Comprehensive molecular dynamics simulations of the stacking fault tetrahedron interacting with a mixed dislocation at elevated temperature.

The defect-free channels were frequently observed in irradiated materials, i.e. copper, as a result of the stacking fault tetrahedron (SFT) interactions with dislocations. However, the underlying mechanisms for this process are still unclear to date. To address them, a comprehensive study on the interactions between SFTs and mixed dislocations was performed using molecular dynamics simulations. In particular, eight interaction geometries were considered, in terms of the dislocation Burgers vector directions, dislocation gliding directions and intersection positions on SFT. Various interaction outcomes were revealed after dislocation detachment. (1) SFT is fully absorbed through the transformation into Lomer dislocations, and subsequently moves out of free surfaces along the dislocation. (2) SFT is partially absorbed with the absorbed SFT base moving out of free surfaces along the dislocation. (3) SFT is not absorbed but sheared with ledges left on the SFT faces. (4) SFT is unaffected by the mixed dislocation. The current simulations, especially the full SFT absorption, provide important insights into the forming mechanisms of defect-free channels in irradiated materials. [ABSTRACT FROM AUTHOR]