Search

The Mn2O3@ZnMn2O4/C hollow microspheres were synthesized by room-temperature stirring and then annealing under air atmosphere. Benefiting from the unique structure, its application in AZIBs as cathode exhibits excellent electrochemical performance.

CrFeNiTix (x = 0.2, 0.3, 0.4, 0.5, and 0.6 molar ratio) compositionally complex alloys were fabricated by vacuum arc melting to investigate the microstructure, hardness, and compressive properties. The results revealed that CrFeNiTix alloys consisted of the principal face-centered cubic (FCC) phase and body-centered cubic (BCC) solid solution, with an amount of (Ni, Ti)-rich hexagonal close-packed phase. CrFeNiTix alloys exhibited the typical dendrite. Ti0.2 and Ti0.3 alloys were composed of FCC and BCC solid solutions in the dendrite, as well as e (Ni3Ti) and R (Ni2.67Ti1.33) phases in the inter-dendrite, simultaneously. For Ti0.4, Ti0.5, and Ti0.6 alloys, (Fe, Cr)-rich solid solution separated out and e phase transformed into R phase gradually. Meanwhile, TEM analysis indicated that Ti0.4 alloy matrix consisted of the principal FCC phase containing (Ni, Ti)-rich intragranular nanoprecipitates. The hardness values of CrFeNiTix alloys were increased with the addition of Ti content and the high compressive strength of CrFeNiTix alloys was maintained, which was attributed to the solid solution strengthening and precipitation hardening.

Analysis the electricmotorcar aluminum wheels’ hole defect on macroscopic and microscopic, observed that the main defects、concentrated site and the main alloy phase. Combined with the local casting technological parameters, the filling and solidification process of aluminium alloy hub was simulated by using Anycasting software. The results showed that: castings filling smoothly, at the junction of the spoke and the rim and the hub central are easy to produce casting defects. Using the optimized process parameters that is lower pouring temperature, higher pouring height and set the vent to experiment, after comparing the results with the original process known, Shrinkage and porosity defects decreased, but there are still some degree of defects, indicating optimized process parameters have some effect.

Vacuum sintering and ball milling methods were employed in the preparation process of Ti-C grain refinement and the ability of refiners with varying ratios of Ti and C to refine ZL111 crystal grains was tested. The refinement effect of the Ti-C ratios on tensile strength, elongation percentage, Brinell hardness, pro-eutectoid αAl and the size of the Si phase of ZL111, after modification by rare-earth and strontium nitrate, were studied by means of metallographic examination, SEM and mechanical property tests. The results show that there is an obvious increase in the tensile strength and elongation percentage of refined ZL111 with these new Ti and C refiner compounding powders, while Brinell hardness remained more or less constant. The pro-eutectoid αAl is considerably reduced in size and the Si phase shows a finer and rounder structure. The refiner exhibits a good grain refining performance when the Ti-C ratio is 25:1, for Al crystals can favorably easily form nuclei and grow up along the TiC surface thanks to the TiAl 3 generated by surplus Ti and Al. The mechanical properties have clearly been improved by the addition of strontium nitrate to ZL111. The effective factors in the modification of mechanical properties of ZL111 are in order of importance: strontium nitrate, Ti-C ratio and rare earth.