Search

The orthorhombic perovskite, Gadolinium aluminum oxide (GdAlO3, GAP) material was successfully prepared by hydrothermal supercritical fluid method using co-precipitated gel of GAP. All experiments were carried out in the pressure and temperature ranges of 100–150 MPa and 180–650 °C respectively. The as-prepared GAP samples were systematically characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FT-IR), X-ray spectroscopy (EDS), thermo gravimetry (TGA) and differential thermo gravimetry analysis (DTA). The XRD profile confirms fully crystalline and orthorhombic nature of as-prepared materials, which is well correlated to the reported results. The SEM studies reveal that the GAP materials synthesized at 650 °C/150 MPa for 92 hrs possesses polycrystalline nature with average particle size in the range of 5–20 µm. The DTA shows a crystallization peak at 361 °C at this temperature the agglomerated GAP gel starts to crystallize into polycrystalline GAP materials. When compared with other methods, like sol-gel and solid-state reactions our crystallization temperature is very much lower and feasible. This work not only demonstrates a simple way to fabricate GAP polycrystalline materials from co-precipitated gels but also shows a possible utilization of same technique for synthesis of other high temperature materials.

The orthorhombic perovskite, Gadolinium aluminum oxide (GdAlO3, GAP) material was successfully prepared by hydrothermal supercritical fluid method using co-precipitated gel of GAP. All experiments were carried out in the pressure and temperature ranges of 100-150 MPa and 180-650 °C respectively. The as-prepared GAP samples were systematically characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FT-IR), X-ray spectroscopy (EDS), thermo gravimetry (TGA) and differential thermo gravimetry analysis (DTA). The XRD profile confirms fully crystalline and orthorhombic nature of as-prepared materials, which is well correlated to the reported results. The SEM studies reveal that the GAP materials synthesized at 650 °C/150 MPa for 92 hrs possesses polycrystalline nature with average particle size in the range of 5-20 µm. The DTA shows a crystallization peak at 361 °C at this temperature the agglomerated GAP gel starts to crystallize into polycrystalline GAP materials. When compared with other methods, like sol-gel and solid-state reactions our crystallization temperature is very much lower and feasible. This work not only demonstrates a simple way to fabricate GAP polycrystalline materials from co-precipitated gels but also shows a possible utilization of same technique for synthesis of other high temperature materials. [ABSTRACT FROM AUTHOR]

Gadolinium aluminum perovskite (GdAlO3, GAP) is a promising high temperature ceramic material, known for its wide applications in phosphors. Polycrystalline gadolinium aluminum perovskites were synthesized using a precursor of co-precipitate gel of GdAlO3 by employing hydrothermal supercritical fluid technique under pressure and temperature ranging from 150 to 200 MPa and 600 to 700 °C, respectively. The resulted products of GAP were studied using the characterization techniques, such as powder X-ray diffraction analysis (XRD), infrared spectroscopy (IR), scanning electron microscopy (SEM) and energy dispersive analysis of X-ray (EDX). The X-ray diffraction pattern matched well with the reported orthorhombic GAP pattern (JCPDS-46-0395). [ABSTRACT FROM AUTHOR]