Search

To address the issues of insufficient strength and poor precision in polystyrene forming parts during the selective laser sintering process, a ternary composite of polystyrene/glass fiber/hollow glass microbeads was prepared through co-modification by incorporating glass fiber and hollow glass microbeads into polystyrene using a mechanical mixing method. The bending strength and dimensional accuracy of the sintered composites were investigated by conducting an orthogonal test and analysis of variance to study the effects of laser power, scanning speed, scanning spacing, and delamination thickness. The process parameters were optimized and selected to determine the optimal combination. The results demonstrated that when considering bending strength and Z-dimensional accuracy as evaluation criteria for terpolymer sintered parts, the optimum process parameters are as follows: laser power of 24 W, scanning speed of 1600 mm/s, scanning spacing of 0.24 mm, and delamination thickness of 0.22 mm. Under these optimal process parameters, the bending strength of sintered parts reaches 6.12 MPa with a relative error in the Z-dimension of only 0.87%. The bending strength of pure polystyrene sintered parts is enhanced by 15.69% under the same conditions, while the relative error in the Z-dimension is reduced by 63.45%. It improves the forming strength and precision of polystyrene in the selective laser sintering process and achieves the effect of enhancement and modification, which provides a reference and a new direction for exploring polystyrene-based high-performance composites and expands the application scope of selective laser sintering technology. [ABSTRACT FROM AUTHOR]

Mercury (Hg 2+ ) contamination in water is associated with potential toxicity to human health and ecosystems. Many research studies have been ongoing to develop new materials for the remediation of Hg 2+ pollution in water. In this study, a novel thiol- and amino-containing fibrous adsorbent was prepared by grafting 2-amino-5-mercapto-1,3,4-thiadiazol (AMTD) onto PAN fiber through a microwave-assisted method. The synthesized functional fiber was characterized by FTIR, SEM, and elemental analysis. Adsorption tests depicted that for mercury uptake, PAN MW -AMTD fiber exhibited enhanced adsorption capacity compared with other fibrous adsorbents and selective adsorption feature under the interference of other metal ions, including Pb 2+ , Cu 2+ , Cd 2+ , and Zn 2+ . The influence of pH on the adsorption process was investigated and the effect of temperature revealed that the adsorption sorption process was endothermic and the adsorption performance of PAN MW -AMTD was elevated with the increase of temperature. Kinetic studies of PAN MW -AMTD fiber followed the pseudo-second-order and the adsorption isotherm of Hg 2+ was well fitted by Sips and Langmuir equations, given the maximum adsorption amount of 332.9 mg/g. XPS results suggested that a synergetic coordination effect of sulfur and nitrogen in functional fiber with mercury took responsibility for the adsorption mechanism in the uptake process. In addition, the prepared PAN MW -AMTD fiber could easily be regenerated with 0.1 M HCl for five times without significant reduction of mercury removal efficiency. Thus, this study will facilitate the research on novel functional material for the removal of mercury from water., (Copyright © 2021 Elsevier Ltd. All rights reserved.)