Search

Considering energy conservation and emission reductions, lightweight automobiles have become a research focus in the automotive industry. Steel/aluminum joining is regarded as an ideal lightweight structure, which can not only reduce the energy consumption but also ensure safety and is already attracting extensive attention. In this study, aluminum alloy 6061 and B410LA steel sheets were successfully joined by refill friction stir spot welding. The tensile properties, microhardness distribution and interfacial microstructure characteristics of the steel/Al welded joints were investigated. The maximum tensile load of the steel/Al joint was 4.3 kN. The mechanical properties of the steel/Al refill friction stir spot welded joint were largely determined by the bonding quality of the sleeve-plunging zone. With the stirring of the sleeve and the pin during the refill friction stir spot welding, work hardening occurred in the stir zone (SZ). The microhardness of the SZ was significantly higher than that of the steel base metal (BM) and could be detected on the steel side. The Fe-Al intermetallic compound (IMC) layer was continuously distributed at the interface of the sleeve-plunging zone, revealing good uniformity in the thickness. In particular, a hook-and-vortex-like structure formed during the refill friction stir spot welding process in the sleeve-plunging zone, producing a mechanical interlock effect at the interface. The ideal mechanical properties of the welded joint could be attributed to the good quality of the metallurgical and mechanical bonding at the interface, especially the mechanical interlock effect, thereby depending on the hook-and-vortex-like structure. [ABSTRACT FROM AUTHOR]

Considering energy conservation and emission reductions, lightweight automobiles have become a research focus in the automotive industry. Steel/aluminum joining is regarded as an ideal lightweight structure, which can not only reduce the energy consumption but also ensure safety and is already attracting extensive attention. In this study, aluminum alloy 6061 and B410LA steel sheets were successfully joined by refill friction stir spot welding. The tensile properties, microhardness distribution and interfacial microstructure characteristics of the steel/Al welded joints were investigated. The maximum tensile load of the steel/Al joint was 4.3 kN. The mechanical properties of the steel/Al refill friction stir spot welded joint were largely determined by the bonding quality of the sleeve-plunging zone. With the stirring of the sleeve and the pin during the refill friction stir spot welding, work hardening occurred in the stir zone (SZ). The microhardness of the SZ was significantly higher than that of the steel base metal (BM) and could be detected on the steel side. The Fe-Al intermetallic compound (IMC) layer was continuously distributed at the interface of the sleeve-plunging zone, revealing good uniformity in the thickness. In particular, a hook-and-vortex-like structure formed during the refill friction stir spot welding process in the sleeve-plunging zone, producing a mechanical interlock effect at the interface. The ideal mechanical properties of the welded joint could be attributed to the good quality of the metallurgical and mechanical bonding at the interface, especially the mechanical interlock effect, thereby depending on the hook-and-vortex-like structure.

In order to develop novel direct manufacturing of ABS resin on Al alloy surface by the 3D printing technique with high interfacial strength, the influences of the temperature and the roughness of the Al-alloy substrate, and the cooling rate after manufacturing on the bonding strength of an additive manufactured ABS-resin/Al-alloy dissimilar joint were investigated. The experimental results reveal that the mechanical interlock mechanism is a primary factor for the adhesion between ABS resin and the Al alloy. Besides, there was optimum surface roughness to improve the interlock effect of the ABS-resin/Al-alloy joints; the high bonding strength was able to be achieved under the condition of the relatively fine roughness of the substrate surface. The surface temperature of the substrate was also an essential factor in getting high bonding strength. The interfacial strength increased with increasing the surface temperature of the substrate because the ABS-resin was able to easily penetrate the subtle depressions of the substrate surface due to the improved resin fluidity. However, the interfacial strength decreased due to high thermal residual stress in the case of a much higher condition of the surface temperature of the substrate. From the experimental results, the optimum process condition to achieve about 10MPa adhesion strength was presented.