Synthesis and characterization of MgAl2O4 micro-rods by a molten salt method.
- Source :
-
Ceramics International . May2015, Vol. 41 Issue 4, p5881-5887. 7p. - Publication Year :
- 2015
-
Abstract
- Large amounts of MgAl 2 O 4 micro-rods were successfully synthesized using the molten-salt technology. The effect of KCl contents on the formation of MgAl 2 O 4 micro-rods was investigated. The structure and morphology of MgAl 2 O 4 were investigated by means of powder X-ray diffraction, field emission scanning electron microscopy, and transmission electron microscopy, respectively. The experimental results showed that the contents of KCl significantly influenced the formation of MgAl 2 O 4 micro-rods. MgAl 2 O 4 micro-rods could be prepared at 1150 °C with a weight ratio of 100:1 between the salt and the starting materials. The formation of MgAl 2 O 4 micro-rods could be suggested to be due to the inhomogeneous nucleation and orientated growth perpendicularly to the surfaces of Al 2 O 3 grains. An impedance-type humidity sensor was finally fabricated based on the as-prepared MgAl 2 O 4 micro-rods. According to tests of the humidity performance, MgAl 2 O 4 micro-rods might be suitable for high-performance humidity sensors. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 02728842
- Volume :
- 41
- Issue :
- 4
- Database :
- Academic Search Index
- Journal :
- Ceramics International
- Publication Type :
- Academic Journal
- Accession number :
- 101002306
- Full Text :
- https://doi.org/10.1016/j.ceramint.2015.01.019