We have developed a photoemission-assisted plasma-enhanced chemical vapor deposition (CVD) process, where DC discharge plasma is assisted by photoelectrons emitted from the substrate under ultraviolet (UV) light irradiation. Under Ar gas atmosphere and in vacuum, plasma current was measured as a function of sample bias voltage to clarify the mechanism, by which photoemission-assisted plasma is generated. Owing to the advantages of the photoemission-assisted plasma-enhanced CVD, where the plasma is generated close to the substrate and in a controllable volume, we have succeeded in growing shiny black films of networked nanographite, without any catalyst, on Si(001) and SiO2(350 nm)/Si(001) substrates at a deposition rate of ∼2 μm/min despite of low electric power consumption of plasma, ∼4 W. Cross-sectional transmission electron microscopy (TEM) and diffraction (TED) observations revealed that samples grown at ∼700°C with Ar-diluted CH4 were composed of multilayer graphene particles (diameter of ∼10 nm) that were closely connected to each other and shared some graphene sheets between them, although their crystallographic configurations were randomly oriented. In bulk-sensitive C 1s photoelectron spectra using synchrotron radiation at 7933 eV, a chemically-shifted component of sp2-bonded carbon atom was dominant and the π—π* transition loss peak was clearly observed for the samples grown on both substrates, indicating that the multilayer graphene particles substantially contain high-quality graphene sheets in agreement with evaluations by microscopic Raman spectroscopy. We named the layered carbon structure “carbon mille-feuille.” [DOI: 10.1380/ejssnt.2009.882]

We have developed networked-nanographite (NNG) wires as the first step for multilayer graphene interconnects. Photoemission-assisted Plasma-enhanced CVD has been proposed as a growth method on dielectrics without catalysts. The activation energy of carrier conduction for NNG wire was almost the same as that of multilayer graphene exfoliated from highly oriented pyrolytic graphite (HOPG). This means that NNG consists of domains of multilayer graphene. Although we need to improve growth conditions, NNG is one of the candidates for future interconnect materials.