A series of Zn-modified HBeta (Zn/HBeta) catalysts were prepared via the wetness impregnation method with different zinc precursors such as ZnSO4·7H2O, ZnCl2, C4H6O4Zn·2H2O and Zn(NO3)2·6H2O, and their catalytic performance in the conversion of ethanol to propylene reaction was evaluated. Results indicate that the amount and strength distribution of the acid sites of the Zn/HBeta catalysts were easily tuned by employing different types of zinc precursors. More importantly, when the zinc species were introduced to the HBeta, the propylene yield was significantly enhanced, whereas the yields of ethylene and C2–C4 alkanes were remarkably suppressed. For the catalyst prepared by using the ZnCl2 precursor, a higher propylene yield of up to 43.4% for Zn/HBeta-C was achieved as a result of the moderate amount and strength distribution of acid sites. The average coking rate of the used Zn/HBeta catalysts strongly depended on the amount of total acid sites, especially the strong acid sites, i.e., the higher the amount of total acid sites of the catalyst, the greater the average coking rate. For the catalyst prepared by using the ZnSO4·7H2O precursor, Zn/HBeta-S exhibited a better stability even after depositing more coke, which was due to the higher amount of strong acid sites. [ABSTRACT FROM AUTHOR]

The size effects of metal catalysts have been widely investigated to optimize their catalytic activity and selectivity. However, the size-controllable synthesis of uniform supported metal nanoparticles without surfactants and/or additives remains a great challenge. Herein, we developed a green, surfactant-free, and universal strategy to tailor the sizes of uniform Pd nanoparticles on metal oxides by an electroless chemical deposition method via defect engineering of supports. The nucleation and growth mechanism suggest a strong electrostatic interaction between the Pd precursor and low-defective CeO 2 and a weak reducing capacity for low-defective CeO 2 , resulting in small Pd nanoparticles. Conversely, large Pd nanoparticles were formed on a highly defective CeO 2 surface. Combined with various ex situ and in situ characterizations, a higher intrinsic activity of Pd for the CO 2 -to-CO hydrogenation was found on large Pd nanoparticles with higher electron density owing to their stronger H 2 dissociation ability and H-spillover effects, as well as the larger number of oxygen vacancies generated in situ for CO 2 activation under hydrogenation conditions.