Search

The femtosecond laser direct writing of metals has gained significant attention for micro/nanostructuring. Copper (I) oxide nanospheres (NSs), a promising material for multi-photon metallization, can be reduced to copper (Cu) and sintered through near-infrared femtosecond laser pulse irradiation. In this study, we investigated the size effect of copper (I) oxide nanospheres on their morphology when coated on Cu thin films and irradiated by near-infrared femtosecond laser pulses. Three Cu2O NS inks were prepared, consisting of small (φ100 nm), large (φ200 nm), and a mixture of φ100 nm and φ200 nm NSs. A unique phenomenon was observed at low laser pulse energy: both sizes of NSs bonded as single layers when the mixed NSs were used. At higher pulse energies, the small NSs melted readily compared to the large NSs. In comparisons between the large and mixed NSs, some large NSs remained intact, suggesting that the morphology of the NSs can be controlled by varying the concentration of different-sized NSs. Considering the simulation results indicating that the electromagnetic fields between large and small NSs are nearly identical, this differential morphology is likely attributed to the differences in the heat capacity of the NSs. [ABSTRACT FROM AUTHOR]

The femtosecond laser direct writing of metals has gained significant attention for micro/nanostructuring. Copper (I) oxide nanospheres (NSs), a promising material for multi-photon metallization, can be reduced to copper (Cu) and sintered through near-infrared femtosecond laser pulse irradiation. In this study, we investigated the size effect of copper (I) oxide nanospheres on their morphology when coated on Cu thin films and irradiated by near-infrared femtosecond laser pulses. Three Cu2O NS inks were prepared, consisting of small (φ100 nm), large (φ200 nm), and a mixture of φ100 nm and φ200 nm NSs. A unique phenomenon was observed at low laser pulse energy: both sizes of NSs bonded as single layers when the mixed NSs were used. At higher pulse energies, the small NSs melted readily compared to the large NSs. In comparisons between the large and mixed NSs, some large NSs remained intact, suggesting that the morphology of the NSs can be controlled by varying the concentration of different-sized NSs. Considering the simulation results indicating that the electromagnetic fields between large and small NSs are nearly identical, this differential morphology is likely attributed to the differences in the heat capacity of the NSs.

Ultrathin flat metalenses have emerged as promising alternatives to conventional diffractive lenses, offering new possibilities for myriads of miniaturization and interfacial applications. Graphene-based materials can achieve both phase and amplitude modulations simultaneously at a single position due to the modification of the complex refractive index and thickness by laser conversion from graphene oxide into graphene like materials. In this work, we develop graphene oxide metalenses to precisely control phase and amplitude modulations and to achieve a holistic and systematic lens design based on a graphene-based material system. We experimentally validate our strategies via demonstrations of two graphene oxide metalenses: one with an ultra-long (~16λ) optical needle, and the other with axial multifocal spots, at the wavelength of 632.8 nm with a 200 nm thin film. Our proposed graphene oxide metalenses unfold unprecedented opportunities for accurately designing graphene-based ultrathin integratable devices for broad applications.