Search

Recent developments in biomimetic hydrogel research have expanded the scope of biomedical technologies that can be used to model, diagnose, and treat a wide range of medical conditions. Cancer presents one of the most intractable challenges in this arena due to the surreptitious mechanisms that it employs to evade detection and treatment. In order to address these challenges, biomimetic design principles can be adapted to beat cancer at its own game. Biomimetic design strategies are inspired by natural biological systems and offer promising opportunities for developing life-changing methods to model, detect, diagnose, treat, and cure various types of static and metastatic cancers. In particular, focusing on the cellular and subcellular phenomena that serve as fundamental drivers for the peculiar behavioral traits of cancer can provide rich insights into eradicating cancer in all of its manifestations. This review highlights promising developments in biomimetic nanocomposite hydrogels that contribute to cancer therapies via enhanced drug delivery strategies and modeling cancer mechanobiology phenomena in relation to metastasis and synergistic sensing systems. Creative efforts to amplify biomimetic design research to advance the development of more effective cancer therapies will be discussed in alignment with international collaborative goals to cure cancer., Competing Interests: The authors declare no conflicts of interest.

Magnetic nanoparticles (MNPs) self-align and transduce magnetic force, two properties which lead to promising applications in cell and tissue engineering. However, the toxicity of MNPs to cells which uptake them is a major impediment to applications in engineered tissue constructs. To address this problem, MNPs were embedded in millimeter-scale alginate beads, coated with glutaraldehyde cross-linked chitosan, and loaded in acellular and MDA-MB-231 cancer cell-seeded collagen hydrogels, providing local micro-actuation under an external magnetic field. Brightfield microscopy was used to assess nanoparticle diffusion from the bead. Phase contrast microscopy and digital image correlation were used to track collagen matrix displacement and estimate intratissue strain under magnetic actuation. Coating the magnetic alginate beads with glutaraldehyde-chitosan prevents bulk diffusion of nanoparticles into the surrounding microenvironment. Further, the beads exert force on the surrounding collagen gel and cells, resulting in intratissue strains of 0-10% tunable with bead dimensions, collagen density, and distance from the bead. Cells seeded adjacent to the embedded beads are subjected to strain gradients without loss of cell viability over two days culture. This study describes a simple way to fabricate crosslinked magnetic alginate beads to load in a collagen tissue construct without direct exposure of the construct to nanoparticles. The findings are significant to in vitro studies of mechanobiology in enabling precise control over dynamic mechanical loading of tissue constructs., (Copyright © 2017 Elsevier B.V. All rights reserved.)

The chemical and physical characteristics of nanocrystalline hydroxyapatite particles which formed during the subcutaneous implantation of crab shell in Sprague-Dawley rats were studied using selected area electron diffraction (SAED) and high resolution transmission electron microscopy (HRTEM). The initial SAED characterization evidence indicated the presence of an amorphous calcium phosphate phase. The electron dense nanophase particles which formed in the wound healing zone displayed broad diffuse rings which usually indicate a low crystalline order or amorphous phase. High resolution transmission electron microscopy (HRTEM) revealed that these mineralized regions contained discrete single crystal particles less than 5nm in size. Micrographs taken at successively higher magnifications revealed very small nanoparticles with a hexagonal arrangement of ion channels with characteristic spacing of 0.54nm and 0.23nm. This study revealed that single crystal hydroxyapatite nanoparticles consisting of only a few unit cells formed via a biomineralization directed process., (Copyright © 2015 Elsevier B.V. All rights reserved.)

Results from the study of a novel, high modulus nanopowder filled resin composite are presented. This composite is developed to serve (1) as a high stiffness support to all-ceramic crowns and (2) as a means of joining independently fabricated crown core and veneer layers. Nanosized Al(2)O(3) (average particle size 47 nm) reinforcement provides stiffness across joins. Two systems are examined: Al(2)O(3) with 50:50 bis-GMA:TEGDMA monomers (ALBT) and Al(2)O(3) with pure TEGDMA (ALT). To obtain higher filler levels, surfactant is used to aid mixing and increase maximum weight percent of nanopowder filler from 72 to 80. The loading level of Al(2)O(3) has significant effects on composite properties. The elastic modulus for cured ALBT systems increases from 4.6 GPa (0 wt % filler) to 29.2 GPa (80 wt % filler). The elastic modulus for cured ALT systems increases from 3.0 GPa (0 wt % filler) to 22.9 GPa (80 wt % filler). Similarly, ALBT hardness increases from 200 MPa (0% filler) to 949 MPa (80 wt % filler), and ALT hardness increases from 93 MPa (0% filler) to 760 MPa (80 wt % filler). Our results indicate that with a generally monodispersed nanosized high modulus filler relatively high elastic modulus resin based composite cements are possible.

Objective: The goal of this program was to identify promising environments that could efficiently minimize machining-induced damage of dental materials., Methods: Single point abrasion (SPA) scratch testing was used on five materials to determine the scratch hardness and amount of edge chipping as functions of chemical environment, including air, water, saline and glycerol solutions. Limited testing was also done under additional environments expected to promote chemomachining effects via crack growth promotion or debris removal. A conical diamond indenter and a conventional tungsten carbide machining tool were used in the scratch tests. One-way ANOVA analysis was used to determine statistical differences among the variables., Results: There was a consistent trend across materials that the water and saline yielded the lowest values of scratch hardness, air the next lowest, and the tests performed in glycerol yielded the highest hardness values. The measured hardness values using the conical diamond tool in the glycerol environments were about twice the hardness values measured under water and saline solutions. Environmental effects on chipping were minimal, but a linear relationship between load and per cent chipping was determined for the WC tool within the 10-50 N test range. The choice of scratch tool strongly affected scratch hardness and chipping tendency., Significance: The chemical environment had an effect on machining characteristics, but the effects were more dependent on tool interactions rather than material specific properties. As a result, it may not be possible to utilize a particular single environment to substantially improve the damage response of dental materials to machining operations. Improvements in damage resistance can be environmentally obtained, but only for shallow cuts (finishing operations).

The influence of esterification reactions on the surface chemistry and colloid stability of hydroxyapatite (HAP) was studied by aging nanophase HAP in dodecyl alcohol at elevated temperatures (115 degrees C and 190 degrees C). The esterified HAP particles were characterized by X-ray diffraction, transmission electron microscopy, diffuse reflectance infra-red Fourier transform spectroscopy (DRIFTS), thermal gravimetric analysis, sedimentation time studies, and electrophoretic mobility (mu) measurements in water and ethyl alcohol. DRIFTS analysis revealed that the HAP surface was modified by dodecyl groups based on the appearance of C-H stretch vibrational modes at 2962, 2930, and 2860cm(-1). Dodecyl alcohol modified HAP exhibited a larger TGA mass loss upon heating (up to 4.8%) compared to untreated HAP (2.5-3.2wt%). Sedimentation studies revealed the following stability trends: HAP dispersed in water was approximately the same as esterified HAP in water (a few hours)