Search

The CO2 methanation mechanism over the highly active (TOF=75.1 h−1), selective (>92%) and stable 10% LaNiO3/CeO2-derived catalyst is still unresolved. The surface of the catalyst is monitored under hydrogenation (H2), oxidizing (CO2) and CO2 methanation (H2 +CO2) conditions by near ambient pressure X-ray photoelectron spectroscopy (NAP-XPS) using synchrotron radiation. Meanwhile, the main reaction intermediates are identified by in situ FTIR analysis. NAP-XPS experiments confirm that LaNiO3 perovskite reduction leads to the ex-solution of Ni0 nanoparticles and Ni2+single bondCeO2−x and Ni2+single bondLa2O3 interfaces conformation, favouring the CO2 adsorption and the H2 dissociation/transfer. In situ FTIR experiments combined with the C1s spectra (NAP-XPS) suggest that the CO2 activation occurs on CeO2−x (oxygen vacancies and OH–) at low temperatures, in the form of bicarbonates; whereas, mono-/bidentate carbonates are formed on different strength La2O3 sites at increasing temperatures. These species are consecutively reduced to formates, as the main reaction intermediate, and methane by the H spilled from Ni0 nanoparticles near to NiOsingle bondCeO2−x and NiOsingle bondLa2O3 interfaces.

Ni/CeO2 catalysts are very active and selective for total hydrogenation of CO2 to methane, but the nature of the active sites is still unclear. The surface of a Ni/CeO2 catalyst has been monitored under CO2 methanation conditions by Near Ambient Pressure-XPS (NAP-XPS) using synchrotron radiation, and has been concluded that the species involved in the redox processes taking place during the CO2 methanation mechanism are the Ni2+-CeO2/Ni0 and Ce4+/Ce3+ pairs. In addition, a small fraction of nickel is present on the catalyst surface forming NiO and Ni2+-carbonates/hydroxyls (around 20% of the total surface nickel), but these species do not participate in the redox processes of the methanation mechanism. Under CO2 methanation conditions the H2 reduction rate of the Ni2+-CeO2/Ni0 and Ce4+/Ce3+ couples is much faster than their CO2 reoxidation rate (2 times faster, at least, at 300ºC), but a certain proportion of nickel always remains oxidized under reaction conditions. The high activity of Ni/CeO2 catalysts for CO2 methanation is tentatively attributed to the simultaneous presence of Ni2+-CeO2 and Ni0 active sites where CO2 and H2 are expected to be efficiently dissociated, respectively.

Hydrogen permeable electrodes can be utilized for electrolytic ammonia synthesis from dinitrogen, water, and renewable electricity under ambient conditions, providing a promising route toward sustainable ammonia. The understanding of the interactions of adsorbing N and permeating H at the catalytic interface is a critical step toward the optimization of this NH3 synthesis process. In this study, we conducted a unique in situ near ambient pressure X-ray photoelectron spectroscopy experiment to investigate the solid-gas interface of a Ni hydrogen permeable electrode under conditions relevant for ammonia synthesis. Here, we show that the formation of a Ni oxide surface layer blocks the chemisorption of gaseous dinitrogen. However, the Ni 2p and O 1s XPS spectra reveal that electrochemically driven permeating atomic hydrogen effectively reduces the Ni surface at ambient temperature, while H2 does not. Nitrogen gas chemisorbs on the generated metallic sites, followed by hydrogenation via permeating H, as adsorbed N and NH3 are found on the Ni surface. Our findings suggest that the first hydrogenation step to NH and the NH3 desorption might be limiting under the operating conditions. The study was then extended to Fe and Ru surfaces. The formation of surface oxide and nitride species on iron blocks the H permeation and prevents the reaction to advance; while on ruthenium, the stronger Ru-N bond might favor the recombination of permeating hydrogen to H2 over the hydrogenation of adsorbed nitrogen. This work provides insightful results to aid the rational design of efficient electrolytic NH3 synthesis processes based on but not limited to hydrogen permeable electrodes., ChemE/Materials for Energy Conversion and Storage, Large Scale Energy Storage

