Morphological study of co-extruded dual-layer hollow fiber membranes incorporated with different TiO2 loadings.

Dual-layer hollow fiber (DLHF) membranes prepared via a phase inversion based co-extrusion technique offer a number of advantages, such as self-supporting structure, high active surface area to volume ratio, easy fabrication and ability to withstand high operating pressure. This paper reports novel DLHF membranes fabricated via a single step co-extrusion technique with immobilized titanium dioxide (TiO 2 ) nanoparticles embedded in their outer layer. In this work, the DLHF membranes were prepared by extruding two different dope solutions simultaneously, in which the inner layer consisted of poly(vinylidene fluoride) (PVDF) and solvent N,N-dimethylacetamide (DMAc) while the outer layer was a mixture of PVDF, TiO 2 and DMAc. The effect of TiO 2 loading, where the mass fraction of TiO 2 /PVDF was varied from 0 to 1, on the morphologies and properties of the DLHF membranes were investigated using scanning electron microscopy (SEM), contact angle goniometer, surface roughness and filtration experiments. The SEM results showed that DLHF membranes have a good interfacial adhesion between layers with no delamination found. The structure of the membranes characterized by the length of their finger-like voids was significantly affected by the TiO 2 addition. The void lengths were elongated by the rise of the TiO 2 loading up to certain fraction of TiO 2 /PVDF. Based on all the findings, it can be concluded that the proposed method of producing the DLHF membranes could provide good layer–layer interfacial adhesion and well-dispersed TiO 2 in their outer layer. [ABSTRACT FROM AUTHOR]