Search

This study aimed to evaluate the effect of light attenuation through ceramic veneers and resin cement on degree of conversion (DC), cohesive strength (CS), and microshear bond strength (µSBS) of experimental adhesive systems. Experimental etch-and-rinse and self-etch adhesives were combined with different ratios of camphorquinone (CQ) and diphenyl(2,4,6-trimethylbenzoyl) phosphine oxide (TPO) photoinitiators: CQ-only; 3CQ:1TPO; 1CQ:1TPO; 1CQ:3TPO and TPO-only. Square-shaped ceramic veneer (IPS Empress Esthetic, Ivoclar Vivadent) (n = 10; 10mm long x 10mm wide x 0.5mm thick) and resin cement specimens (Variolink Esthetic LC, Ivoclar Vivadent) (n = 10; 10 mm long x 10 mm wide and 0.3 mm thick) were prepared. Light transmittance of a multiple-peak LED (Bluephase G2, Ivoclar Vivadent) was measured through restorative materials using a spectrometer (n = 5). Adhesive specimens were analyzed for DC, CS, and µSBS by light-curing the adhesive with or without (control) ceramic veneer, and with resin cement fixed to output region of the light-curing tip (n = 10). Data were submitted to ANOVA and Tukey's test (a = 0.05). Total light transmittance through the restorative materials was attenuated, and this attenuation was more evident for the violet spectrum. The DC for the TPO groups in ratios up to 1CQ:1TPO was similar to the control. 1CQ:3TPO showed lower values for CS. µSBS was reduced for all groups with light attenuation, but lower values were observed for 1CQ:3TPO and TPO-only. In conclusion, light transmission was reduced with interposed restorative materials. Adhesives combined with CQ and TPO up to 1CQ:1TPO showed greater cure efficiency and mechanical properties compared with a higher amount of TPO. [ABSTRACT FROM AUTHOR]

Aim: The aim of this study was to evaluate how acid-etching of the cavosurface enamel in Class I resin composite restorations influences the bond strength to the pulpal wall and the restoration, Knoop microhardness and nanoleakage after thermomechanical aging. For this research 76 fresh human molars were selected and restored with Silorane or Clearfil SEBond/Z350XT composite divided in 4 groups (Silorane system restored with or without enamel cavosurface acid-etching and Clearfil SEBond/Z350XT with or without enamel cavosurface acid-etching). To induce artificial aging, samples were subjected to thermomechanical cycling through 200,000 and thermal cycling between 5 and 55 °C with 30 second filling and 15-second drainage steps. Microhardness and microtensile bond strength were evaluated in 32 teeth (n=8) each and nanoleakage evaluation was performed in 12 teeth (n=3). Samples restored by Clearfil SEBond/Z350 XT without cavosurface acid-etching showed significantly lower microtensile bond strength results. The resin composite Z350XT presented higher values of Knoop microhardness. It was observed little or no infiltration for Silorane groups and moderate infiltration for Clearfil SE Bond groups. Acid-etching of the cavosurface enamel during restoration procedure with Clearfil Se Bond resulted in a stronger bond after thermomechanical cycling. Silorane groups showed less infiltration than Clearfil SE Bond groups. [ABSTRACT FROM AUTHOR]

Copyright of Revista Dental Press de Estética is the property of Dental Press International and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Copyright of Revista Dental Press de Estética is the property of Dental Press International and its content may not be copied or emailed to multiple sites or posted to a listserv without the copyright holder's express written permission. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)

Purpose: To evaluate the light transmittance of ceramic veneers of different thicknesses and verify their influence on the degree of conversion, color stability, and dentin bond strength of light-curing resin cements containing different photoinitiator systems., Materials and Methods: Experimental resin cements were fabricated containing camphorquinone and amine (CQ-amine), TPO, Ivocerin (IVO), or TPO and Ivocerin (TPO-IVO). All photoinitiators were characterized by UV-Vis spectrophotometry. Disk-shaped lithium disilicate ceramic specimens that were 0.4, 0.7, and 1.5 mm in thickness were prepared using IPS e.max Press (Ivoclar Vivadent, shade LT/A2). Light transmittance through each specimen was measured using spectrophotometry. Specimens of each cement (n = 10) were made in a custom-designed mold and were light cured through each glass-ceramic disk using a multiwave LED (Bluephase G2, Ivoclar Vivadent). CS was evaluated using spectrophotometry before and after artificial aging with UV light. DC was evaluated using FTIR-spectroscopy. Dentin µSBS was evaluated using 0.75-mm-thick specimens that were light cured under the same protocol (n = 10). All data were submitted to two-way ANOVA and Tukey's test (α = 0.05; β = 0.2)., Results: CQ-amine cements showed the highest color changes (p < 0.05) due to increased yellowing when compared to the amine-free cements (p < 0.05). However, all cements showed a significant color change after aging when cured through ceramics up to 1.5 mm thick (p < 0.05). The TPO-IVO cement showed the highest DC and the IVO cement showed a similar DC when compared to the CQ-amine cement. The TPO cement presented the lowest DC (p = 0.0377). No differences in mean dentin µSBS were found among the cements, except for the TPO cement, which presented a lower mean dentin µSBS (p = 0.0277)., Conclusion: Amine-free cements containing Ivocerin and TPO seem to be a better alternative to CQ-amine cements, while not reducing either DC or dentin µSBS of amine-free cements. However, CQ-amine and amine-free cements still seem to change color over time.

The aim of this in vitro study was to evaluate the nanoleakage of fiber posts luted using different adhesive strategies and to investigate the effect of 2% chlorhexidine (CHX) on nanoleakage at the resin-dentin interfaces of self-adhesive cements. The self-adhesive and etch-and-rinse adhesive groups tested demonstrated similar results with regard to nanoleakage. Pretreatment with CHX promoted an adequate seal at the resin-dentin interface for self-adhesive cements.

Unlabelled: The aim of this study was to evaluate the effect of low shrinkage monomers on physicochemical properties of dental resin composites. Two low shrinkage resin composites: one with a crosslink branching monomer (Kalore, GC Corp) and a novel monomer (Venus Diamond, Heraeus Kulzer) were compared to a conventional resin composite formulation (Filtek Z250, 3M/ESPE). The volumetric shrinkage was evaluated by µCT analysis (n=5) and the physicochemical properties by degree of C=C conversion (DC), flexural strength (FS) and Young's modulus (YM) (n=10). All samples were light cured by a LED device (Radii, SDI) with 16 J/cm2. The results were analysed by one-way ANOVA and Tukey test for multiple comparisons (α=0.05). No statistical difference was found between µCT shrinkage values to Kalore (1.8%) and Venus Diamond (1.7%) (p≥0.05); Z250 presented statistical highest shrinkage value (2.0%). Kalore presented higher statistical DC (60.8%) than Venus Diamond (49.5%) and Z250 (49.6%). No statistical difference was found between FS or YM properties to Venus Diamond and Z250; Kalore presented statistical lowest FS and YM properties (p≥0.05)., Conclusion: Using novel monomers seem to reduce polymerization shrinkage without affecting the physicochemical properties evaluated of resin composites rather than using crosslink branching monomers.

Discrepancies in tooth size and shape can interfere with smile harmony. Composite resin can be used to improve the esthetics of the smile at a low cost while offering good clinical performance. This article presents an approach for restoring and correcting functional, anatomic, and esthetic discrepancies with minimal intervention, using composites and a direct adhesive technique. This conservative restorative procedure provided the patient with maximum personal esthetic satisfaction.