treatment of CNF with methyltrimethoxysilane improved compatibility between the foams and paraffin. The prepared highly porous (porosity >96%) foams had paraffin absorption capacities exceeding 90%. The form-stable PCM composites displayed negligible paraffin leakage and had a compact structure. The prepared PCM composites had enhanced heat transfer performance, reasonable phase change properties and thermal stabilities. The enthalpy of the SCNF/CNT 50 -Pw PCM composite decreased by 6% after 100 melting/freezing cycles. Compared with pristine paraffin, the PCM composites exhibited superior form-stabilities and improved thermal properties, which suggested application in a solar-thermal-electricity energy harvesting and conversion system., (Copyright © 2021. Published by Elsevier Ltd.)

Salt hydrate phase change materials (PCMs) possess the challenge of supercooling, which must be addressed to allow more efficient energy storage and utilisation. In this work, cellulose nanofibril (CNF), a versatile biopolymer was used to support and disperse silver nanoparticles (AgNPs), and the synthesised CNF/AgNPs composite was used to improve the performance of sodium acetate trihydrate (SAT). Results showed that CNF dispersed the AgNPs uniformly and prevented their aggregation. Through the synergistic effect of 1% CNF/AgNPs and 2% sodium phosphate dibasic dodecahydrate, a low supercooling degree of 1.2 °C was achieved. Moreover, AgNPs were uniformly distributed in the prepared PCM composite. Differential scanning calorimetry results indicated that the prepared PCM@CNF/AgNPs 0.02 composite showed a similar melting point (57.4 °C) and enthalpy (269 kJ/kg), compared to those of pure SAT. Thermogravimetric analysis showed that the PCM composite did not lose all moisture until a heating temperature of 160 °C, showing improved thermal stability. The thermal conductivity of PCM@CNF/AgNPs 0.02 composite was 31.6% higher than that of SAT. The enthalpy of this composite decreased only around 2% after 100 melting/freezing cycles, showing satisfying thermal reliability. This composite can therefore be used to fabricate high-performance TES systems with negligible supercooling and improved thermal properties., Competing Interests: Declaration of competing interest There are no conflicts to declare., (Copyright © 2021. Published by Elsevier B.V.)

Poly(3,4-ethylenedioxythiophene) doped with the polymer anion poly(styrenesulfonate), PEDOT:PSS, is a common electrochromic material used in the preparation of electrochromic devices (ECDs). In this paper, the PEDOT:PSS doped with a solvent was used both as the electrode and the electrochromic functional layer for fabrication of ECDs on absorptive paper surfaces. The doped PEDOT:PSS dispersion was assessed for the film-forming evenness, sheet resistance and conductivity, and the performance of prepared ECDs for their color contrast and switching dynamics. The ECD performance is discussed in relation to the absorptive characteristics of the substrates. The results indicate that it is feasible to prepare ECDs onto absorptive substrates, despite the partial polymer material imbibition into them. The extent of polymer absorption influences the ECD performance: an increased absorption reduces the color contrast but speeds up the color switching. The electrochemical properties of the used solid electrolyte were found to be crucial for functioning of the ECDs. Insufficient ion transport and associated high resistance led to failure of the devices.

Biodegradable and renewable materials, such as cellulose nanomaterials, have been studied as a replacement material for traditional plastics in the biomedical field. Furthermore, in chronic wound care, modern wound dressings, hydrogels, and active synthetic extracellular matrices promoting tissue regeneration are developed to guide cell growth and differentiation. Cells are guided not only by chemical cues but also through their interaction with the surrounding substrate and its physicochemical properties. Hence, the current work investigated plant-based cellulose nanomaterials and their surface characteristic effects on human dermal fibroblast (HDF) behavior. Four thin cellulose nanomaterial-based coatings produced from microfibrillar cellulose (MFC), cellulose nanocrystals (CNC), and two TEMPO-oxidized cellulose nanofibers (CNF) with different total surface charge were characterized, and HDF viability and adhesion were evaluated. The highest viability and most stable adhesion were on the anionic CNF coating with a surface charge of 1.14 mmol/g. On MFC and CNC coated surfaces, HDFs sedimented but were unable to anchor to the substrate, leading to low viability.

Due to the high electric conductivity and large surface area of nanographites, such as graphene and graphite nanoplatlets, these materials have gained a large interest for use in energy storage devices. However, due to the thin flake geometry, the viscosity of aqueous suspensions containing these materials is high even at low solids contents. This together with the use of high viscosity bio-based binders makes it challenging to coat in a roll-to-roll process with sufficient coating thickness. Electrode materials for commercial energy storage devices are often suspended by organic solvents at high solids contents and coated onto metal foils used as current-collectors. Another interesting approach is to coat the electrode onto the separator, to enable large-scale production of flat cell stacks. Here, we demonstrate an alternative, water-based approach that utilize slot-die coating to coat aqueous nanographite suspension with nanocellulose binder onto the paper separator, and onto the current collector as reference, in aqueous metal-free supercapacitors. The results show that the difference in device equivalent series resistance (ESR) due to interfacial resistance between electrode and current collector was much lower than expected and thus similar or lower compared to other studies with a aqueous supercapacitors. This indicates that electrode coated paper separator substrates could be a promising approach and a possible route for manufacturing of low-cost, environmentally friendly and metal-free energy storage devices.

Stencil printing is a commonly used printing method, but it has not previously been used for production of pharmaceuticals. The aim of this study was to explore whether stencil printing of drug containing polymer inks could be used to manufacture flexible dosage forms with acceptable mass and content uniformity. Formulation development was supported by physicochemical characterization of the inks and final dosage forms. The printing of haloperidol (HAL) discs was performed using a prototype stencil printer. Ink development comprised of investigations of ink rheology in combination with printability assessment. The results show that stencil printing can be used to manufacture HAL doses in the therapeutic treatment range for 6-17 year-old children. The therapeutic HAL dose was achieved for the discs consisting of 16% of hydroxypropyl methylcellulose (HPMC) and 1% of lactic acid (LA). The formulation pH remained above pH 4 and the results imply that the drug was amorphous. Linear dose escalation was achieved by an increase in aperture area of the print pattern, while keeping the stencil thickness fixed. Disintegration times of the orodispersible discs printed with 250 and 500 µm thick stencils were below 30 s. In conclusion, stencil printing shows potential as a manufacturing method of pharmaceuticals., Competing Interests: The authors declare no conflict of interest.