Search

Laser shock peening (LSP), a surface modification technique, is promising to enhance the strength and wear resistance for Ni-based superalloys. To understand the strengthening mechanism in a laser shock peened Ni-based superalloy DZ417G, we utilize synchrotron poly- and monochromatic X-ray microdiffraction, as well as electron microscopy and microhardness to quantify the local microstructures and mechanical properties at various depths. In the 1.2-mm-deep hardened layer, the microhardness increases monotonically by ∼50% from the unaffected interior to the surface. Quantitative microdiffraction analysis shows that large amounts of dislocations are introduced by LSP. High densities of 7.1 × 1015 m−2 and 11.8 × 1015 m−2 are seen close to the peened surface for the γ- and γ′-phases, respectively, which are 5 and 20 times of those in the unaffected region. Different gradients of dislocation density are observed for the two phases from interior to surface, and their combined effect accounts well for the hardness increment. Due to the unaltered γ′-precipitates and chemical composition in the LSP affected zone, the large density of dislocations dominates the observed strengthening. Combined poly- and monochromatic X-ray microdiffraction allows quantifying the local microstructures of plastic deformation over a large sampling scale that can hardly be achieved using other materials characterization techniques.

Progress in computing speed and algorithm efficiency together with advances in area detector and X-ray optics technologies have transformed the technique of synchrotron radiation-based scanning Laue X-ray microdiffraction. It has now evolved into a near real-time quantitative imaging tool for material structure and deformation at the micrometer and nanometer scales. We will review the achievements of this technique at the Advanced Light Source (Berkeley, CA, USA), and demonstrate its application in the thorough microstructural investigations of laser-assisted 3D printed nickel-based superalloys.

Synchrotron-based Laue microdiffraction has been widely applied to characterize the local crystal structure, orientation, and defects of inhomogeneous polycrystalline solids by raster scanning them under a micro/nano focused polychromatic X-ray probe. In a typical experiment, a large number of Laue diffraction patterns are collected, requiring novel data reduction and analysis approaches, especially for researchers who do not have access to fast parallel computing capabilities. In this article, a novel approach is developed by plotting the distributions of the average recorded intensity and the average filtered intensity of the Laue patterns. Visualization of the characteristic microstructural features is realized in real time during data collection. As an example, this method is applied to image key features such as microcracks, carbides, heat affected zone, and dendrites in a laser assisted 3D printed Ni-based superalloy, at a speed much faster than data collection. Such analytical approach remains valid for a wide range of crystalline solids, and therefore extends the application range of the Laue microdiffraction technique to problems where real-time decision-making during experiment is crucial (for instance time-resolved non-reversible experiments).