Search

To adequately understand the waterborne epoxy resin and enhance the compressive, tensile strength of oil-well cement stone, the cement composite materials were prepared with different addition of waterborne epoxy resin, and the specimens were cured for 3days, 7 days, 14days, 28days at 50°C thermostatic water bath to test the compressive strength and tensile strength, respectively. The results showed when the content of resin emulsion is 30%, the compressive strength and tensile strength of the cement are increased by 303.09% and 306.04% compared with pure cement, respectively. Obviously, in the mechanical performance testing, oil-well cement stone modified by waterborne epoxy resin have been significantly improved compared with the pure cement. To explore the enhanced microstructure of oil-well cement modified with waterborne epoxy resin, the cement specimens were prepared with 30% waterborne epoxy resin analyzed by scanning electron microscopy (SEM).

The improvement of strength and ductility is a challenging task for application of oil well cement. As a 2D nanomaterial with high strength and toughness, graphene oxide (GO) was used as a reinforcing additive in oil well cement. The mechanical properties and micro-structure of oil well cement enhanced by GO were investigated. The compressive strength and flexrual strenghth of cement stone both showed a good enhancement effect when the content of GO was 0.02% -0.05%. The compressive strength and flexrual strength could increase by 15.8% and 33.5%, respectively. The results of SEM and MIP revealed that GO played a template role in promoting the formation of hydration products and further filled in the pores between the hydration products, which refined the micro-structure and improved mechanical properties of the cement consequently.

On account of that the domestic polymer fluid loss additive exists some severe problems, such as, inferior thermal resistance, poor salt tolerance, strong shear-and thermal thinning behavior, a novel polymer/silica nanocomposite PADMO-V@NS is used as ultra-high temperature fluid loss control additive for cementing. In the present study PADMO-V@NS was prepared through an in situ free radical copolymerization of 2-acrylamico-2-methylpropane sulfonic acid (AMPS), N,N-dimethylacryl amide (DMAM), maleic anhydride (MA), octadecyl dimethylallyl ammonium chloride (ODAAC) and triethoxyvinylsilane (VTS) modified nanosilica. The linear hydrophobic associated copolymer was regarded as the shell and the modified nanosilica as the core. The microstructure, compositions and thermal resistance of PADMO-V@NS were investigated through FTIR and TGA techniques. The results showed that the copolymer modified with nanosilica particles possessed more excellent thermal stability than that of PADMO, and the most rapid decomposing temperature of PADMO-V@NS was highly up to 396.9°C. The application performance of PADMO-V@NS in cement slurry exhibited that it had excellent fluid loss control capacity, good high temperature resistance, strong salt tolerance and mild shear-/ thermal thinning performance, and could be used in 220°C and saturated brine circumstances. Moreover, comparing to PADMO, the compressive strength of set cement containing the copolymer increased over 20 % at 80°C, atmosphere pressure and curing time of 1 day due to the reaction of residual silanol groups with Ca (OH)2. The laboratory research results indicated that the multi-functional fluid loss additive composed of hydrophobic associated polymer/silica nanocomposite had bestowed on the cement slurry systems good comprehensive properties, and may have extensive applications in deep & ultra-deep oil/gas wells cementing.

In this study, a novel polymer retarder DRH-200LG was synthesized to solve the problems of retarding failure, strong dispersivity under high temperature and adverse impact on the strength development of cement stone. The composition of the polymer was confirmed by IR, and its thermal stability was proved by DSC, TG analysis and thermal treatment at 200 °C. Furthermore, the stability and strength development of cement slurry was evaluated by the comparative consistency method and ultrasonic method, respectively. The results show that DRH-200LG has good high temperature-resistance and retarding performance, presenting favourable influence on the stability and strength development of cement slurry. DRH-200LG shows a good application prospect in the cementation of deep & ultra-deep wells. And it has some guiding significance in the research and innovation of a novel polymer used as oil well cement retarder.

It is important for modern agricultural production to measure temperature and humidity in a real time way. This paper combined the short-distance wireless communication technology ZigBee with the long-distance wireless communication technology GPRS to design a solar-powered temperature and humidity measuring system. The system is easy to install and can run in low cost, so it is especially suitable for small and medium agricultural producers.

Logical framework of enterprise integration platform is constructed, which is based on the model of user-process-applications. The application systems and business processes are encapsulated by the neutral and standard web services with the support of enterprise applications and database. By using services publishing and discovering mechanisms, enterprise resources can be located and shared. Services within the enterprise can by dynamically orchestrated as processes, so that the enterprise business process can by dynamically constructed and monitored according to the changing environment. Core of the platform is orchestration and management of web services, which is driver by a process engine. The platform is exhibited as enterprise portal supporting single sing-on. An enterprise –wide Kanban system is also incorporated within the platform, covering the enterprise and workshop information. An example is given at the end.