Synthesis and characterization of high performance CaZrO3-doped X8R BaTiO3-based dielectric ceramics.

A novel system of lead-free X8R BaTiO 3 -based dielectric materials with high dielectric constants was prepared via conventional mixing method. The phase structure, dielectric and electrical properties and the “relaxorlike” characteristic of ceramic materials were systemically studied. The XRD results indicate that no secondary phase formed in the CaZrO 3 -doped samples after sintering. SEM micrographs reveal that the grain size of CaZrO 3 -doped BaTiO 3 -based samples are not uniform, ranging from 0.2 to 0.9 µm. Bulk densities and dielectric properties were measured as a function of CaZrO 3 concentration. The Curie temperatures of all CaZrO 3 doped samples increase due to the existence of an internal stress between grain cores and shells caused by the diffusion of CaZrO 3 . The oxygen vacancies have a profound effect on the dielectric loss and frequency characteristics. The 3.5 wt% CaZrO 3 -doped sample sintered at 1250 °C showed the optimal dielectric performance ( ε r =4330, tan δ <1.5%, Δ C / C 20 °C ≤±14%) that satisfied EIA-X8R specification. [ABSTRACT FROM AUTHOR]