The optimization of the catalysts incorporated to the electrodes for anion exchange membrane water electrolysers is a key issue to maximize their performance through the improvement of the oxygen evolution reaction (OER) yield. In this work, we show that the modification of the microstructure and the chemical properties of a mixed copper-cobalt oxide anode may contribute to increase the activity of this reaction. For this purpose, the OER has been systematically studied, either in a half cell or in a membrane electrode assembly configuration, as a function of the load and agglomeration degree of the catalysts used as electrodes, as prepared on a carbon paper support by magnetron sputtering deposition in an oblique angle configuration. Chemical analysis by X-ray absorption spectroscopy and electrochemical analysis by cyclic voltammetry and impedance spectroscopy have shown that cobalt-copper mixed oxide catalysts with a 1.8 Co/Cu atomic ratio and about one micron equivalent thickness maximizes the cell performance. The chemical, structural and microstructural factors controlling the final behaviour of these anodes and accounting for this maximization of the reaction yield are discussed on the basis of these characterization results and as a function of preparation variables of the electrodes and operating conditions of the cell.

[EN] Solar fuels production is a cornerstone in the development of emerging sustainable energy conversion and storage technologies. Light-induced H2 production from water represents one of the most crucial challenges to produce renewable fuel. Metalorganic frameworks (MOFs) are being investigated in this process, due to the ability to assemble new structures with the use of suitable photoactive building blocks. However, the identification of the reaction intermediates remains elusive, having negative impacts in the design of more efficient materials. Here, we report the synthesis and characterization of a new MOF prepared with the use of bismuth and dithieno[3,2-b:2',3'-d]thiophene-2,6-dicarboxylic acid (DTTDC), an electron-rich linker with hole transport ability. By combining theoretical studies and time-resolved spectroscopies, such as core hole clock and laser flash photolysis measurements, we have completed a comprehensive study at different time scales (fs to-ms) to determine the effect of competitive reactions on the overall H2 production. We detect the formation of an intermediate radical anion upon reaction of photogenerated holes withan electron donor, which plays a key role in the photoelectrocatalytic processes. These results shed new light on the use of MOFs for solar fuel production.

A new operation mode of a HPXPS (high-pressure X-ray photoelectron spectroscopy) analyzer is evaluated on a HPXPS system fitted with an Al K alpha X-ray source. A variety of metal foil samples (gold, silver and copper) were measured in different sample gas environments (N-2 and H2O), and a front aperture diameter of 0.8 mm. The new design concept is based upon "swiftly" accelerating the photoelectrons to kinetic energies of several keV after they pass the analyzer front aperture. Compared to the standard mode, in which the front section between the two first apertures is field-free, this gives a wider angular collection and a lower tendency for electron losses in collisions with gas molecules within the analyzer. With the swift-acceleration mode we attain, depending on the experimental conditions, up to about 3 times higher peak intensities in vacuum and about 10 to 20 times higher peak intensities in the 6-9 mbar regime, depending on kinetic energy. These experimental findings agree well with simulated transmission functions for the analyzer. The new mode of operation enables faster data acquisition than the standard mode of operation, particularly valuable in a home laboratory environment. Further demonstrations of performance are highlighted by measurements of the valence band structure in dye sensitized solar cell photoelectrodes under a 2 mbar H2O atmosphere, a molecularly modified surface of interest in photoelectrochemical devices.

In a high-pressure photoelectron spectrometer, the sample is positioned close to a differential pumping aperture, behind which the pressure is several orders of magnitude lower than the pressure in the analysis chamber. To find the optimal sample position, where the path length of the photoelectrons through the high pressure region is minimized as far as possible without compromising knowledge of the actual pressure at the sample surface, an understanding of the pressure variations near the sample and the aperture is required. A computational fluid dynamics study has been carried out to examine the pressure profiles, and the results are compared against experimental spectra whose intensities are analyzed using the Beer-Lambert law. The resultant pressure profiles are broadly similar to the one previously derived from a simplistic molecular flow model, but indicate that as the pressure in the analysis chamber is raised, the region over which the pressure drop occurs becomes progressively narrower.