Search

The long-term degradation of epoxy as the matrix and adhesive serviced in harsh environments plays a key role in engineering applications. Understanding how to improve the toughness and durability of epoxy through reasonable material replacement and design is significant to prolong the service life of engineering structures. In the present paper, thermoplastic polypropylene and thermosetting epoxy were exposed in a coupling environment of elevated temperature, water immersion and sustained bending loading. The evolutions of mechanical and thermal properties were further analyzed and compared. Long-term life prediction was conducted to evaluate the corrosive resistances of polypropylene and epoxy. It can be found that polypropylene has better hydrophobic behavior compared to epoxy. At 80 °C, the ratios of the diffusion coefficient and saturated water uptake between the two matrices were 114.4 and 2.94. At the longest immersion time of 90 days, the degradation percentages of tensile strength were 4.7% (40 °C), 7.5% (60 °C) and 8.8% (80 °C), respectively, which had the higher strength retention (>90%). The maximum strength increase in the multiples of polypropylene/epoxy and polypropylene/polyurethane was 1.95 and 1.75, respectively. The bending loading led to a maximum increase in tensile strength (~1.47%) owing to the oxygen isolation effect. The degradation mechanism was attributed to the active functional groups from the production process reacting with oxygen, resulting in the fracture of the local chain segment. By comparison, water molecules reacted with the hydroxyl groups or interrupted the intermolecular Van der Waals force/hydrogen bond of the epoxy, resulting in irreversible hydrolysis and property degradation. Through the comparison, it can be found that polypropylene and its composites have outstanding properties compared to epoxy, which can make them achieve great application prospects in engineering applications when considering a complex service environment. [ABSTRACT FROM AUTHOR]

The long-term degradation of epoxy as the matrix and adhesive serviced in harsh environments plays a key role in engineering applications. Understanding how to improve the toughness and durability of epoxy through reasonable material replacement and design is significant to prolong the service life of engineering structures. In the present paper, thermoplastic polypropylene and thermosetting epoxy were exposed in a coupling environment of elevated temperature, water immersion and sustained bending loading. The evolutions of mechanical and thermal properties were further analyzed and compared. Long-term life prediction was conducted to evaluate the corrosive resistances of polypropylene and epoxy. It can be found that polypropylene has better hydrophobic behavior compared to epoxy. At 80 °C, the ratios of the diffusion coefficient and saturated water uptake between the two matrices were 114.4 and 2.94. At the longest immersion time of 90 days, the degradation percentages of tensile strength were 4.7% (40 °C), 7.5% (60 °C) and 8.8% (80 °C), respectively, which had the higher strength retention (>90%). The maximum strength increase in the multiples of polypropylene/epoxy and polypropylene/polyurethane was 1.95 and 1.75, respectively. The bending loading led to a maximum increase in tensile strength (~1.47%) owing to the oxygen isolation effect. The degradation mechanism was attributed to the active functional groups from the production process reacting with oxygen, resulting in the fracture of the local chain segment. By comparison, water molecules reacted with the hydroxyl groups or interrupted the intermolecular Van der Waals force/hydrogen bond of the epoxy, resulting in irreversible hydrolysis and property degradation. Through the comparison, it can be found that polypropylene and its composites have outstanding properties compared to epoxy, which can make them achieve great application prospects in engineering applications when considering a complex service environment.

Fiber reinforced polymer composites have great potential to replace steel for bridge cables, underground oil extraction and ocean engineering owing to light weight, high strength and desirable corrosion and fatigue resistances. How to reduce the material cost and improve the durability through the reasonable material design is significant to promote the engineering application. In the present paper, two kinds of carbon/glass fiber hybrid plates were developed including the fiber random hybrid (RH) and core–shell hybrid (CH) modes. The exposure of sustained bending loading and water immersion as long as 360 days was conducted to investigate the effect of fiber hybrid mode and bending loading on the mechanical properties. The results showed the synergetic effects between the carbon and glass fibers can be fully developed through the random fiber hybrid mode. Furthermore, the incongruous bearing behavior and stress concentration of carbon/glass fiber/resin interface were largely relieved, which contributed to higher mechanical properties. Compared to CH plate, the maximum increase percentages of tensile and flexural strength for RH plate after 360 days were 51.3% and 39.7%, respectively. Higher bending loading level resulted in the fast formation of microcracks, which provided more storage space for the water molecule and accelerated the resin hydrolysis and interface debonding of fiber/resin. Finally, the long-term life prediction of hybrid plate in three typical bridge service environments showed the RH plate has superior corrosive resistance compared to CH plate. The retentions of tensile and flexural strength for the service time of five years were close to 30–40% and 50–60%, which provided the durability guideline based on fiber hybrid design for the engineering applications. [ABSTRACT FROM AUTHOR]