Photoelectrochemical (PEC) water splitting provides a pathway to generate sustainable clean fuels using the two most abundant resources on Earth: sunlight and water. Currently, most of the successful models of PEC cells are still fabricated on small scales near 1 cm2, which largely limits the mass deployment of solar-fuel production. Here, the scale-up to 8 cm2 of an integrated PEC (IPEC) device is demonstrated and its performance compared to a 1 cm2 IPEC cell, using state-of-the-art iridium and platinum catalysts with III–V photoabsorbers. The initial photocurrents at 1 sun are 8 and 7 mA cm−2 with degradation rates of 0.60 and 0.47 mA cm−2 day−1, during unbiased operation for the 1 and 8 cm2 devices, respectively. Evaluating under outdoor and indoor conditions at two U.S. National Laboratories reveals similar results, evidencing the reproducibility of this design's performance. Furthermore, the emerging degradation mechanisms during scale-up are investigated and the knowledge gained from this work will provide feedback to the broader community, since PEC device durability is a limiting factor in its potential future deployment.

The rapidly increasing solar conversion efficiency (PCE) of hybrid organic–inorganic perovskite (HOIP) thin‐film semiconductors has triggered interest in their use for direct solar‐driven water splitting to produce hydrogen. However, application of these low‐cost, electronic‐structure‐tunable HOIP tandem photoabsorbers has been hindered by the instability of the photovoltaic‐catalyst‐electrolyte (PV+E) interfaces. Here, photolytic water splitting is demonstrated using an integrated configuration consisting of an HOIP/n+silicon single junction photoabsorber and a platinum (Pt) thin film catalyst. An extended electrochemical (EC) lifetime in alkaline media is achieved using titanium nitride on both sides of the Si support to eliminate formation of insulating silicon oxide, and as an effective diffusion barrier to allow high‐temperature annealing of the catalyst/TiO2‐protected‐n+silicon interface necessary to retard electrolytic corrosion. Halide composition is examined in the (FA1‐xCsx)PbI3 system with a bandgap suitable for tandem operation. A fill factor of 72.5% is achieved using a Spiro‐OMeTAD‐hole‐transport‐layer (HTL)‐based HOIP/n+Si solar cell, and a high photocurrent density of −15.9 mA cm−2 (at 0 V vs reversible hydrogen electrode) is attained for the HOIP/n+Si/Pt photocathode in 1 m NaOH under simulated 1‐sun illumination. While this thin‐film design creates stable interfaces, the intrinsic photo‐ and electro‐degradation of the HOIP photoabsorber remains the main obstacle for future HOIP/Si tandem PEC devices. [ABSTRACT FROM AUTHOR]