Search

Ambient-Pressure X-ray Photoelectron Spectroscopy (AP-XPS) and Infrared Reflection Absorption Spectroscopy (AP-IRRAS) have been used to elucidate the active sites and mechanistic steps associated with the ethanol steam reforming reaction (ESR) over Ni-CeO2(111) model catalysts. Our results reveal that surface layers of the ceria substrate are both highly reduced and hydroxylated under reaction conditions while the small supported Ni nanoparticles are present as Ni(0)/NixC. A multifunctional, synergistic role is highlighted in which Ni, CeOx and the interface provide an ensemble effect in the active chemistry that leads to H2. Ni(0) is the active phase leading to both C-C and C-H bond cleavage in ethanol and it is also responsible for carbon accumulation. On the other hand, CeOx is important for the deprotonation of ethanol/water to ethoxy and OH intermediates. The active state of CeOx is a Ce(3+)(OH)x compound that results from extensive reduction by ethanol and the efficient dissociation of water. Additionally, we gain an important insight into the stability and selectivity of the catalyst by its effective water dissociation, where the accumulation of surface carbon can be mitigated by the increased presence of surface OH groups. The co-existence and cooperative interplay of Ni(0) and Ce(3+)(OH)x through a metal-support interaction facilitate oxygen transfer, activation of ethanol/water as well as the removal of coke.

Ambient-Pressure X-ray Photoelectron Spectroscopy (AP-XPS) and Infrared Reflection Absorption Spectroscopy (AP-IRRAS) have been used to elucidate the active sites and mechanistic steps associated with the ethanol steam reforming reaction (ESR) over Ni-CeO2(111) model catalysts. Our results reveal that surface layers of the ceria substrate are both highly reduced and hydroxylated under reaction conditions while the small supported Ni nanoparticles are present as Ni(0)/NixC. A multifunctional, synergistic role is highlighted in which Ni, CeOx and the interface provide an ensemble effect in the active chemistry that leads to H2. Ni(0) is the active phase leading to both C-C and C-H bond cleavage in ethanol and it is also responsible for carbon accumulation. On the other hand, CeOx is important for the deprotonation of ethanol/water to ethoxy and OH intermediates. The active state of CeOx is a Ce(3+)(OH)x compound that results from extensive reduction by ethanol and the efficient dissociation of water. Additionally, we gain an important insight into the stability and selectivity of the catalyst by its effective water dissociation, where the accumulation of surface carbon can be mitigated by the increased presence of surface OH groups. The co-existence and cooperative interplay of Ni(0) and Ce(3+)(OH)x through a metal-support interaction facilitate oxygen transfer, activation of ethanol/water as well as the removal of coke.

Ceria-supported Ni has shown unique catalytic activity due to unique properties of small Ni particles and strong metal-support interaction. Identification of adsorption sites and understanding the chemical interaction over Ni-ceria at the fundamental level provide crucial insights into the reaction pathways of complex catalytic processes. In this study, to probe the surface sites, the adsorption of CO was carried out with model Ni/ceria systems consisting of Ni nanoparticles vapor-deposited on well-ordered CeOx(111) (1.5 < x < 2) thin films using infrared reflection absorption spectroscopy (IRRAS) and temperature-programmed desorption (TPD) under ultrahigh vacuum (UHV) conditions. Fully oxidized CeO2(111) (Ce4+) and partially reduced CeO1.75(111) (Ce4+/Ce3+) thin films were grown on Ru(0001) to examine the role of the ceria support. Ni with low coverages (e.g., 0.2 ML) grows forming small two-dimensional particles on ceria at 300 K, which develop into three-dimensional clusters after heating to 700 K. In the absence of Ni, CO adsorption at 1 mTorr at 100 K shows distinct IR bands at 2158 cm−1 on CeO2 and 2165 cm−1 on CeO1.75. Bridging and atop IR bands associated with CO adsorption over metallic Ni were observed on the Ni-CeO1.75 surface at 300 K under UHV conditions. CO adsorption over Ni0 was also observed over as-deposited Ni on CeO2. However, a new IR band at 2146 cm−1 due to CO adsorption over Ni2+ species was detected at 100 K over the annealed Ni particles on CeO2. CO IRRAS data suggest the oxidation of Ni to Ni2+ on CeO2 and the formation of predominant Ni2+ species with heating, which is further confirmed with CO TPD data and previous x-ray photoelectron spectroscopy results. [ABSTRACT FROM AUTHOR]

Ambient-Pressure X-ray Photoelectron Spectroscopy (AP-XPS) and Infrared Reflection Absorption Spectroscopy (AP-IRRAS) have been used to elucidate the active sites and mechanistic steps associated with the ethanol steam reforming reaction (ESR) over Ni–CeO2(111) model catalysts. Our results reveal that surface layers of the ceria substrate are both highly reduced and hydroxylated under reaction conditions while the small supported Ni nanoparticles are present as Ni0/NixC. A multifunctional, synergistic role is highlighted in which Ni, CeOx and the interface provide an ensemble effect in the active chemistry that leads to H2. Ni0 is the active phase leading to both C–C and C–H bond cleavage in ethanol and it is also responsible for carbon accumulation. On the other hand, CeOx is important for the deprotonation of ethanol/water to ethoxy and OH intermediates. The active state of CeOx is a Ce3+(OH)x compound that results from extensive reduction by ethanol and the efficient dissociation of water. Additionally, we gain an important insight into the stability and selectivity of the catalyst by its effective water dissociation, where the accumulation of surface carbon can be mitigated by the increased presence of surface OH groups. The co-existence and cooperative interplay of Ni0 and Ce3+(OH)x through a metal–support interaction facilitate oxygen transfer, activation of ethanol/water as well as the removal of coke. [ABSTRACT FROM AUTHOR]